text: Initially, the chemical reactions that normally occur in the cement paste, generate an alkaline environment, bringing the solution in the cement paste pores to pH values around 13. In these conditions, passivation of steel rebar occurs, due to a spontaneous generation of a thin film of oxides able to protect the steel from corrosion. Over time, the thin film can be damaged, and corrosion of steel rebar starts. The corrosion of steel rebar is one of the main causes of premature failure of reinforced concrete structures worldwide, mainly as a consequence of two degradation processes, carbonation and penetration of chlorides. With regard to the corrosion degradation process, a simple and accredited model for the assessment of the service life is the one proposed by Tuutti, in 1982. According to this model, the service life of a reinforced concrete structure can be divided into two distinct phases.
  * ,  initiation time: from the moment the structure is built, to the moment corrosion initiates on steel rebar. More in particular, it is the time required for aggressive agents (carbon dioxide and chlorides) to penetrate the concrete cover thickness, reach the embedded steel rebar, alter the initial passivation condition on steel surface and cause corrosion initiation.
  * ,  propagation time: which is defined as the time from the onset of active corrosion until an ultimate limit state is reached, i.e. corrosion propagation reaches a limit value corresponding to unacceptable structural damage, such as cracking and detachment of the concrete cover thickness. 
  The identification of initiation time and propagation time is useful to further identify the main variables and processes influencing the service life of the structure which are specific of each service life phase and of the degradation process considered.