text: referring now to the drawings in the specification , more particularly to fig1 a , 1b and 1c , there are illustrated profile views of openings in conventional masks used in the process of screen printing . such masks are normally made by depositing a resist layer on opposite sides of the metal sheet 10 , exposing similar patterns in the resist layers that are in alignment , and etching from both sides of the sheet 10 . in fig1 a the amount of etching from each side is approximately the same , and opening 12 is symmetrical . the tapered sidewalls results because the metal etchant etches downwardly and laterally . the opening 14 in mask 10 that is illustrated in fig1 b is non - symmetrical , and formed by etching more of the depth of the opening from one side than from the other . in fig1 c and 1d there is illustrated an opening 12 , defining a line , that is provided with a tab 16 that bridges the line opening at periodic intervals . the tabs preserve the integrity of the mask and it is particularly important when the mask contains many long , closely - spaced line openings . referring now to fig2 a and 2b , profile view of line patterns produced by screened printing are illustrated . line 18 on substrate 20 illustrates a screened paste stripe with a well - defined , symmetrical , smooth profile , with a relatively low height . the line is typical of the desired type of line produced by the process of our invention . such lines when laminated will not spread out and short across to adjacent lines . in contrast , line 22 illustrated in 2b has a poorly defined , relatively high height which is undesirable . such lines are much more likely to spread out and short across to an adjacent line when a sheet containing the lines are laminated . referring now to fig3 a to 3b , there is illustrated the basic steps in the screening method of our invention . a screening mask 30 is placed over substrate 32 with the opening pattern oriented to via holes ( not shown ) in the substrate 32 . as shown in fig3 b , a layer 34 of conductive paste is deposited ( 1 ) in openings 36 , ( 2 ) in via holes ( not shown ) in the substrate 32 , and ( 3 ) as a thin layer 38 on the top surface of the mask 30 . the paste deposition can be done with any suitable apparatus . it is preferably achieved with an extrusion type printer 40 of the type shown in fig4 . printer 40 has a cylinder 42 filled with paste 44 that is forced out of nozzle 46 by piston 48 . the nozzle 46 is provided with spaced shoulders 50 , as shown in fig5 which hold the end of the nozzle in spaced relation to the mask 30 . this spaced relation results in the spreading of paste on the surface of the mask to form the layer 38 . it has been discovered that the porous nature of a ceramic or glass - ceramic substrate very quickly absorbs the solvent in the paste that is deposited in the openings in the mask . this causes the paste to become &# 34 ; dried out &# 34 ;. when the mask is lifted from the substrate , the paste must remain fluid in order to flow through the slightly constricted openings , shown in fig1 a and 1b , and to subsequently form a relatively low and uniform stripe profile as shown in fig2 a and 3c . when the paste is dried by the removal of some of the solvent , the resultant stripe 22 will have a higher profile , with a rough surface , as illustrated in fig2 b . further , if the drying of the paste is severe , segments thereof may remain with the mask thereby forming an &# 34 ; open &# 34 ; in the printed line . the more drying of the paste , the more non - uniform will be the line height since the paste flow is restricted , particularly in the area of the tabs . the above - described problems are prevalent in screen printing of paste by prior art techniques on substrates capable of absorbing the solvent . the problems become more severe as the geometry of the lines become more miniaturized . in the method of this invention , there is provided a layer of paste on the top surface of the mask , which is a source of additional paste solvent in the printed lines in the openings of the mask to replace the solvents absorbed by the substrate as the solvent is removed from the paste . the retention of the solvent assures that the paste within the openings in the mask will remain fluid and result in uniform , relatively low printed lines with a smooth exterior surface . the paste layer on the mask must be removed prior to re - use of the mask . the practice of our invention is useful when depositing paste on any substrate that has a tendency to absorb a solvent in the paste . it is particularly useful in screen printing lines on green ceramic sheets or green glass ceramic sheets that will be laminated to form a multilayer substrate with an internal metallurgy system . such sheets can have any suitable thickness , but usually have a thickness in the range of 7 to 12 mils . any suitable paste can be used in the process . normally the paste will include conductive metal particles such as mo , ta , cu , ag , etc . or combinations thereof . the paste can have any suitable solvent or combination of solvents . a typical solvent is butyl carbitol acetate . normally the paste will include an organic binder , such as ethylcellulose , and a vehicle . the metal mask can have any suitable thickness . a typical mask has a thickness in the range of 2 - 5 mils , most preferably of the order of 4 mils . the processing of the invention is most applicable to the screen printing of relatively fine lines which are formed by line openings in the mask having a width in the range of 2 - 6 mils . the thickness of the paste layer on the top surface of the mask can be any suitable thickness . preferably the paste layer will have a thickness in the range of 1 / 2 - 3 mils . an alternate method of stating the paste thickness is that the ratio of the layer of paste to the mask thickness is in the range of 1 / 4 to 1 . the mask thickness is conventionally in the range of 2 - 5 mils , more preferably of the order of 4 mils . while the invention has been illustrated and described with reference to preferred embodiments thereof , it is to be understood that the invention is not limited to the precise construction herein disclosed and the right is reserved to all changes and modifications coming within the scope of the invention as defined in the appended claims .