text: one component of the ceramic composite according to the present invention is ceramic fiber . ceramic fibers are known and many are commercially available . preferably the ceramic fibers will be aluminosilicate fibers , but other fibers may be utilized including , but not limited to , fibers of silica , alumina , boroaluminasilica ( commercially available under the trademark ultrafiber ® 440 from 3 - m company ), zirconia , silicon nitride , and mixtures thereof . the fibers are available in various dimensions , usually from about 0 . 3 to 4 inches in length ( the longest dimension of the fiber ) and about 1 to 10 microns in diameter . it should be realized that the dimensions of the fibers can generally be tailored to meet the physical characteristics which are desired in terms of mechanical strength , etc . preferred fibers are from about 1 / 4inch in length and about 1 micron in diameter . another component of the slurry may be ceramic microparticles , preferably glass microballoons , many types of which are commercially available in many sizes and are generally hollow spheres , made from various types of glass compositions with various wall thicknesses , usually in the size of about 5 to 200 microns in diameter . solid spheres or diatoms may also be utilized in place of or in addition to the hollow microballoons . as in the case of the fibers , the size of the microballoons will in part determine the mechanical strength and physical characteristics of the composite . preferably , the microballoons should be in a range of about 5 to 50 microns , which appears to be the preferred size for filling the voids which would otherwise exist between the fibers , thus increasing the strength of the composite . in some cases the slurry may contain microballoons and / or diatoms without fibers . also , diatoms ( porous silica inner support structures of certain marine and fresh water algae ) may be added to the slurry . the extremely fine porosity of the diatoms may increase mechanical strength while also increasing the bulk porosity , if desired . the diatoms may comprise up to 100 % of the combined weight of the fibers and microparticles ( microballoons and diatoms ). typically , an aqueous slurry of the ceramic fibers and microballoons and / or diatoms is mixed to provide a substantially uniform dispersion . the concentration of the slurry is not particularly critical . a useful slurry will comprise up to 10 wt % of the fibers , up to 10 wt % of the microballoons with the remainder being water . the slurry may contain from 0 - 99 wt % of ceramic fibers and from 1 - 100 wt % microparticles , based on the combined weight of fibers and microparticles . an aqueous slurry of ceramic fibers is thoroughly mixed to provide a substantially uniform dispersion of the fibers . the slurry will preferably comprise from up to about 10 weight percent alumino - silicate fibers , but other fibers of silica , alumina , boroaluminasilica ( commercially available under the trademark ultrafiber ® 440 from 3m company ), zirconia , silicon nitride , or mixtures thereof may be used at different concentrations , as desired . it may be desirable to use fibers of different materials to tailor the mechanical characteristics or density of the ceramic composite . for instance , a mat having distinct layers of alumina and aluminosilicate fibers would be useful at higher temperatures . fibers of boroalumiasilica or of an alumina - zirconia mixture would reduce the density of the resulting ceramic composite without substantially affecting , for example , its insulation or temperature limit . after the slurry has been thoroughly mixed , it is poured over a form - defining mold ( usually porous enough to allow passage of the water therethrough but not the fibers or microballoons ) which may be flat , irregular , curved , or virtually of any size or shape . the water is then removed typically by vacuum through the porous mold thereby forming a wet mat . then , optionally , the mat may be secured by weaving or tying with a ceramic or glass thread . such threads are commercially available . this may be desirable in order to provide a relatively even surface for application of the ceramic cloth . then the ceramic cloth is applied over the mat and , if desired , woven into the mat again using ceramic thread . the weaving may or may not be necessary depending upon the ultimate use of the ceramic composites , strength desired , etc . for example , if the ceramic composite is not intended to be exposed to severe mechanical stresses then the weaving of the cloth to the wet mat may not be unnecessary . then more of the fiber slurry ( optionally containing microballoons ) is applied over the ceramic cloth to form a fiber mat over the cloth , thereby forming a sandwich of the fiber cloth between two fiber mats . the wet mat is then molded , preferably by the vacuum removal of the excess water , as described above . in a particularly preferred embodiment of the invention , the cloth utilized is larger than the upper and lower fiber mats between which it is sandwiched so that a portion of the cloth extends beyond the periphery of the mat . this flap of cloth will provide a means for attaching the final ceramic product to adjacent ceramic pieces , substrates , structural pieces , etc . then the process of applying a ceramic cloth in a fiber mat may be repeated as desired to obtain the required thickness of the overall mat and number of reinforcing cloths which are desired . of course , the thickness of each of the fiber interlayers between the fiber cloth may be varied by thereby altering the mechanical , dielectric properties , etc . of the mat , as desired . the mat is then dried , usually at a temperature of up to about 200 ° f ., to remove the water . duration of the drying will , of course , depend upon the size and shape of the mat . then , a sol - gel binder is introduced , usually in incremental stages , although a single stage application may be utilized in some instances . the binder is preferably an alumina sol - gel glass that can be prepared by known techniques , such as those disclosed in our prior application . other sol - gel glasses may be utilized , such as silica sol - gel glass or sol - gel glass of similar compositions to the particular fiber in the mat . incremental addition of the binder involves repeating the steps of impregnating the mat with the binder , gelling the binder and curing the mat and binder . usually a light coating of binder is applied in the first stage followed by an air dried gelation to dimensionally stabilize the fiber mat . thereafter , the steps of impregnating , gelling and curing are repeated one or more times until the total desired amount of binder has been added . typically about 15 to 300 wt % of binder is used based on the initial weight of fibers and microballoons in the mat . the impregnating step may be accomplished by wicking , spraying , vacuum infiltrating , and the like . spraying is preferred . after impregnation , the binder is converted to a rigid gel , usually by air drying or by subjecting the binder - impregnated mat to an atmosphere of ammonia gas . since the ammonia - sol reaction is exothermic , there is a tendency for bubbles to form in the mat which can be avoided , however , by allowing the first batch of binder to gel in air . thereafter , the trapped bubbles are not a problem and ammonia gelation can be used . after gelling the binder , the mat is cured , preferably by heating to about 200 ° f . for several hours ( about four hours are preferred ), then by slowly increasing the temperature to about 600 ° f . for a longer period of time ( usually about five hours ), and finally by rapidly reducing the temperature ( quenching ). in addition to the ceramic fibers and microballoons , the slurry may also contain additives which can alter the physical characteristics of the composite . for example , by adding small ceramic whiskers ( about 0 . 4 to 1 micron in diameter , 100 : 1 aspect ratio average ) in small amounts ( usually about 5 to 30 % by weight of the slurry ), the compression strength and modulus of the composite may be increased . whiskers of silicon carbide of about 0 . 4 to 1 micron in diameter are useful for this purpose . the final ceramic composite may also be coated with glass , metals , metal oxides , and the like , if desired . for example , this may be accomplished by brushing a water slurry of pyrex ® glass powder (- 325 mesh is a convenient size ) on its surface , drying , preferably in air , in an oven at about 160 ° f ., and firing the composite at about 2000 ° f . this forms a layer of pyrex ® glass on the surface of the composite . other methods of applying pyrex ® glass to the surface include fusing the glass to the composite surface by torch , plasma spray , laser rastering , etc . pyrex ® glass may also be applied to the composite by the method disclosed in copending , commonly assigned application ser . no . 212 , 397 , filed jun . 27 , 1988 , which is incorporated herein by reference , in which a mixture of colloidal silica , boroaluminasilica powder , single crystal whiskers ( such as silicon carbide or silicon nitride ) and trona are mixed with pyrex ® glass powder and applied as a slurry onto the composite . the coating may be dried and fired as described above . referring to the figures , in fig1 there is shown the steps for a preferred method for making the composite ceramic according to the present invention . in step 10 , a slurry of ceramic fibers in water , optionally containing glass microballoons , is prepared . this slurry is then applied in step 11 to a porous mold and a vacuum is applied to the mold to form the wet fibrous mat . optionally , in step 12 the mat is secured with a glass or ceramic thread . in step 13 a ceramic cloth is applied over the mat . in step 14 more of the slurry is applied over the cloth . if desired , edges of the cloth are left exposed to provide a means for attaching the ceramic to a substrate . then , steps 11 , 12 , 13 and 14 are optionally repeated as many times as desired , depending on the desired number of fiber mat layers and reinforcing cloths . in step 15 the entire mat , including the cloths , are dried by heating . in step 16 the mat , including the cloths , is soaked with a sol - gel ceramic precursor and in step 17 , the sol - gel is gelled and heat - cured to solidify the ceramic composite . thereafter , the soaking in sol - gel , gelling and heat curing ( steps 16 and 17 ) are repeated as necessary . in step 18 a glass binder or overcoat is applied to the completed composite , if desired . this produces a ceramic fabric reinforced fiber ceramic composite according to the present invention . in fig2 there is shown an apparatus and its use to form a cylindrical ceramic composite according to the present invention . referring to fig2 a , a hollow drum 20 is shown having solid ends 21 and 22 with a porous cylindrical surface 23 . the interior of the drum can be subjected to vacuum through opening 24 . referring to fig2 b , the porous drum 20 is immersed into a tank 25 containing the fiber ( and microballoon ) containing slurry . a vacuum is applied to end 24 . while still applying the vacuum , referring to fig2 c , the drum 20 is withdrawn from the tank 25 and the vacuum is continued until the fiber mat 26 is firmly in place . referring to fig2 d , the fiber mat 26 is then held in place by winding or weaving a glass or other fiber thread 27 around the mat 26 . referring to fig2 e , the ceramic reinforcement cloth 29 is then wrapped around the fiber mat 26 . referring to fig2 f , to add additional layers of fiber mat , the entire drum 20 , mat 26 and ceramic reinforcement cloth 29 are then reimmersed into tank 25 and the vacuum is applied as described above to add another fiber layer . the wrapping or weaving with glass thread , binding the ceramic reinforcement cloth and reimmersing in the tank 25 are then repeated until the desired thickness and number of cloth layers are attained . thereafter , the entire mat , including the reinforcement cloths , are dried , the sol - gel applied , gelled and cured as described above . referring to fig3 a there , is shown a form for making the leading edge of a airfoil according to the present invention . the tool 30 is hollow and has solid sides 31a and back 31b with porous upper and lower surfaces 31 . an inlet 32 for applying a vacuum to the interior of the form 30 is provided . this form can be used as described in fig2 to make a single mat composite 34 ( fig3 b ) or multiple fiber mat composite 35 ( fig3 c ) wherein desired portions of the mat are selectably reinforced with the reinforcement cloth 33 . reinforcement cloth may be , for example , glass cloth , graphite cloth , or a cloth which may be chosen for other characteristics , such as electrical characteristics . while preferred embodiments have been shown and described , those skilled in the art will recognize modifications , variations , or alternatives that can be made without departing from the invention . the examples are provided to illustrate the invention and are not meant to limit it . therefore , the specification and claims should be interpreted broadly to protect the invention here described . the claims should be limited only as is necessary in light of the pertinent prior art .