text: at first referring to fig3 description will be made as regards an mram according to a first embodiment of this invention . the mram illustrated in fig3 comprises a substrate 21 and an integrated device portion 22 mounted on the substrate 21 . the integrated device portion 22 is connected through lead wires 23 to lead terminals 24 . the substrate 21 , the integrated device portion 22 , the lead wires 23 , and the lead terminals 24 are collectively molded in mold body 25 made of a plastic resin . upon molding , a high - frequency current suppressor 26 is arranged on a lower surface of the substrate 21 . another high - frequency current suppressor 27 is arranged above the integrated device portion 22 with a space kept therefrom . the high - frequency current suppressors 26 and 27 will later be described in detail . the integrated device portion 22 has a number of memory device portions which will later become clear . each of the memory device portions serves as a memory cell . the integrated device portion 22 has a transistor portion ( not shown ) arranged between each memory device portion and the substrate 21 to select a particular memory cell . referring to fig4 the description will be made as regards the structure of the integrated device portion 22 . the integrated device portion 22 comprises a first conductor 31 on the substrate 21 , a first insulator layer 32 on the first conductor 31 , a first ferromagnetic member 33 on the first insulator layer 32 , a second insulator layer 34 covering the first ferromagnetic member 33 , a second ferromagnetic member 35 on the second insulator layer 34 , a third insulator layer 36 covering the second ferromagnetic member 35 , and a fourth insulator layer 37 and a second conductor 38 both of which are formed on the third insulator layer 36 . a combination of the first ferromagnetic member 33 , the second insulator layer 34 , and the second ferromagnetic member 35 forms a magnetic tunnel function device as one of the above - mentioned memory device portions . each of the first and the second conductors 31 and 38 is arranged so that the second ferromagnetic member 35 is applied with a magnetic field when an electric current is supplied thereto . in case where both of the first and the second conductors 31 and 38 are supplied with electric currents , magnetic fields are produced by the electric currents and combined into a composite magnetic field . under the composite magnetic field , magnetization of the second ferromagnetic member 35 is rotated and reversed . on the other hand , the first ferromagnetic member 33 is fixed in magnetization , for example , by the use a ferromagnetic material having high saturation magnetization . the first ferromagnetic member 33 is made of a copt alloy while the second ferromagnetic member 35 is made of a nife alloy . the second insulator layer 34 is made of al 2 o 3 or the like . each of the first and the second high - frequency current suppressors 26 and 27 serves to suppress harmonic distortion of a pulse current flowing through the first or the second conductor 31 or 37 , to suppress high - frequency radiation noise , and to prevent the noise from being superposed upon a reading current flowing between the first and the second ferromagnetic members 33 and 35 . next , the description will be directed to formation of the high - frequency current suppressors 26 and 27 . each of the high - frequency current suppressors 26 and 27 comprises a granular magnetic thin film containing fe , al , and o . in a vacuum chamber equipped with an oxygen gas supplier , a film was deposited on a polyimide plate by vapor deposition using a fe 70 al 30 alloy as a deposition material . the vacuum degree before deposition was 1 . 33 × 10 − 4 pa or less . the oxygen gas flow rate during deposition was 3 . 0 sccm . after the vapor deposition , heat treatment was carried out in a vacuum magnetic field for two hours at 300 ° c . thus , the granular magnetic thin film was obtained . the thin film had a thickness of 2 . 0 μm , a d . c . resistance of 530 μω · cm , anisotropic magnetic field h k of 18 oe ( 1422 a / m ), saturation magnetization ms of 16800 gauss ( 1 . 68 t ), and a relative bandwidth bwr of 148 %. the relative bandwidth bwr is obtained by extracting a frequency bandwidth between two frequencies at which the value of μ ″ is 50 % of the maximum μ ″ max and normalizing the frequency bandwidth at the center frequency thereof . the saturation magnetization of the thin film was 72 . 2 % of the saturation magnetization of a bulk material comprising a magnetic metal alone . referring to fig5 the magnetic loss term μ ″ has a frequency characteristic illustrated in the figure . the abscissa and the ordinate represent the frequency and the magnetic loss term which is the imaginary part μ ″ of the complex permeability . investigation was made of the high - frequency current suppressing effect of the thin film thus obtained . specifically , the thin film was placed directly on a microstrip line having a length of 75 mm and a characteristic impedance of 50ω . by the use of a network analyzer , transmission characteristic was measured . the result of measurement is shown in fig6 . by the use of the granular magnetic thin film , the s 21 transmission characteristic was monotonously reduced from the frequency around 100 mhz and exhibited − 10 db at about 3 ghz . the result shows that the s 21 transmission characteristic depends upon the distribution of μ ″ and that the level of the suppression effect depends upon the product of μ ″ and the thickness δ . in the foregoing , the formation of the film by the vacuum vapor deposition is described . alternatively , use may be made of sputtering , ion beam deposition , and gas deposition . as far as the magnetic loss material is uniformly deposited , no limitation is imposed upon the technique of forming the thin film . referring to fig7 the description will be made as regards an mram according to a second embodiment of this invention . the mram illustrated in fig7 comprises a substrate 41 and an integrated device portion 42 mounted on the substrate 41 . the integrated device portion 42 is connected through lead wires 43 to lead terminals 44 . the substrate 41 , the integrated device portion 42 , the lead wires 43 , and the lead terminals 44 are molded by a resin mold 45 . upon molding , a high - frequency current suppressor 46 is arranged on a lower surface of the substrate 41 . the integrated device portion 42 is similar in structure to the integrated device portion 22 illustrated in fig4 . the high - frequency current suppressor 46 comprises a thin film of a granular magnetic material . the thin film can be formed in a manner substantially similar to that of the high - frequency current suppressor 26 in the mram described in conjunction with fig3 and 4 . preferably , the thin film is made of a material and has a composition such that no heat treatment is required after deposition by vapor deposition or the like . referring to fig8 the description will be made as regards an mram according to a third embodiment of this invention . the mram illustrated in fig8 comprises a substrate 51 and an integrated device portion 52 mounted on the substrate 51 . the integrated device portion 52 is connected through lead wires 53 to lead terminals 54 . the substrate 51 , the integrated device portion 52 , the lead wires 53 , and the lead terminals 54 are molded by a resin mold 55 . upon molding , a high - frequency current suppressor 56 is arranged above the integrated device portion 52 with a space kept therefrom . the integrated device portion 52 is similar in structure to the integrated device portion 22 illustrated in fig4 . the high - frequency current suppressor 56 comprises a thin film of a granular magnetic material . for example , the thin film can be formed on a polyimide plate in a manner substantially similar to that of the high - frequency current suppressor 27 in the mram described in conjunction with fig3 and 4 . the high - frequency current suppressor 56 thus obtained is arranged above the integrated device portion 52 by molding with the resin mold 55 such as polyimide . in any one of the mrams described above , harmonic distortion of a signal pulse current is decreased and undesired emission or radiation can be reduced . therefore , it is possible to avoid substantial decrease in data writing speed and in data reading speed .