text: according to the present invention , plant fibre , at least one of the following : e . g . rice husk , corncob , peanut shell , coconut shell , wheat husk , bagasses , cereal stalks , corn stalks or sorghum stalks , was placed into a crushing machine , e . g . a dry turbo crushing mill traded by wdj under the model no . wdj - 350 , which has a yield of roughly 500 kg / hour , for grinding . the plant fibre so grounded was then fed into a sieving machine , which was a zsx series tri - vibratory sieving machine of model zsx900 - 2s and of a yield of roughly 850 kg / hour . the sieving criterion was set at 40 - mesh . grounded plant fibre which could not pass through a 40 - mesh sieve was passed back into the dry crushing mill for re - grinding until all the particulate could pass through a 40 - mesh sieve . “ mesh ” ( which may also be called “ pore ”) is a scale for particulate material which represents the number of “ pores ” for every 25 . 4 mm ( i . e . 1 inch ) of a sieve . in this connection , the mesh ( pore ) number and the scale have the relationship as in table 1 below : ( a ) carboxymethyl cellulose ( of a general chemical formula of ( c 6 h 9 o 4 . och 2 cooh ) n where n is a natural number ) of up to 5 wt %, which acts as a viscosity increasing agent to increase the initial viscosity of the material ; ( b ) talc powder ( mg 3 ( si 4 o 10 )( oh ) 2 ) of up to 5 wt %, which acts as a flow aid to increase the fluidity of the material in the mould cavity during the moulding procedure ; ( c ) calcium stearate ([ ch 3 ( ch 2 ) 16 coo ] 2 ca ) of 0 . 1wt % to 5 wt %, which acts as a demoulding agent to promote the release of the resultant container from the mould cavity , and to smoothen the surface of the container ; ( d ) titanium dioxide ( tio 2 ) of 0 . 5 wt % to 3 wt %, which acts as a whitening agent to improve the whiteness of the container ; ( e ) starch ( of a general formula of ( c 6 h 10 o 5 ) n wherein n is a natural number ) of up to 5 wt %, which acts as a modifying agent to improve the adhesive strength of the material , and also to increase the rate of degradation ; 5 wt %, which acts as a reinforcing agent to increase the tensile strength of the container , and to improve its other physical properties ; and ( g ) water ( h 2 o ) of up to 10 wt % to wet the ingredients and thereby to enhance stirring action , and to enhance the smoothness of the surface of the ultimate container . the above ingredients and the grounded plant fibre were all fed into a rotating device for mixing at a speed of 500 - 1 , 300 r . p . m . ( rounds per minute ) for 2 to 5 minutes at a temperature of 30 ° c . to 50 ° c . since heat was generated during the mixing procedure , no external heat was required to keep the temperature within the above range . a modified urea - formaldehyde resin ( to be further discussed below ) was then added and the resultant solution was mixed by rotation at a speed of 2 , 500 - 3 , 600 r . p . m . for 10 to 25 minutes , and at a temperature of 50 ° c . to 80 ° c . the resultant material was then ready for use in the formation of the container . it may also be stored for future use . it is important to control the water content of the resultant material such that it falls within the range of 15 wt % to 22 wt %. the resultant material obtained above was then introduced into a mould for subsequent moulding ( thermo - setting ). the material was firstly pressed at a temperature of 100 ° c . to 200 ° c . and at a pressure of 5 to 8 mpa for 5 to 10 seconds . the pressure was then reduced to normal atmospheric pressure for 5 to 30 seconds . since the material contained water , during the thermo - pressing process , the water vaporized . reduction of the pressure to atmospheric pressure allowed such water vapour to be exhausted in time , thus preventing air bubbles from being trapped in the container . the product was then re - pressed for a period of 5 to 30 seconds at a pressure of 1 . 5 mpa to 16 mpa , to form the formal container . the mould was unloaded to allow the container to be retrieved therefrom . the mould was then cleaned for the next cycle of operation . the moulding procedure is in fact a curing process , under which the material was cured under pressure and temperature to form the container . the basic criteria for the design of the mould are that the shape and dimension of the cavity of the mould should be identical to those of the container , the positioning of the mould should be reliable , the mould should be of sufficient strength , and the mould should have the necessary exhaust channel , and the necessary space for the overflow of surplus moulding material . the container retrieved from the mould was then trimmed to cut off any unwanted parts , in order to standardize the shape of the product . the surface of the container was then coated with a film of water base terpolymer to enhance its resistance to heat and chemicals . the water base terpolymer is vinyl acetate - ethylene - acrylic acid copolymer , with cross - linking agent and silicone anti - foaming agent . the vinyl acetate - ethylene - acrylic acid copolymer is of a general chemical formula of : where n , n ′ and n ′ are all natural numbers , and r and r ′ may each stand for h , alkyl or other substituting groups . the cross - linking agent is methyl - triethoxy silicane ( ch 3 si [ oc 2 h 6 ] 3 ). the silicone anti - foaming agent is siloxane emulsion of the general chemical formula of : the container was then dried in a stove for about 5 minutes , and subsequently packed in a sterilized environment . the room is a relatively sealed place subject to ultraviolet irradiation regularly to eliminate various bacteria in the air , in order to prevent pollution of the container during packaging . a method of the manufacture of the modified urea - formaldehyde resin is demonstrated by example 1 below . table 2 below shows the ingredients used in the manufacture of the modified urea - formaldehyde resin . 1 , 280 grams of formaldehyde was mixed with 50 grams of hexamethylene - tetramine , and the solution was stirred . after 5 minutes of stirring , the ph value of the solution was determined . as the ph value was below 7 . 0 , an appropriate amount of caustic soda was - added to bring the ph value of the solution within the range of 7 . 0 to 7 . 5 . 440 grams of urea was then added and the resultant solution was again stirred for 15 minutes . the temperature was subsequently increased and kept at about 65 ° c . for 15 minutes . the temperature was then increased to 90 ° c . to 95 ° c . the temperature was maintained within this range until the ph value of the solution reached 4 . 1 to 4 . 4 . a sample of the solution was taken and put into clean water of room temperature , whereupon a white cloud appeared . an appropriate amount of caustic soda was then immediately added to bring the ph value to about 6 . 0 . the temperature was promptly brought down to below 75 ° c ., and the ph value of the solution was kept at 7 . 0 to 7 . 5 by addition of 50 grams of aqueous ammonia . 220 grams of urea was added and the solution was kept at a temperature of not lower than 65 ° c . for 20 minutes . when the temperature started to increase slowly , an additional 140 grams of urea was added and the solution was kept at a temperature of about 65 ° c . for another 10 minutes . the remaining aqueous ammonia was added to adjust the ph value of the solution to 8 . 8 to 9 . 0 and the solution was kept for 10 minutes . when the temperature was raised to 85 ° c ., 50 grams of trimeric cyanamide was added . the solution was allowed to react for about 10 minutes while the ph value was kept at about 9 . 0 . vacuum dehydration was started when the temperature was raised to over 90 ° c . vacuum dehydration was stopped when 400 ml was removed from the solution , and the solution was then cooled down . when the temperature fell below 50 ° c ., 50grams of ab - 1 ( trade mark ) was added . the solution was stirred for 10 minutes , whereupon the resultant modified urea - formaldehyde resin was discharged for use in the present invention . such a modified urea - formaldehyde resin is of the general chemical formula of : where n is a natural number , and r stands for h , a hydroxyl group or an amino group . ab - 1 ( trade mark ) is a water - base epoxy resin traded by chang jiang enterprise company , of jiang men city , guangdong province , china , and acts as a formaldehyde absorbing agent . the molar ratio of formaldehyde and urea should be low , such as : when the formaldehyde reacted with the urea to produce urea - formaldehyde molecules , the reaction medium was formaldehyde . in the present example , although the molar ratio of formaldehyde was not high , there was still a surplus of 0 . 2 m , which acted as the medium for the formation of urea - formaldehyde molecules . urea was added in several times to ensure that such reacted sufficiently with formaldehyde to form urea - formaldehyde molecules , in order to maximize the production of the modified urea - formaldehyde resin , and minimize the amount of any remaining free formaldehyde . hexamethylene - tetramine was formed by reacting formaldehyde with aqueous ammonia , to ensure the ph value necessary for the reaction , and to consume any surplus free formaldehyde . the formation of hexamethylene - tetramine also guaranteed the stability of the urea - formaldehyde resin . vacuum dehydration was employed to facilitate the evaporation of surplus free formaldehyde after the completion of the reaction . since formaldehyde is soluble in water , when the pressure in the system decreased , the vapour pressure equilibrium in the formaldehyde solution was broken , the volatility of formaldehyde decreased , and it was easy to overflow . any surplus free formaldehyde was also absorbed by the ab - 1 ( trade mark ). the level of free formaldehyde in the above modified urea - formaldehyde resin is below 0 . 2 %, as compared with 3 % in commonly available urea - formaldehyde resin . this effect is achieved in part by the addition of ab - 1 , which acts as a formaldehyde absorbing agent . tables 3a to 3d below collectively show a total of fifteen examples of containers produced in accordance with the above invention . according to our research , there have not yet been very accurate or quantitative definitions for “ degradation ”. in accordance with the results of various experiments carried out by us , the definition for “ degradation ” for our product is that in several months or days in the natural environment , through the agency of water , sunlight , moisture , micro - organisms , a product according to the present invention can soften , crack , reduce into powder form , decompose , and finally disperse and be absorbed into the soil , and again participates in the innocuous ecological cycle of nature . our experience indicates that a product according to the present invention will be softened in water at normal air temperature in 24 hours , totally softened in 48 hours , and totally dissolved in about 72 hours . on the other hand , it will be totally dissolved in boiling water in about 12 hours . in the case of degradation in the natural environment , through the agency of water , sunlight , moisture and micro - organisms , in 2 to 5 months &# 39 ; time , the container according to the present invention will soften , crack , be reduced into powder form , decompose , disperse and vanish in the soil . during the whole course of the manufacture of the containers , from the selection of the materials to the degradation and vanishing thereof after use , there is no problem of solution . after degradation of the containers in soil , such elements as nitrogen , phosphorous and organic silicon are replenished . containers of the present invention may be bowls , dishes and cups for use in the fast food industry . the material used in the production of the containers may also be used as packaging materials , shock - proof materials for domestic electric appliances or other household utensils , construction materials , decoration materials , handrails of staircase , door planks , floor boards , furniture materials , toys for children , and pet appliances . b ) there are a large variety of sources of plant fibre suitable for use in the present invention , and their prices are low . such plant fibre was previously treated as trash for disposal or burning , but can now be used for the production of useful utensils ; c ) there is no problem of contamination or pollution associated with the degradation of the containers obtained in the present invention . after use and disposal of the containers , they may be reclaimed and reused . if some nutritive matters are added in , they can also be used as fodder for livestock and domestic fowls .