text: the invention may be embodied in many different forms and should not be construed as limited to the illustrated embodiments set forth herein . rather , these illustrated embodiments are provided so that this disclosure will be thorough and complete , and will fully convey the scope of the invention to those skilled in the art . fig1 shows a heat resistant component as known by state of the art . the highly oxidation resistant component has a substrate 4 , a mcraly layer 7 on the substrate , on which a thermally grown oxide layer 10 ( tgo ) is formed or applied and finally an outer thermal barrier coating 13 . fig2 shows an highly oxidation resistant component 1 according the invention . the component 1 can be a part of gas turbine , especially a turbine blade or vane or heat shield . the substrate 4 is metallic , e . g . a super alloy ( ni — al - based , e . g .) on the substrate 4 the mcraly layer zone 16 is a conventional mcraly layer 16 of the type e . g . nicocraly with a typical composition ( in wt %) 10 %- 50 % cobalt ( co ), 10 %- 40 % cromium ( cr ), 6 %- 15 % aluminium ( al ), 0 . 02 %- 0 . 5 % yttrium ( y ) and nickel ( ni ) as base or balance . this mcraly layer 16 may contain further elements such as : 0 . 1 %- 2 % silicon ( si ), 0 . 2 %- 8 % tantalum ( ta ), 0 . 2 %- 5 % rhenium ( re ). instead at least a part of yttrium or in addition this mcraly layer zone 16 can also contain hafnium ( hf ) and / or zirconium ( zr ) and / or lanthanum ( la ) and / or cerium ( ce ) or other elements of the lanthanide group . the thickness of this conventional layer 16 is in the range from 100 to 500 micrometer and is applied by plasma spraying ( vps , aps ) or other conventional coating methods . in this example the inventive highly oxidation resistant component 1 reveals a mcraly layer 16 with another outer layer zone 19 on top , which forms together with the layer zone 16 the protective layer 17 . for example , the outer layer zone 19 consists of the phase β - nial . the thickness of this layer 19 is in the range between 1 and 75 micrometer , especially up to 50 micrometer . the disadvantage of brittleness of the β - nial phase is overcome by the fact that the β - nial layer 19 is thin compared to the mcraly layer 16 . the outer layer 19 can solely consist of the two elements ni and al . the concentration of these two elements is given by the binary phase diagram ni — al and must be chosen in such a way that the outer layer 19 consists of pure β - nial phase at the temperature at which the oxidation of the layer 19 , which forms the tgo 10 , occurs ( 21 - 37 wt % al or 32 - 50 at % al ). nevertheless this β - nial phase can contain further alloying elements as long as these elements do not destroy the phase β - nial phase structure . examples of such alloying elements are chromium and / or cobalt . the maximum concentration of chromium is given by the area of the β - phase in the ternary phase diagram ni — al — cr at the relevant temperatures . cobalt has a high solubility in the β - nial phase and can nearly completely replace the nickel in the nial - phase . similar further alloying elements can be chosen such as si ( silicon ), re ( rhenium ), ta ( tantal ). the main requirement of the concentration of the alloying elements is , that it does not lead to the development of new multi - phase microstructures . also elements ( additions ) such as hafnium , zirconium , lanthanum , cerium or other elements of the lanthanide group , which are frequently added to improve the properties of mcraly coatings , can be added to the β - phase layer . the nial based layer is applied by plasma spraying ( vps , aps ) and / or other conventional coating methods . the advantage of the β - nial phase structure is that a meta - stable aluminium oxide ( θ — or a mixture with γ - phase ) is formed in the beginning of the oxidation of the layer 19 . the tgo ( e . g . aluminium oxide layer ) 10 which is formed or applied on the outer layer 19 has a desirable needle like structure and leads therefore to a good anchoring between the tgo 10 and the ceramic thermal barrier coating 13 . on conventional mcraly coatings , usually the stable α - phase of aluminium oxide is formed upon high temperatures exposure of the coating . however during the use of the heat resistant component 1 with its outer layer 19 meta - stable aluminium oxide 10 is allowed to be transformed into the stabile α - phase during high temperature exposure , which leads to a desirable microporosity in the tgo . another possibility of a component 1 according to the invention is given in such a way that the standard mcraly layer 16 is of the type nicocraly and has an amount of aluminium between 8 % to 14 wt % with a thickness from 50 to 600 micrometer , especially between 100 and 300 micrometer . on this mcraly layer 16 a second mcraly layer zone 19 of the type nicocraly is applied . the composition of this second layer is chosen in such a way that the modified mcraly layer 19 as outer layer 19 shows at a high application temperature ( 900 °- 1100 ° c .) a pure γ - ni matrix . a suitable composition of the second layer ( 19 ) can be derived from the known phase diagrams ni — al , ni — cr , co — al , co — cr , ni — cr — al , co — cr — al . compared to conventional mcraly coatings this modified mcraly layer 19 has a lower concentration of aluminium with a concentration of aluminium between 3 - 6 . 5 wt %, which can easily be applied by plasma spraying by only changing the powder feed of the plasma spraying apparatus accordingly . however , layer 19 can also be applied by other conventional coating methods . a typical composition of this modified mcraly layer 19 which consists of γ - phase is : 15 - 40 wt % chromium ( cr ), 5 - 80 wt % cobalt ( co ), 3 - 6 . 5 wt % aluminium ( al ) and ni base , especially 20 - 30 wt % cr , 10 - 30 wt % co , 5 - 6 wt % al and ni base . instead of yttrium this mcraly layer zone 19 can also contain further additions of so called reactive elements such as hafnium ( hf ) and / or zirconium ( zr ) and / or lanthanum ( la ) and / or cerium ( ce ) or other elements of the lanthanide group , which are commonly used to improve the oxidation properties of mcraly coatings . the total concentration of these reactive elements may be in the range between 0 . 01 and 1 wt %, especially between 0 . 03 and 0 . 5 wt %. the thickness of the modified mcraly layer 19 is between 1 and 80 micrometer especially between 3 and 20 micrometer . further alloying elements can be chosen such as sc ( scandium ), titanium ( ti ), re ( rhenium ), ta ( tantalum ), si ( silicon ). a heat treatment prior to applying a thermal barrier coating can be carried out in an atmosphere with a low oxygen partial pressure , especially at 10 − 7 and 10 − 15 bar . the formation of the desired meta - stable aluminium oxide on top of the modified γ - phase based mcraly layer 19 can be obtained by oxidation of the modified mcraly layer 19 at a temperature between 850 ° c . and 1000 ° c . prior to opposition of a thermal barrier coating , especially between 875 ° c . and 925 ° c . for 2 - 100 hours , especially between 5 and 15 hours . the formation of these meta - stabile aluminium oxide during that mentioned oxidation process can be promoted by addition of water vapour ( 0 . 2 - 50 vol %, especially 20 - 50 vol %) in the oxidation atmosphere or by the use of an atmosphere with a very low oxygen partial pressure at a temperature between 800 ° c . and 1100 ° c ., especially between 850 ° c . and 1050 ° c . in addition to water vapour the atmosphere can also contain non - oxidizing gases such as nitrogen , argon or helium . because the modified mcraly layer 19 is thin , aluminium from the inner or standard mcraly layer 16 can diffuse through the modified mcraly layer 19 in order to support the formation of aluminium oxide on the outer surface of the layer 19 during long term service , which could not be performed by the modified mcraly layer 19 alone because of its low concentration of aluminium . fig2 shows a two layered protective layer 17 . fig3 shows a component with a high oxidation resistance according to the invention . the concentration c of the mcraly layer 16 is continuously graded in such a way , that near the substrate 4 the composition of the mcraly layer 16 is given by a standard mcraly layer 16 as described in fig2 or 1 , and that near the thermal barrier coating 13 the composition of the outer layer 19 shows the composition of the layer 19 as described in fig2 . on the outer layer zone ( 19 ) a thermal barrier coating ( tbc ) ( 13 ) is applied . due to the good oxidation resistance of the protective layer ( 17 ) and the good bonding of the tbc to the tgo ( 10 ) due to adjustment of structure , phases and microstructure the life term of the component 1 is prolonged .