text: thus , the present invention relates also to a process for making a latex foam by a ) compounding the polymer latex of the present invention into a foamable and vulcanizable latex compound ; c ) filling the foam obtained in step b ) into a mold of desired shape ; in order to compound the rubber dispersion of the present invention into a foamable and vulcanizable latex compound the dispersion is preferably mixed with emulsifiers , thickening agents and a vulcanizing paste as known by a person skilled in the art . emulsifiers are added to the rubber dispersion of the present invention in order to increase its mechanical and chemical stability and to facilitate foaming of the rubber dispersion . anionic , cationic or non - ionic surfactants can be chosen depending on the process requirements whereby anionic surfactants are preferred for foaming applications . preferred anionic surfactants are fatty acid soaps , fatty alcohol sulfonates and alkylaryl or aralkyl sulfonates , succinates and amido sulfosuccinates . particularly preferred are alkali metal and ammonium salts of fatty acids and rosin acids and combinations thereof , most preferred are alkali metal salts of fatty acids and rosin acids and combinations thereof . the vulcanization paste , preferably employed in the foaming process of the present invention , comprises sulfur or sulfur compounds , zinc oxide , vulcanization accelerators and customary additives , like antiaging agents or surfactants . examples of suitable sulfur compounds are described in d . c . blackley , high polymer latices , vol . 1 1966 , pages 69 72 . suitable vulcanization accelerators are described in d . c . blackley , high polymer latices , vol . 1 1966 , pages 73 - 86 , and in encyclopedia of polymer science and engineering , vol . 14 , john wiley & amp ; sons , pages 719 - 746 ( 1985 ). suitable antiaging agents are described in d . c . blackley , high polymer latices , vol . 1 1966 , pages 86 - 89 . the vulcanization pastes are suitably applied in amounts of 3 - 15 weight percent , preferably 4 - 12 weight percent , and most preferred 4 - 10 weight percent , based on the weight of the solids of the rubber dispersion . the thus obtained foamable and vulcanizable latex compound can be processed by any process known to the person skilled in the art for making foamed articles . preferably , the foamable and vulcanizable latex compound is processed by the dunlop process or the talalay process , whereby the dunlop process is most preferred . in case the foamed article is prepared according to the dunlop process an appropriate amount of gelling agent is added to the readily mixed vulcanizable latex compound . the quantity of the gelling agent will depend on the desired pot life of the foamable compound which should be advantageously adjusted to be 5 - 20 minutes . preferably according to the dunlop process an aqueous sodium silicofluoride dispersion is used as gelling agent . the compound can be first foamed and then the gelling agent is added and foaming is continued to obtain a homogeneous distribution of the gelling agent within the foam , the desired foam density , as well as the desired foam structure . alternatively , after the addition of the gelling agent the compound is foamed immediately using mechanical means in a way to prepare a stable foam of the desired foam density . thereafter the foamed latex compound is filled into the mold of desired shape . usually closed molds are used but in some cases , for example shoe soles , open molds can be employed . according to the dunlop process the foam structure in the mold is stabilized by gelling the latex foam at elevated temperatures . thereafter the molds are heated , in case of closed molds preferably in saturated steam , to vulcanize the latex foam . after vulcanization the latex article is removed from the mold and if necessary washed and dried . alternatively the talalay process may be employed to prepare the latex foams according to the present invention . in the talalay process the vulcanizable latex compound is first prefoamed to give a foam with relatively high density and then poured into the molds . the closed molds are then evacuated whereby the latex compound foams to the finally desired density due to the vacuum applied and thus fills the mold completely . by cooling the mold to approximately − 30 ° c . the foam structure is stabilized . thereafter carbon dioxide is lead into the mold to pressurize the mold whereby at the same time the ph of the frozen foamed latex compound is lowered resulting in gelling . the foam then may be thawed without changing its structure and the mold is heated in stages up to 110 ° c . to vulcanize the latex foam . after complete vulcanization the article is removed from the mold , optionally washed and dried . the foamed articles of the present invention may be used for mattresses , pillows , neck rests , toppers , shock absorbers , shaped parts of shoes , shoe inside soles , garments padding , protectors for sportswear , athletic implements , bike saddles , motorbike saddles , furniture upholstery material , bumpers , automotive dashboards and carpets . a further object of the present invention is a method for making a latex sealing by : b ) applying the latex compound to a metal substrate ( like for example can ends ), and the can sealing compound should have no impact on the odor and flavor properties of the contents ( food and drinks ) of the can and serves to protect the contents from gases ( oxygen ) and bacterial intrusion from outside as well as gas loss ( carbon dioxide ) from inside . the compound has to be mechanically stable during the compounding and processing and has to exhibit good adhesion properties on metal during the can closing and life cycle of the can . one example of a can sealing compound is given below : the ingredients are added to the compound in the mentioned sequence a - f under continuous stirring with a low shear equipment . moreover , the present invention is directed to an article comprising an aforementioned latex sealing and / or latex film obtained from the aforementioned latex . the article preferably is selected from can sealings and adhesives . surprisingly the latex of the present invention leads to polymer latices and articles manufactured thereof which are very low in odor . surprisingly the mechanical properties of the latex and the products manufactured therefrom are not affected . the latex can be used in any customarily used manufacturing process . the following measuring methods were used to determine the physical parameters of the rubber dispersion of the present invention , as well as of the latex foam . the glass transition temperature tg , the particle size distribution psd , the odor and the mechanical data of the foam are measured as follows . all data given within the entire specification including the claims are measured in accordance with the detailed description given below . thus the description of the measuring methods is not restricted to the examples only . the glass transition temperature was measured according to din 53765 . a traditional dsc system is used ( perkin elmer pyris 6 dsc ). the sample is dropped into a pan . then the sample and the empty reference pan are placed into the dsc oven . the dsc oven is closed and the temperature program for the sample preparation is started . the program starts at 30 ° c . the heating rate is 20 k / min . the maximum temperature is 160 ° c . which is held for 10 min . the sample is cooled down to − 20 ° c . and again heated to 20 ° c . afterwards the dsc measuring is started . the temperature program starts at − 70 ° c . the heating rate is 20 k / min . the maximum temperature is 180 ° c . finally the oven is cooled to room temperature again . the raw data is collected and processed with the pyris ta manager software . the particle size distribution is measured on the particle size distribution analyzer from polymerlaboratories . the diluted latex sample under investigation and a small molecule marker solution are introduced into the system via a two position , electrically actuated valve , such that the eluent flow is not interrupted . the sample components are separated by an hdc mechanism in a “ cartridge ”, and their concentration is measured by a uv detector . the system is calibrated using a series of particle size standards . the mooney - viscosity is measured according to the din 53523 . for the coagulation of the latex 250 g of the latex with 30 % total solids are required . 50 ml of sodium chloride solution ( 25 %) is added to the stirred latex . then 250 ml of a wingstay l / ethanol solution ( 0 . 75 %) are added within 30 seconds . furthermore , 10 ml of sulfuric acid ( 18 %) are dropped into the latex . the coagulate and the serum is filtered through a 200 μm monodur cloth . the residual water is squeezed out and the polymer clump is reduced to small pieces . those are washed with 1 l of demineralised water . the polymer is again squeezed , reduced into small pieces ( 1 - 2 cm ) and dried for 2 h at 105 ° c . the dried rubber pieces are then pressed free of blow holes and cut into the specimen . the measurement is performed at 100 ° c . with a previous heating time of 1 min and a measuring time of 4 min and a rotor speed of 2 rpm ( large rotor ). samples are sensory evaluated in an informal way by experienced staff not having obtained on forehand any information about the samples . odor scores are given using a scale from 1 - 5 ( 0 = no odor , 1 = just noticeable , 5 = very strong ). the volatiles are extracted from the sample by a combined steam distillation and extraction method ( so - called likens and nickerson method , see “ handbuch der aroma forschung ” h . maarse and r . belz , akademie verlag , berlin , 1981 ). 25 g of sample is mixed with 500 ml water and anti - foam ( 1 ml dow corning ® rd ) is added . extraction time is 2 hours . as solvent a mixture of pentane and ether ( 2 : 1 ) is used . the solvent phase is dried and concentrated on a water bath to 0 . 5 ml using a vigreux column . concentrated extracts are analysed with gc - sniff - ms ( agilent 5973 gc - ms ). 1 . 5 μl extract is injected splitless on a 30 m capillary column db - 5ms . diameter 0 . 25 mm , film 1 μm . oven temperature program 0 ° c . ( 1 min ), 10 ° c ./ min to 320 ° c . ( 2 min ). the end of the column is connected to a splitter which leads approx 50 % of the effluent to a sniff port and the other part to the ms detector . at the sniff port the effluent is mixed with humidified air . the sniffing is performed by one person who notes the descriptions of the odors observed at the port with the corresponding retention times ( no chromatograms are shown during sniffing ). the odors are scored from weak to strong ( 0 = no odor , 1 = just noticeable , 5 = very strong ). 389 . 6 g of the aqueous reinforced rubber dispersion were weighted together with 10 . 8 g potassium oleate as 17 . 5 % aqueous solution , 24 . 5 g of sodium carboxyl methyl cellulose solution 2 . 5 % in water ( blanose na - cmc type 12m 31p available from hercules gmbh ) and 36 . 8 g of a 60 % solid vulcanization paste suprotex ugb , obtainable from weserland textilchemie , into the bowl of a hobart planetary mixer ( type n50 ). in a separate vessel 23 . 1 g of 25 % sodium silicofluoride dispersion in water was weighted . the aqueous reinforced rubber dispersion in the mixing bowl was foamed using the hobart planetary mixer until a wet foam density of about 112 g / l was achieved that corresponds to a dry foam density of about 75 g / l . thereafter the sodium silicofluoride dispersion gelling agent was added and mixing was continued for 2 min to achieve homogeneous distribution of the gelling agent within the foam and a homogeneous foam structure . the latex compound thus obtained from each composition according to the examples was filled into a 290 mm × 290 mm × 28 mm mold . the mold was sealed and its content vulcanized at 100 ° c . with saturated steam for 20 min . the vulcanized foam was removed from the mold , washed and dried for 90 min at 120 ° c . in a forced circulation oven . thereafter the samples were conditioned and measured as indicated above with respect to the measuring methods . the actual foam density was measured for normalizing the hardness according to the above equation for a foam density of 75 g / dm 3 . the testing is performed on the tensile testing model zwick / z 010 from zwick . the elongation at break is measured in accordance with din en iso 1798 . deviating from this norm the samples are stored for 16 hours at room temperature the dimension of the sample ( type a ) and the testing speed ( 500 mm / min ) remain unchanged . the hardness of the latex foam is measured in accordance with din en iso 2439 , following the method according to process a — determination of indentation hardness index . conditioning of the samples was performed as follows . this method was followed with the following exceptions . after preparation the samples were stored at room temperature for 16 h . the sample dimensions have been altered to have a square shape with an edge length of 280 ± 2 mm and a sample thickness of 30 ± 2 mm . the hardness is normalized to a hardness at 75 g / dm 3 according to the following equation : whereby a x is the measured hardness as obtained according to the method described above and σ is the actual density of the measured foam given in g / dm 3 . hysteresis is measured in accordance with din en iso 3386 with the following alterations . square shape with an edge length of 60 ± 2 mm and a thickness of 30 ± 2 mm . hysteresis is measured on two samples instead of three , and the samples are stored for 16 h at room temperature . the reactor is charged with a solution of 29 . 3 g potassium oleate , 3 . 75 g potassium chloride and 0 . 73 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 1405 . 5 g deionized water . 324 . 8 g styrene and 1 . 64 g tert - dodecyl mercaptan are added . the reactor is pressed with nitrogen and evacuated . 791 . 0 g butadiene are added . the mixture is cooled to 15 ° c . 0 . 56 g p - menthane hydroperoxide in 34 . 5 g styrene is added , followed by 34 . 5 g deionized water . a solution of 0 . 59 g sodium formaldehyde sulfoxylate , 0 . 12 g ethylenediamine tetraacetic acid and 0 . 06 g iron ( ii ) sulfate heptahydrate in 33 . 18 g deionized water is added , followed by 34 . 5 g deionized water . the reactor temperature is increased to 50 ° c . within 3 hours and then kept constant . then a solution of 0 . 29 g p - menthane hydroperoxide and 1 . 68 g potassium oleate in 23 . 0 g deionized water is added at time 3 hours for two hours at a feeding rate of 12 . 49 g / h . the reaction is stopped at a conversion of 60 to 80 %. at the end of the polymerisation a solution of 0 . 61 g potassium chloride , 6 . 29 g naphthalene sulfonic acid formaldehyde condensate , sodium salt and 0 . 42 g n , n - diethylhydroxyamine in 32 . 8 g deionized water is added , followed by 23 . 0 g deionized water . a solution of 1 . 16 g polyethylene oxide ( prepared according to the teaching of de 1 213 984 ) and 0 . 06 g ethylenediamine tetraacetic acid in 2 . 54 g deionized water is added , followed by 46 . 0 g deionized water . after 3 hours a solution of 4 . 12 g potassium oleate , 0 . 03 g potassium chloride and 0 . 36 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 21 . 7 g deionized water , followed by 46 . 0 g of deionized water . finally the latex has a solids content of ca . 31 %. the latex is then concentrated under stirring and nitrogen atmosphere in a water bath at 70 ° c . to a solid content of ca . 67 %. the reactor is charged with a solution of 26 . 8 g potassium oleate , 3 . 75 g potassium chloride and 0 . 73 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 1399 . 8 g deionized water . 324 . 8 g styrene are added . the reactor is pressed with nitrogen and evacuated . 791 . 0 g butadiene are added . the mixture is cooled to 15 ° c . 0 . 56 g p - menthane hydroperoxide in 34 . 5 g styrene is added , followed by 34 . 5 g deionized water . a solution of 0 . 59 g sodium formaldehyde sulfoxylate , 0 . 12 g ethylenediamine tetraacetic acid and 0 . 06 g iron ( ii ) sulfate heptahydrate in 33 . 18 g deionized water is added , followed by 34 . 5 g deionized water . the reactor temperature is increased to 25 ° c . within 3 hours and then kept constant . then a solution of 0 . 76 g p - menthane hydroperoxide and 4 . 19 g potassium oleate in 28 . 8 g deionized water is added at time 1 hour for 4 hours at a feeding rate of 8 . 44 g / h . the reaction is stopped at a conversion of 60 to 80 %. at the end of the polymerisation a solution of 0 . 61 g potassium chloride , 6 . 29 g naphthalene sulfonic acid formaldehyde condensate , sodium salt and 0 . 42 g n , n - diethylhydroxyamine in 32 . 8 g deionized water is added , followed by 23 . 0 g deionized water . a solution of 1 . 16 g polyethylene oxide ( prepared according to the teaching of de 1 213 984 ) and 0 . 06 g ethylenediamine tetraacetic acid in 2 . 54 g deionized water is added , followed by 46 . 0 g deionized water . after 3 hours a solution of 4 . 12 g potassium oleate , 0 . 03 g potassium chloride and 0 . 36 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 21 . 7 g deionized water , followed by 46 . 0 g of deionized water . finally the latex has a solids content of ca . 30 %. the latex is then concentrated under stirring and nitrogen atmosphere in a water bath at 70 ° c . to a solid content of ca . 67 %. the reactor is charged with a solution of 29 . 3 g potassium oleate , 3 . 75 g potassium chloride and 0 . 73 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 1405 . 5 g deionized water . 324 . 8 g styrene and 1 . 64 g n - dodecyl mercaptan are added . the reactor is pressed with nitrogen and evacuated . 791 . 0 g butadiene are added . the mixture is cooled to 15 ° c . 0 . 56 g p - menthane hydroperoxide in 34 . 5 g styrene is added , followed by 34 . 5 g deionized water . a solution of 0 . 59 g sodium formaldehyde sulfoxylate , 0 . 12 g ethylenediamine tetraacetic acid and 0 . 06 g iron ( ii ) sulfate heptahydrate in 33 . 18 g deionized water is added , followed by 34 . 5 g deionized water . the reactor temperature is increased to 50 ° c . within 3 hours and then kept constant . then a solution of 0 . 29 g p - menthane hydroperoxide and 1 . 68 g potassium oleate in 23 . 0 g deionized water is added at time 3 hours for two hours at a feeding rate of 12 . 49 g / h . the reaction is stopped at a conversion of 60 to 80 %. at the end of the polymerisation a solution of 0 . 61 g potassium chloride , 6 . 29 g naphthalene sulfonic acid formaldehyde condensate , sodium salt and 0 . 42 g n , n - diethylhydroxyamine in 32 . 8 g deionized water is added , followed by 23 . 0 g deionized water . a solution of 1 . 16 g polyethylene oxide ( prepared according to the teaching of de 1 213 984 ) and 0 . 06 g ethylenediamine tetraacetic acid in 2 . 54 g deionized water is added , followed by 46 . 0 g deionized water . after 3 hours a solution of 4 . 12 g potassium oleate , 0 . 03 g potassium chloride and 0 . 36 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 21 . 7 g deionized water , followed by 46 . 0 g of deionized water . finally the latex has a solids content of ca . 31 %. the latex is then concentrated under strirring and nitrogen atmosphere in a water bath at 70 ° c . to a solid content of ca . 67 %. the reactor is charged with a solution of 29 . 3 g potassium oleate , 3 . 75 g potassium chloride and 0 . 73 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 1405 . 5 g deionized water . 324 . 8 g styrene and 2 . 46 g n - dodecyl mercaptan are added . the reactor is pressed with nitrogen and evacuated . 791 . 0 g butadiene are added . the mixture is cooled to 15 ° c . 0 . 56 g p - menthane hydroperoxide in 34 . 5 g styrene is added , followed by 34 . 5 g deionized water . a solution of 0 . 59 g sodium formaldehyde sulfoxylate , 0 . 12 g ethylenediamine tetraacetic acid and 0 . 06 g iron ( ii ) sulfate heptahydrate in 33 . 18 g deionized water is added , followed by 34 . 5 g deionized water . the reactor temperature is increased to 50 ° c . within 3 hours and then kept constant . then a solution of 0 . 29 g p - menthane hydroperoxide and 1 . 68 g potassium oleate in 23 . 0 g deionized water is added at time 3 hours for two hours at a feeding rate of 12 . 49 g / h . the reaction is stopped at a conversion of 60 to 80 %. at the end of the polymerisation a solution of 0 . 61 g potassium chloride , 6 . 29 g naphthalene sulfonic acid formaldehyde condensate , sodium salt and 0 . 42 g n , n - diethylhydroxyamine in 32 . 8 g deionized water is added , followed by 23 . 0 g deionized water . a solution of 1 . 16 g polyethylene oxide ( prepared according to the teaching of de 1 213 984 ) and 0 . 06 g ethylenediamine tetraacetic acid in 2 . 54 g deionized water is added , followed by 46 . 0 g deionized water . after 3 hours a solution of 4 . 12 g potassium oleate , 0 . 03 g potassium chloride and 0 . 36 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 21 . 7 g deionized water , followed by 46 . 0 g of deionized water . finally the latex has a solids content of ca . 31 %. the latex is then concentrated under stirring and nitrogen atmosphere in a water bath at 70 ° c . to a solid content of ca . 67 %. the reactor is charged with a solution of 26 . 8 g potassium oleate , 3 . 75 g potassium chloride and 0 . 73 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 1399 . 8 g deionized water . 324 . 8 g styrene and 3 . 28 g n - dodecyl mercaptan are added . the reactor is pressed with nitrogen and evacuated . 791 . 0 g butadiene are added . the mixture is cooled to 15 ° c . 0 . 56 g p - menthane hydroperoxide in 34 . 5 g styrene is added , followed by 34 . 5 g deionized water . a solution of 0 . 59 g sodium formaldehyde sulfoxylate , 0 . 12 g ethylenediamine tetraacetic acid and 0 . 06 g iron ( ii ) sulfate heptahydrate in 33 . 18 g deionized water is added , followed by 34 . 5 g deionized water . the reactor temperature is increased to 25 ° c . within 3 hours and then kept constant . then a solution of 0 . 76 g p - menthane hydroperoxide and 4 . 19 g potassium oleate in 28 . 8 g deionized water is added at time 1 hour for 4 hours at a feeding rate of 8 . 44 g / h . the reaction is stopped at a conversion of 60 to 80 %. at the end of the polymerisation a solution of 0 . 61 g potassium chloride , 6 . 29 g naphthalene sulfonic acid formaldehyde condensate , sodium salt and 0 . 42 g n , n - diethylhydroxyamine in 32 . 8 g deionized water is added , followed by 23 . 0 g deionized water . a solution of 1 . 16 g polyethylene oxide ( prepared according to the teaching of de 1 213 984 ) and 0 . 06 g ethylenediamine tetraacetic acid in 2 . 54 g deionized water is added , followed by 46 . 0 g deionized water . after 3 hours a solution of 4 . 12 g potassium oleate , 0 . 03 g potassium chloride and 0 . 36 g naphthalene sulfonic acid formaldehyde condensate , sodium salt in 21 . 7 g deionized water , followed by 46 . 0 g of deionized water . finally the latex has a solids content of ca . 30 %. the latex is then concentrated under stirring and nitrogen atmosphere in a water bath at 70 ° c . to a solid content of ca . 67 %. comparative example 1 shows suitable polymer and foam but disturbing odor properties . moreover , comparative example 2 shows insufficient polymer and foam but the desired odor properties . in contrast thereto , the aqueous rubber dispersions according to the present invention show the desired odor properties , i . e . the odor intensity is equal or lower than 1 . at the same time the mooney viscosity is in the desired region , namely below 155 . the foam properties are matching the expectations as well .