text: fig1 is a perspective view of a test sample useful with the present invention . the sample 10 may comprise a laminated structure of composite materials such as glass filaments or graphite filaments embedded in resin matrices with the specimen shaped as a thin walled tube or cylinder having an external surface and an internal surface . the test samples are preferably short cylinders of approximately four inches in diameter . a short specimen is used because the load transfer mechanism insures uniformity of axial stress even at the stress ends . a short length is also desirable from a buckling standpoint . wall thicknesses will vary depending upon the number and thickness of piles of composite material . when a specimen is formed from a tape for example , complimentary structures will be formed by wrapping the tape or laminate in opposite direction for the complimentary specimen . as will be described further hereinbelow , complimentary structures may be necessary to achieve a failure envelope for quadrants ii , iii , and iv of a biaxial stress plane . a sample such as illustrated in fig1 is tested in apparatus in accordance with the invention such as the embodiment shown in exploded view in fig2 . the apparatus includes an upper platen 20 , a lower platen 22 , and an outer pressure collet 24 . the platens and collet are preferably made of hardened steel ( e . g . 4344 or 300 m ). alternatively , hardened inserts may be used on the surfaces where the load is applied to a test sample . platen 20 includes a cylindrical bottom portion 26 and a top portion 28 with a sample receiving surface 30 on the top portion 28 extending outwardly from cylindrical portion 26 . groove 32 is provided in top portion 28 for receiving an o ring which provides a hydraulic oil seal in the assembled test apparatus , and groove 31 receives thumb screws for retaining the platens within the collet . platen 22 is cylindrically shaped with the outer diameter corresponding to the diameter of the top portion 28 of platen 20 and with an inner diameter corresponding to the diameter of the cylindrical portion 26 of platen 20 . a groove 34 is provided in the outer surface of platen 22 for receiving an &# 34 ; o &# 34 ; ring oil seal . collet 24 has an inner cylindrical surface of diameter corresponding to the outer diameter of platen 22 and the diameter of the top portion 28 of platen 20 whereby the assembled platens can be inserted into collet 24 . thumbscrews 36 , 38 extend through collet 24 to engage groove 31 of platen 20 and maintain the assembled platens in position during a stress test . the top platen 20 and the outer pressure collet 24 have pressure channels through which pressure is exerted on a sample during the test procedures , as will be described further hereinbelow with reference to fig3 . referring now to fig3 a specimen 10 such as illustrated in fig1 is shown in the cross section view of the assembled test apparatus of fig2 . like elements in the several views have the same reference numerals . test sample 10 is mounted between platen 20 and platen 22 with the top of the sample butting surface 30 of platen 20 , and the bottom of the sample abutting surface 33 of platen 22 . o - rings 50 , 52 and 54 are provided in the grooves 32 , 34 and 56 of platens 20 and 22 to provide pressure seals for the test chamber in which sample 10 is mounted . the o - ring pressure seals should provide an oil seal to maintain pressure up to 8 , 000 psi . platen 20 includes a pressure line 60 through which hydraulic pressure can be applied to the internal surface of specimen 10 . advantageously , the hydraulic line may be connected to a silicone rubber bladder 62 to insulate the test sample from the hydraulic oil used for application of pressure . however , bladder 62 is not essential to operation of the test apparatus . similarly , a channel 64 is provided through collet 24 for the application of pressure to the exterior surface of sample 10 . again , a silicone rubber bladder 66 , similar to the bladder 62 , may be connected to channel 64 to receive the hydraulic oil and apply pressure to the exterior surface of sample 10 . the bladders 62 and 66 are toroidally shaped to abut the interior and exterior cylindrical surfaces , respectively , of the sample 10 . pins 70 and 72 may be provided in upper platen 20 to limit travel thereof when inserted into collet 24 whereby thumbscrews 36 and 38 can be properly seated in groove 31 in the exterior surface of platen 20 . metal lubricants such as a thin sheet of copper or lead are provided at either end of sample 10 in abutment with the platen surfaces to minimize restraint . the foils equalize loading of the specimen ends and compensate for slight irregularities and mismatch between the platens and the test sample . this minimizes blooms of the specimen ends , a problem frequently encountered in the compression testing of composites . the foil further insures uniformity of axial stress . additionally , the foil prevents the silicone rubber oil bladders from extruding under the specimen ends . in testing the specimen , the assembled platens and collet are placed in a hydraulic actuated load frame for the application of axial force . fig4 illustrates schematically all of the biaxial states of stress which can be imparted to a test specimen using the apparatus in accordance with the present invention . it will be noted that in each of illustrated cases the same principal stress states may be produced by applying axial stress , s ax and surface pressure , s h . thus , an axial load and surface pressure can generate all of the stress states producible by an axial load and torsion without the drawback of principal axes rotation . further , it can obtain compression -- compression , a stress state unobtainable in a torsion machine . as illustrated , the unit area 70 is receiving only axial stress and experiences only compression . by adding some surface pressure with the axial stress both compression and shear is realized as shown in 72 . by balancing the axial stress and surface pressure pure shear will be experienced by the sample shown at 74 . development of a failure envelope using the test apparatus in accordance with the present invention is illustrated in fig5 a - 5c . in fig5 a a specimen is tested by the application of axial compression and both internal pressure and external pressure to develop the failure envelope in quadrants ii and iii of the stress plane . as above described , the failure envelope indicates the point of failure of a specimen for varying stresses . by using a complimentary sample in which filament alignment in the composite is reoriented in a complimentary direction , a failure envelope for quadrants iii and iv is generated as illustrated in fig5 b . thus , by combining the failure envelope from fig5 a , and the failure envelope from fig5 b , the envelope for quadrants ii , iii and iv is realized as shown in fig5 c . to complete the envelope , as shown by the dotted line 80 , a sample would be subjected to stress by pulling in a conventional failure analysis test apparatus . the method of testing a material using the apparatus in accordance with the present invention provides accurate and reproducible stress analysis without the employment of torsion to test specimens . the invention has proved particularly advantageous in the testing of composites and laminar structures . while the invention has been described with reference to specific embodiments the description is illustrative and is not to be construed as limiting the scope of the invention . various applications , modifications , and changes may occur to those skilled in the art without departing from the true spirit and scope of the invention as defined by the appended claims .