How do epoxys cross-link?

What's the mechanism of cross-linkage for a typical household 2-party epoxy mix? I was working with some epoxy the other day and I was instructed to mix equal parts of epoxy and epoxy hardener. Stoichiometry at its finest. 


The hardener contained "polymercaptans amines" according to the label. Google told me that a mercaptan is a broad name for a class of thiols. Makes sense; the $\ce{-SH}$ group is likely strongly nucleophilic (to better pop open the epoxide rings). Amines contain the also nucleophilic $\ce{-NH2}$ group. 


However, what are *polymercaptan amines*? Do these contain both thiol and amine functional groups? And again, how does cross-linkage work? I presume that this involves opening the epoxide ring. But then does the resulting oxide anion attack another epoxide ring? Wouldn't we then need a 2:1 ratio of epoxide to hardener? 




**What's the mechanism of cross-linkage for a typical household 2-party epoxy mix?**


![enter image description here](https://i.stack.imgur.com/9xEvJ.png)


Considering the polymeric epoxy backbone, two functional groups can be distinguished that are chemically active.
The hydroxyl-groups may react with phenol-/urea-/melamine-formaldehyde resins at elevated temperatures. At room temperature reaction with for instance isocyanates is possible.
The epoxy group is very reactive, reaction enthalpy is around 96 kJ/mol typically, with many chemical species. Curing chemistries using phenol(ic) hardeners is for instance employed in powder coating applications whereas anhydride cure is often used in epoxy composite applications.
At room temperature however by far the largest groups of chemicals used are amine-functional curing agents capable of cross linking epoxy resins at room temperature.


![enter image description here](https://i.stack.imgur.com/mN6hp.png)


An epoxy group reacts with ONE amine-hydrogen, i.e. one hydrogen attached directly to a Nitrogen atom (hence also amine-hydrogen equivalent weight). Note that every time that an epoxy group is opened; one Hydroxyl group is generated (adhesion !, internal catalyst !, …). Initial chemical reaction builds linear molecular weight, the molecules get longer and longer giving (s)low viscosity increase.


The next step in the curing process is the linking of the chains with each other; cross linking. In order for this to occur it is necessary that each amine molecule will have more-than-two active amine-hydrogen’s. The inter-linking of larger molecules causes a rapid increase of the observed viscosity.
Sterical hindrance can result in non-fully chemical cure which can be remedied by means of for instance post-cure or the use of plasticisers.


![enter image description here](https://i.stack.imgur.com/1sSAf.png)


Non-reacted epoxy groups, either deliberately generated through off-stoichiometry or caused by non-full cure can undergo “hydroxyl-cure” catalysed by tert.-amine and heat (sun-light).


![enter image description here](https://i.stack.imgur.com/mGi3z.gif)


**What are polymercaptan amines? Do these contain both thiol and amine functional groups?**


Mercaptans have been used commercially for over 30 years to cure epoxies. Despite the numerous epoxy hardeners on the market, the mercaptans provide some unique properties. The main one is their ability to cure epoxies rapidly at ambient temperature. The other key property is that the mercaptans are less sensitive in their curing speed to mass of material than other hardeners. Thus, they can be used in thin-film cures. Additional factors in favor of the polymercaptans are their low toxicity compared to other hardeners, their light color, their excellent adhesion, and the ability to accelerate other amines and polyamides. 
 Polymercaptans are used when the speed of cure is important. Even the “fast”-cure amine systems are slow in comparison, especially when the mass of epoxy is small and a thin film is used. This has led to the use of the mercaptans in a wide variety of applications:
Consumer and industrial adhesives, Coatings, Sealants, Industrial patch and filler kits,Floor and flooring repair, Encapsulation, and Acceleration of other epoxy systems.


A number of commercial mercaptan hardeners are available. They are sold with and without amine accelerators. The polymercaptan without the accelerator (Capcure 3-800) allows the formulator to have more control over the cure speed and flexibility of the product. This material is also used to accelerate amine, amidoamine and polyamide curing of epoxies. The standard five-minute cure is obtained with the accelerated Capcure® 3830-81. The fastest polymercaptan (Capcure 40 sec HV) has a gel time of 40 seconds with a 25-gram mass. There is a more water-resistant version (Capcure WR-6) for exterior uses.


To sum up polymercaptan amines contains at least one pair of $\ce{SH}$ (thiol) groups and


an amine


**How does cross-linkage work?**


The chemistry of the mercaptan reactions is fairly straightforward. The tertiary amine catalyst forms a salt with the mercaptan to generate a mercaptide anion, which is a strong nucleophile. The mercaptide will readily open the epoxy. Reaction with another mercaptan group can regenerate the mercaptide anion, as illustrated in the Figure below:


![enter image description here](https://i.stack.imgur.com/VEocn.gif)


The low activation energy for the process allows the reaction to go at or below room temperature. Since heat is not necessary for the reaction to occur, it can cure in thin films even on metal substrates. The cure rate does slow as the mass gets smaller, and the film is thinner, but the decrease is not as dramatic as when using amine-based hardeners. 


**Wouldn't we then need a 2:1 ratio of epoxide to hardener?**


Another aspect of the mercaptan chemistry is the formulation flexibility. At a 1:1 weight ratio, there is an excess of epoxy compared to mercaptan groups. However, the tertiary-amine accelerator will cause the epoxy to self-cure. Thus, some variation in ratio is self-compensating: 
1. More epoxy will self-cure by the tertiary-amine accelerator; 
2. More mercaptan will still have epoxy groups with which to react;
3. More or less tertiary amine changes the rate of cure, but not significantly the final degree of cure.
Of course, deviating greatly from the 1:1 ratio will cause problems of incomplete cure. 


 5

"Epoxy" here refers to an epoxy resin, which is comprised of oligomers that contain at least two epoxide functional groups. Hardening agents, like polyamines and polysufides, react with the resin via nucleophilic attack on the epoxide (as you desribed). Because the hardening agent has multiple nucleophilic groups, it will react with multiple epoxy oligomers. Likewise, the epoxy oligomer reacts with multiple hardening agents. This allows a complex crosslinked network to form.


Looking at the MSDS for a typical epoxy hardener, "polymercaptan amines" is listed as a "blend." Likely this is just a mix of polysulfides and polyamines that was given an ambiguous name by the manufacturer. These molecules likely contain a varying number of nucleophilic functional groups.



> 
> Stoichiometry at its finest.
> 
> 
> 


The stoichiometry is actually not straightforward here at all. It is possible that the total number of epoxide groups in the resin equals the total number of nucleophilic groups in the hardener, but that isn't necessarily the case. The reason you get to mix the parts 1:1 is because the manufacturer provides an approprite blend of hardeners to provide the desired stoichiometry, whatever it may be.



> 
> But then does the resulting oxide anion attack another epoxide ring?
> 
> 
> 


This reaction certainly competes with attack by the hardening agent. Whether it is competitive enough to be relevant depends on the identity and available amount of the hardening agent. It may even intentionally utilized in the crosslinking process.


As a side note, it is unlikely that an alkoxide anion is involved here. Often times a Lewis acid catalyst is added to facilitate crosslinking, which would provide an alkoxide-Lewis acid adduct. Alternatively, there are plenty of hydrogen bond donors available in these mixtures, so a proton would likely be associated with the epoxide during the ring opening, providing a neutral alcohol upon completion of the reaction.