Impact of Various Catalysts on Transesterification of Used Cooking Oil and Foaming Processes of Polyurethane Systems

The search for new sources of raw materials that can be used in the synthesis of polyurethanes and other polymer groups is extremely important. Currently, according to the principles of green chemistry and a circular economy, waste materials with a high reuse potential are being sought. This article presents a way of obtaining used-cooking-oil-based compounds capable of participating in the reaction of polyurethane creation. The transesterification reaction can be carried out using a variety of homo- and heterogeneous acid or base catalysts. Here, we looked at the impact of selected catalysts on the course of transesterification reactions, the composition of the post-reaction mixture and the possibility of using the products in polyurethane foam synthesis. The raw materials and the products were analyzed by means of gel permeation chromatography, FTIR spectroscopy and 1H NMR. The polyurethane foam formation process was analyzed using a FOAMAT® apparatus.


Introduction
Two basic components are used for the synthesis of polyurethanes: polyhydric alcohols known as polyols and diisocyanates. Various methods of obtaining polyols from natural raw materials are described in the literature [1]. One of them is the transesterification of vegetable oils [2]. For this purpose, oils such as rapeseed oil, sunflower oil, palm oil and soybean oil can be used [3]. In addition, in recent years, the use of waste cooking oil as a raw material for the production of components applied in the synthesis of polyurethanes has attracted a lot of interest [2].
Transesterification is a generic name for one important class of reactions in organic chemistry in which one ester can be transformed into another via a partial alkoxy group exchange. In the process of the transesterification of vegetable oils, triglycerides (esters of fatty acids and glycerol) react with alcohol to form a mixture of fatty acid alkyl esters and glycerol.
The transesterification reaction is characterized by an equilibrium between the reactants [4]. The process is a sequence of three consecutive and reversible reactions in which the intermediates are di-and monoglycerides. According to the stoichiometry of the reaction, 1 mole of triglycerides reacts with 3 moles of alcohol. An excess of alcohol is used in practice to obtain higher yields of the products to allow for better phase separation of the esters and glycerol formed [5]. Redundant alcohol is typically used in biodiesel production, where a high degree of conversion of triglycerides to monoesters is required, and the unreacted transesterification agent is then removed from the mixture [6]. The effectiveness of the transesterification process of vegetable oils depends on many factors, including the type of catalyst, the molar ratio of alcohol to vegetable oil, the temperature and the purity of the reactants [7,8]. In contrast to the production of biodiesel, where monohydric alcohols, e.g., methanol [6], are used, at least a dihydric alcohol is required as a transesterification agent to obtain polyols. Most reports in the literature mention the use of glycerol, diethylene glycol and triethanolamine [9]. a transesterification agent. Based on a literature review, several catalysts with different properties were selected and used for the synthesis of polyols via transesterification. The reaction products were analyzed in terms of their composition. Their potential to be used as bio-polyols in the synthesis of rigid polyurethane foams was also assessed.

Materials
Used cooking oil (UCO) characterized by an iodine value of 104 gI 2 /100 g was supplied by local restaurants. Monoethylene glycol (MEG) was used as a transesterification agent and was supplied by Avantor Performance Materials Poland S.A (Gliwice, Poland). Nine different substances were used as catalysts: sodium hydroxide (NaOH), potassium hydroxide (KOH), aluminum hydroxide (Al(OH) 3  Poland) and polymeric methylene diphenyldiisocyanate (PMDI) with a free isocyanate groups content of 31 wt.% was supplied by Minova Ekochem S.A (SiemianowiceŚląskie, Poland). Distilled water was also used to prepare the polyurethane foams.

Transesterification of the Waste Cooking Oil
The reaction was carried out in a 500 mL flask equipped with a magnetic stirrer set at 800 rpm, at atmospheric pressure, under reflux conditions and in an inert gas environment. The oil (250 g) was placed in the reactor and the temperature was set to 175 • C. After reaching the desired temperature, MEG with a selected catalyst was added to the reactor. MEG was added in an amount equal to the molar ratio of the oil and the transesterification agent of 1:3. The catalyst was added in an amount of 0.15% by weight relative to the total mass of the reactants. The reaction was carried out for 2 h at 175 • C. The reaction conditions used were based on previous research and a literature review [2,20,21].

Characterization of the Bio-Polyols
The hydroxyl value (Hval) was determined in accordance with the PN-C-89052-03:1993 standard. The acid value (Aval) was determined in accordance with PN-EN ISO 660:2009. The water content in polyols was determined in accordance with PN-81/C-04959 using the Karl Fisher method. The chemical structures of bio-polyols were analyzed using an FTIR spectrometer from Thermo Fisher Scientific, model Nicolet iS5 equipped with an ATR accessory and a diamond crystal. Spectra were recorded in the infrared range of 4000-500 cm −1 . The number average molecular weight (Mn), weight average molecular weight (Mw) and dispersity (D) were determined using a gel permeation chromatography (GPC) analysis. GPC measurements were performed using a Knauer chromatograph equipped with a Plgel MIXED-E column and a refractometric detector.
The functionality (f ) of the final bio-polyols was calculated following the formula below: The chemical composition of each sample and the effect of the catalyst on the transesterification reaction were analyzed using 1 H NMR analysis. Spectra were recorded with a Bruker Avance 500 MHz spectrometer (Billerica, MA, USA) with CDCl 3 as the solvent at a temperature of 298 K. The tetramethylsilane (TMS) signal was used as a reference for the chemical shift values. The spectra were analyzed using MestReNova software (Mestrelab Research, S.L., Spain, Version 14.0.0).

Characterization of the Foaming Process
The bio-polyols obtained in the transesterification reaction were used to analyze the foaming process. The polyol premix (bio-polyol, catalyst, surfactant, water) was mixed for 30 s and then an isocyanate was added. Next, the whole reaction mixture was stirred for 5 s and poured into an open mold. The formulations of foams are summarized in Table 1. The weight of the isocyanate needed was calculated by taking into account the Hval of the resultant bio-polyols so that the value of the isocyanate index was equal to 1. An analysis of the polyurethane foaming process using a foam qualification system FOAMAT ® (Format Messtechnik GmbH, Karlsruhe, Germany) was carried out in a form made of cardboard. The foam qualification system FOAMAT ® consists of an ultrasonic sensor, a thermocouple, a pressure measurement and curing monitor devices. The measurement sequence and data processing are controlled using the "FOAM ver.3.1" software. Dielectric polarization gives insight into the electrochemical processes that occur during foam formation. This parameter is essentially determined by chain-like molecules with a large dipole moment due to their polar ends (-OH, -NCO). Chain formation precedes the crosslinking reaction that ultimately suppresses all dipole mobility during the curing process. At the same time, it is possible to measure changes in the height and speed of growth of the expanding polyurethane system.

Results and Discussion
The transesterification reactions were carried out in the presence of four groups of catalysts: acids, bases, salts and an oxide. The selected catalysts are among the most commonly used in transesterification reactions. Figure 1 shows photographs of the products of the used cooking oil transesterification with ethylene glycol using the following catalysts: H 2 SO 4 , H 3 PW 12 O 40 , NaOH, KOH, Al(OH) 3 , CH 3 COOK, (CH 3 COO) 2 Zn, K 2 CO 3 and CaO.
The labels assigned to the polyols include the type of raw material (UCO) and the type of catalyst that was used in the transesterification reaction.
In the case of bio-polyols UCO_H 3 PW 12 O 40 and UCO_Al(OH) 3 , separation of the products was observed, which may indicate a lack of or a low level of conversion of UCO in the reaction with MEG. The separation indicated that the mixture contained substances that did not mix and had different properties, i.e., polar (ethylene glycol) and non-polar (UCO). The remaining polyols were uniform liquids. Only a small amount of dark liquid (glycerol) or light sediment (saponification products) was observed at the bottom of the cylinder [22]. In addition, it was observed that the UCO_H 2 SO 4 polyol had a much darker color compared with the others ones. The labels assigned to the polyols include the type of raw material (UCO) and the type of catalyst that was used in the transesterification reaction.
In the case of bio-polyols UCO_H3PW12O40 and UCO_Al(OH)3, separation of the products was observed, which may indicate a lack of or a low level of conversion of UCO in the reaction with MEG. The separation indicated that the mixture contained substances that did not mix and had different properties, i.e., polar (ethylene glycol) and non-polar (UCO). The remaining polyols were uniform liquids. Only a small amount of dark liquid (glycerol) or light sediment (saponification products) was observed at the bottom of the cylinder [22]. In addition, it was observed that the UCO_H2SO4 polyol had a much darker color compared with the others ones.
All transesterification reactions were performed at equivalent molar ratios. Neither byproducts nor catalysts were removed from the reaction mixture. This approach reduced the consumption of energy, water and chemicals by reducing the number of process steps.
The transesterification reaction products were monitored through GPC, 1 H NMR and FTIR analyses.
The transesterification of UCO with MEG results in a product that is a mixture of different compounds. Figure 2 shows the theoretical course of the transesterification reaction of UCO with MEG [8,[23][24][25].  All transesterification reactions were performed at equivalent molar ratios. Neither byproducts nor catalysts were removed from the reaction mixture. This approach reduced the consumption of energy, water and chemicals by reducing the number of process steps.
The transesterification reaction products were monitored through GPC, 1 H NMR and FTIR analyses.
The transesterification of UCO with MEG results in a product that is a mixture of different compounds. Figure 2 shows the theoretical course of the transesterification reaction of UCO with MEG [8,[23][24][25]. The labels assigned to the polyols include the type of raw material (UCO) and the type of catalyst that was used in the transesterification reaction.
In the case of bio-polyols UCO_H3PW12O40 and UCO_Al(OH)3, separation of the products was observed, which may indicate a lack of or a low level of conversion of UCO in the reaction with MEG. The separation indicated that the mixture contained substances that did not mix and had different properties, i.e., polar (ethylene glycol) and non-polar (UCO). The remaining polyols were uniform liquids. Only a small amount of dark liquid (glycerol) or light sediment (saponification products) was observed at the bottom of the cylinder [22]. In addition, it was observed that the UCO_H2SO4 polyol had a much darker color compared with the others ones.
All transesterification reactions were performed at equivalent molar ratios. Neither byproducts nor catalysts were removed from the reaction mixture. This approach reduced the consumption of energy, water and chemicals by reducing the number of process steps.
The transesterification reaction products were monitored through GPC, 1 H NMR and FTIR analyses.
The transesterification of UCO with MEG results in a product that is a mixture of different compounds. Figure 2 shows the theoretical course of the transesterification reaction of UCO with MEG [8,[23][24][25].   The 1 H NMR analysis confirmed that the resulting transesterification products were a mixture of many compounds, and their composition depended on the catalyst used. The presence of the MEG monoester and MEG diester; 1-/2-monoglycerides (1-MG/2-MG); 1,2-/1,3-diglycerides (1,2-DG/1,3-DG); unreacted substrates, i.e., triglycerides (TG) and MEG, as well as the glycerol formed in the reaction ( Figure 2) were found. The samples tested were not purified or separated in any manner, which resulted in the appearance of some overlapping signals. The analysis of the signals was based on the studies of [26,27].  The 1 H NMR analysis confirmed that the resulting transesterification products were a mixture of many compounds, and their composition depended on the catalyst used. The presence of the MEG monoester and MEG diester; 1-/2-monoglycerides (1-MG/2-MG); 1,2-/1,3-diglycerides (1,2-DG/1,3-DG); unreacted substrates, i.e., triglycerides (TG) and MEG, as well as the glycerol formed in the reaction ( Figure 2) were found. The samples tested were not purified or separated in any manner, which resulted in the appearance of some overlapping signals. The analysis of the signals was based on the studies of [26,27].  The use of CaO and (CH3COO)2Zn catalysts led to the formation of MEG monoesters (signals P and V) without the production of MEG diesters (signal O). On the other hand, it was observed that significant amounts of 1,2DG (signal T) and small amounts of 1-MG and 2-MG (signals Q and S, respectively) were produced, indicating the incomplete conversion of UCO. Low-intensity peaks from the presence of MEG monoesters (signals P and V) were also observed for the H2SO4 catalyst.
The formation of ethylene glycol diesters (signal O), as well as high amounts of 1-MG and 2-MG (signals Q and S, respectively), were observed when H2SO4, NaOH, KOH, CH3COOK and K2CO3 were used as catalysts. However, signals from MEG monoesters (signals P and V) were not observed when using the abovementioned catalysts. The presence of unreactive ethylene glycol diesters in a bio-polyol is highly undesirable and significantly reduces the product's suitability for use as a component in polyurethane formulations.
In the case of Al(OH)3 and H3PW12O40 as catalysts, no transesterification reaction was observed.
The products were also analyzed using GPC. The chromatograms of the products and data are shown in Figure 5 and Table 2, whereas Table 3 presents their selected properties. The use of CaO and (CH 3 COO) 2 Zn catalysts led to the formation of MEG monoesters (signals P and V) without the production of MEG diesters (signal O). On the other hand, it was observed that significant amounts of 1,2DG (signal T) and small amounts of 1-MG and 2-MG (signals Q and S, respectively) were produced, indicating the incomplete conversion of UCO. Low-intensity peaks from the presence of MEG monoesters (signals P and V) were also observed for the H 2 SO 4 catalyst.
The formation of ethylene glycol diesters (signal O), as well as high amounts of 1-MG and 2-MG (signals Q and S, respectively), were observed when H 2 SO 4 , NaOH, KOH, CH 3 COOK and K 2 CO 3 were used as catalysts. However, signals from MEG monoesters (signals P and V) were not observed when using the abovementioned catalysts. The presence of unreactive ethylene glycol diesters in a bio-polyol is highly undesirable and significantly reduces the product's suitability for use as a component in polyurethane formulations.
In the case of Al(OH) 3 and H 3 PW 12 O 40 as catalysts, no transesterification reaction was observed.
The products were also analyzed using GPC. The chromatograms of the products and data are shown in Figure 5 and Table 2, whereas Table 3 presents their selected properties.     GPC separates based on the hydrodynamic volume of the analytes. If the analyzed compounds have approximately similar hydrodynamic volumes, they will appear as one peak in a chromatogram, as they elute from the chromatograph column at a similar time. The separation resolution of the chromatograph that was used does not allow for the separation of a mixture consisting of monoglycerides and MEG monoesters, nor diglycerides and MEG diesters, because they have very similar hydrodynamic volumes and molar masses [23].
The chromatograms show peaks coming from triglycerides (peak 1), diglycerides or MEG diesters or a mixture of these two compounds (peak 2), monoglycerides and MEG monoesters or a mixture of these two compounds (peak 3), and unreacted MEG and glycerol (peak 4). It was observed that the lowest yield of the reaction was obtained with the use of the catalysts Al(OH) 3 and H 3 PW 12 O 40 , which was confirmed by the highest content of triglyceride (peak 1). The content of triglyceride in these products was about 87%, whereas only negligible amounts of di-and monoglyceride/esters were present. This showed that the transesterification reaction catalyzed by H 3 PW 12 O 40 and Al(OH) 3 was almost completely absent and the catalysts were ineffective under the conditions of the reactions. It can be concluded that the two layers present in these products ( Figure 1) were the UCO layer and the unreacted MEG layer.
The products obtained as a result of transesterification carried out with the use of the catalysts containing potassium and sodium ions (strongly basic), i.e., NaOH, KOH, K 2 CO 3 and CH 3 COOK, were characterized using the highest contents of monoglycerides/MEG monoesters desirable as components for the production of polyols. These products were characterized by a monoglycerides/MEG monoesters content of over 50 wt.% and a content of unreacted UCO below 2 wt.%. The bio-polyols UCO_H 2 SO 4 , UCO_CaO and UCO_(CH 3 COO) 2 Zn were characterized by a monoglycerides/MEG monoesters content of about 40 wt.%. From the values of reaction rate constants reported in the literature, it follows that reactions catalyzed by alkali catalysts occur several hundred or even several thousand times faster than those catalyzed by acids. Therefore, higher triglyceride conversion rates were obtained with alkali catalysts in the case of the experiments conducted. In their case, the step that determines the speed of the reaction is the last step, i.e., the transition from monoglyceride to glycerol [22,25].
One of the most important properties of bio-polyols is their Hval, which determines the application of a particular polyol and its effect on the properties of polyurethane foams. The values of Hval, Aval, Mn and Mw dispersity, and functionality are presented in Table 3. The polyols UCO_ KOH, UCO_K 2 CO 3 , UCO_CH 3 COOK and UCO_NaOH had the highest values of Hval with 281, 280, 280 and 269 mgKOH/g, respectively. All polyols had Aval values below 1.0 mgKOH g, with the exception of the polyol catalyzed with sulfuric acid (5.55 mg KOH/g and a low content of water (<0.05 wt.%).
FTIR analyses of the products were also performed ( Figure 6). The FTIR spectra of the polyols synthesized in our experiment correlated with the GPC results, as well as the hydroxyl numbers. The broad band at 3340-3390 cm −1 corresponded to free hydroxyl groups in the bio-polyols. The region of hydroxyl group vibration is shown in detail in Figure 6a. The absorption intensities were the highest for UCO_KOH, UCO_NaOH and UCO_K 2 CO 3 . The lower the hydroxyl number, the lower the absorption intensity. For UCO, there was no peak in this area, while for the transesterification products catalyzed with H 3 PW 12 O 40 and Al(OH) 3 , the peak in this area originated from the unreacted MEG and had a very low intensity. Hval-hydroxyl number; Aval-acid number; Mn-number average molecular weight; Mwweight average molecular weight; D-dispersity; H2O%-water content.
FTIR analyses of the products were also performed ( Figure 6). The FTIR spectra of the polyols synthesized in our experiment correlated with the GPC results, as well as the hydroxyl numbers. The broad band at 3340-3390 cm −1 corresponded to free hydroxyl groups in the bio-polyols. The region of hydroxyl group vibration is shown in detail in Figure 6a. The absorption intensities were the highest for UCO_KOH, UCO_NaOH and UCO_K2CO3. The lower the hydroxyl number, the lower the absorption intensity. For UCO, there was no peak in this area, while for the transesterification products catalyzed with H3PW12O40 and Al(OH)3, the peak in this area originated from the unreacted MEG and had a very low intensity.  In the 3000-2800 cm −1 range (Figure 6b), two intense bands at 2920 and 2850 cm −1 were observed due to stretching vibrations of the CH 2 groups of the aliphatic structures in the chain backbone [29]. An absorption band at 1735-1743 cm −1 corresponded to the carbonyl C=O bonds in the ester groups (Figure 6c). That peak was the highest for the unreacted UCO, UCO_H 3 PW 12 O 40 and UCO_AL(OH) 3 . As the transesterification reaction progressed toward monoglycerides, the intensity of this peak decreased. Foaming a polyurethane system is the most important stage during polyurethane (PUR) foam preparation. In this process, the reaction mixture increases its volume several dozen times. During the foaming process, both foaming and gelling reactions take place in parallel, and thus, each component added to the polyurethane system affects the foaming process. The chemical structure of bio-polyol, its Hval and the presence of additional groups in its structure, e.g., an amine group, have an impact on the foaming process, as shown in previous studies [30]. Given the fact that the reaction to obtain bio-polyols (with characteristics presented in Table 3) is a single-stage process and the catalyst is not removed from the reaction medium, it is important to analyze the effect of the polyols obtained with various catalysts on the foaming process.
In order to analyze the foaming process of PUR systems, seven different bio-polyols were selected. Figure 7 shows the effect of the bio-polyols obtained via transesterification with the use of various catalysts ((CH 3 COO) 2 Zn, CH 3 COOK, NaOH, KOH, CaO, K 2 CO 3 , H 2 SO 4 ) on the course of the foaming process of polyurethane systems, including the temperature in the foam core (a), change in dielectric polarization (b), pressure (c) and foam height (d). The course of the foaming process was analyzed for a period of 600 s. The formulations of the PUR systems are given in Table 1. Table 4 summarizes the parameters of the foaming process, i.e., characteristic times for the formation of a foam, maximum temperature and pressure, and shrinkage. In the 3000-2800 cm −1 range (Figure 6b), two intense bands at 2920 and 2850 cm −1 were observed due to stretching vibrations of the CH2 groups of the aliphatic structures in the chain backbone [29]. An absorption band at 1735-1743 cm −1 corresponded to the carbonyl C=O bonds in the ester groups (Figure 6c). That peak was the highest for the unreacted UCO, UCO_H3PW12O40 and UCO_AL(OH)3. As the transesterification reaction progressed toward monoglycerides, the intensity of this peak decreased. Foaming a polyurethane system is the most important stage during polyurethane (PUR) foam preparation. In this process, the reaction mixture increases its volume several dozen times. During the foaming process, both foaming and gelling reactions take place in parallel, and thus, each component added to the polyurethane system affects the foaming process. The chemical structure of bio-polyol, its Hval and the presence of additional groups in its structure, e.g., an amine group, have an impact on the foaming process, as shown in previous studies [30]. Given the fact that the reaction to obtain bio-polyols (with characteristics presented in Table 3) is a single-stage process and the catalyst is not removed from the reaction medium, it is important to analyze the effect of the polyols obtained with various catalysts on the foaming process.
In order to analyze the foaming process of PUR systems, seven different bio-polyols were selected. Figure 7 shows the effect of the bio-polyols obtained via transesterification with the use of various catalysts ((CH3COO)2Zn, CH3COOK, NaOH, KOH, CaO, K2CO3, H2SO4) on the course of the foaming process of polyurethane systems, including the temperature in the foam core (a), change in dielectric polarization (b), pressure (c) and foam height (d). The course of the foaming process was analyzed for a period of 600 s. The formulations of the PUR systems are given in Table 1. Table 4 summarizes the parameters of the foaming process, i.e., characteristic times for the formation of a foam, maximum temperature and pressure, and shrinkage.  It was observed that when using different bio-polyols, different temperatures were achieved in the foam core. The highest temperatures, reaching approx. 150 • C, were found in the materials obtained with the following bio-polyols: UCO_KOH, UCO_NaOH, UCO_CH 3 COOK and UCO_K 2 CO 3 (Figure 7a). The lowest temperature of 133 • C was inside the PUR foam obtained with the use of bio-polyol catalyzed with CaO. This biopolyol had the lowest hydroxyl number and the lowest monoglyceride content.
On the basis of the dielectric polarization measurements (Figure 7b), it was found that the PUR systems obtained using the bio-polyols synthesized with (CH 3 COO) 2 Zn and CH 3 COOK were characterized by the highest reactivity. In this case, the dielectric polarization reached approx. 10% of its initial value the fastest, after about 300 s. A dielectric polarization value close to 0 indicates that the reactions took place and there was a small amount of free hydroxyl and isocyanate groups in the mixture. The systems with the bio-polyols UCO_K 2 CO 3 and UCO_KOH were also very reactive. The systems containing UCO_MEG_H 2 SO 4 and UCO_CaO were characterized by the slowest decrease in dielectric polarization, and thus, in reactivity.
The pressure exerted by the forming foam on the measuring table was also analyzed. The highest pressures were in the case of the foams obtained with the bio-polyols UCO_NaOH, UCO_KOH and UCO_K 2 CO 3 (Figure 7c). The foams that reached high pressures also had high shrinkage values (Table 4, Figure 8).
The above-described analyses show that the transesterification carried out with the use of reactive catalysts such as NaOH or KOH led to the formation of side products, namely, MEG diesters, that do not have hydroxyl groups capable of reacting with isocyanates. The bio-polyols contained different amounts of MEG and glycol, which are small molecules compared with the mono-and diglycerides/esters that are formed in the reaction. Consequently, MEG and glycol have a greater potential to react with isocyanate because there are fewer steric hindrances between these components. MEG and glycol, which are involved in the formation of polyurethane bonds, cause the reaction to produce a polyurethane foam with a greater number of rigid segments. Figure 8 shows a cross-section of the foams in a cardboard tube 24 h after their synthesis. The foams PU_UCO_H 2 SO 4 , PU_UCO_CaO and PU_UCO_(CH 3 COO) 2 Zn had the highest dimensional stability and adhered well to the cardboard tube wall. The catalysts used to obtain those foams led to the formation of MEG-based monoesters and diglycerides. All other foams, which contained bio-polyols characterized by the presence of MEG diesters (non-reactive compounds) in the absence of MEG monoesters and a higher amount of monoglycerides, were not dimensionally stable and exhibited significant shrinkage, especially the PU_UCO_CH 3 COOK foam. The above-described analyses show that the transesterification carried out with the use of reactive catalysts such as NaOH or KOH led to the formation of side products, namely, MEG diesters, that do not have hydroxyl groups capable of reacting with isocyanates. The bio-polyols contained different amounts of MEG and glycol, which are small molecules compared with the mono-and diglycerides/esters that are formed in the reaction. Consequently, MEG and glycol have a greater potential to react with isocyanate because there are fewer steric hindrances between these components. MEG and glycol, which are involved in the formation of polyurethane bonds, cause the reaction to produce a polyurethane foam with a greater number of rigid segments. Figure 8 shows a cross-section of the foams in a cardboard tube 24 h after their synthesis. The foams PU_UCO_H2SO4, PU_UCO_CaO and PU_UCO_(CH3COO)2Zn had the highest dimensional stability and adhered well to the cardboard tube wall. The catalysts used to obtain those foams led to the formation of MEG-based monoesters and diglycerides. All other foams, which contained bio-polyols characterized by the presence of MEG diesters (non-reactive compounds) in the absence of MEG monoesters and a higher

Conclusions
In the conducted research, transesterification reactions were carried out with the use of selected catalysts. Depending on the catalyst used, a different composition of the final mixture was obtained. The following products were identified in the final mixture: glycerol, MEG, triglyceride, diglyceride, monoglyceride, MEG diesters and an MEG monoester.
Two of the selected catalysts worked very poorly, as evidenced by the low proportion of di-and monoglycerides/MEG esters in the post-reaction mixture. Those were the catalyst H 3 PW 12 O 40 , for which the amount of monoglyceride/MEG monoester was 1.14%, and Al(OH) 3 , with 0.37% of monoglyceride/MEG monoester in the final product mixture. The use of those two catalysts in amounts greater than 0.15% by weight and their effectiveness at higher temperatures than 175 • C or extended testing times above 2 h were not studied because such procedures are not compatible with the principles of green chemistry.
The efficiency of monoglyceride/ethylene glycol monoester formation was between 39 and 53 wt.% for the reactions catalyzed by sulfuric acid and potassium hydroxide, respectively. The products obtained as a result of transesterification carried out with the use of the catalysts containing potassium and sodium ions (strongly basic), i.e., NaOH, KOH, K 2 CO 3 and CH 3 COOK, were characterized by the highest contents of monoglycerides. The products were characterized by a monoglyceride content of over 50% and a content of unreacted used cooking oil below 2%. However, those compounds also catalyzed the formation of MEG diesters. A MEG diester does not contain reactive hydroxyl groups that could participate in the polyurethane bond formation reaction; therefore, they are not desirable products.
The use of H 2 SO 4 , CaO and (CH 3 COO) 2 Zn as catalysts resulted in products containing ethylene glycol monoesters. No ethylene glycol diesters were observed in these cases. The products obtained using these catalysts were characterized by the presence of monoglyceride/ethylene glycol monoester content of about 40 wt.%. The resultant bio-polyols had hydroxyl values in the range of 170-280 mg KOH/g. Rigid polyurethane foams were obtained from the synthesized polyols.
The catalyst (CH 3 COO) 2 Zn can be considered the best choice. The bio-polyol obtained with it was characterized by both higher hydroxyl value and higher ethylene glycol monoglycerol/monoester content compared with the bio-polyol obtained in the CaOcatalyzed reaction. The polyurethane system obtained using the bio-polyol obtained in the (CH 3 COO) 2 Zn-catalyzed reaction was also characterized by the fastest start time (highest reactivity) and lowest shrinkage, as well as the best adhesion to the test cardboard tube 24 h after manufacture.