The Structure of Monomeric Hydroxo-CuII Species in Cu-CHA. A Quantitative Assessment

Using EPR and HYSCORE spectroscopies in conjunction with ab initio calculations, we assess the structure of framework-bound monomeric hydroxo-CuII in copper-loaded chabazite (CHA). The species is an interfacial distorted square-planar [CuIIOH(O-8MRs)3] complex located at eight-membered-ring windows, displaying three coordinating bonds with zeolite lattice oxygens and the hydroxo ligand hydrogen-bonded to the cage. The complex has a distinctive EPR signature with g = [2.072 2.072 2.290], CuA= [30 30 410] MHz, and HA = [−13.0 −4.5 +11.5] MHz, distinctively different from other CuII species in CHA.

materials promoting a wide range of important catalytic transformations, 1 feature a plurality of different copper species ranging from monomeric copper sites 2 3,4 and polynuclear clusters, 5 each one related to specific catalytic functions. 6−8 These different copper species are crucially related to the zeolite composition and exhibit unique spectroscopic features, which reflect specific electronic structures that can make key contributions to reactivity. For example, specific (μ-oxo)dicopper(II) species ([Cu 2 O] 2+ ) in Cu-CHA have been recently shown to react with methane to form methanol at low temperature. 3 The precursors of such copper-coupled dimers are paramagnetic monocopper hydroxo species ([Cu(OH)] + ). 8,9 Despite their relevance, however, geometric and electronic structure/function correlations are scanty.
Recent studies 10−14 indicate the presence of two major Cu sites in activated Cu-CHA, namely, interfacial complexes coordinated with four oxygen donor atoms of the sixmembered-ring (6MR) cavities ([Cu II (O-6MR) 4 ]), whereby Cu II is stabilized by two neighboring charge-balancing Al 3+ framework ions, and [Cu II (OH)] + species at eight-memberedring (8MR) cages next to an isolated Al 3+ ion. Importantly, only the second complex is redox-active, allowing for Cu II /Cu I redox cycles. 8,9,13 The relative population of the two species depends on the number and distribution of Al ions in the framework and on the Cu/Al ratio. Materials with low Si/Al and Cu/Al ratios should contain predominantly [Cu II (O-6MR) 4 ] species, while materials with high Si/Al and Cu/Al ratios are dominated by [Cu II (OH)] + species. 15,16 First suggested by Valyon,17 [Cu II (OH)] + has been identified in high loaded Cu-CHA (Si/Al = 11−15) after dehydration in O 2 /He by Giordanino and Borfecchia et al. 13,18 through characteristic IR stretching and bending bands at 3656 and 905 cm −1 . Electron paramagnetic resonance (EPR) spectroscopy has been used to indirectly evaluate the amount of [Cu II (OH)] + ; 19−22 however, no direct detection of these species in dehydrated Cu-CHA has been reported so far. Herein we identify the EPR signature of framework-bound [Cu II (OH)] + species, elucidating their structure that is different from past assignments. 2,8,13,15,21−23 The structural requirement for the stabilization of [Cu II (OH)] + is based on the availability of single Al framework sites, which are assumed to be populated after 2Al sites. 12 Paolucci et al. 12 Figure 1a) to about 40% of total Cu (point D in Figure 1a). The samples were activated by adopting conditions known to maximize [Cu II (OH)] + sites (dehydration at 523 K under an O 2 atmosphere), 8 and the corresponding EPR spectra are shown in Figure 1b.
The CW-EPR spectrum of Cu-CHA with composition Si/Al = 7; Cu/Al = 0.001 (spectrum A in Figure 1b) shows the characteristic hyperfine structure due to coupling of the electronic spin S = 1/2 of the Cu II ion with the nuclear spin I = 3/2 of both copper isotopes 63 Cu and 65 Cu (natural abundances 69.17% and 30.83%, respectively) with g || > g ⊥ > g e . Computer simulation of the spectrum ( Figure S1, Table 1 and Table S1) reveals the contribution of a single species with spin-Hamiltonian parameters corresponding to the [Cu II (O-6MR) 4 ]. Previous work based on 17 O EPR assessed the singly occupied molecular orbital (SOMO) character to be predominantly Cu d x 2 −y 2 with a covalent contribution of about 30% from the coordinating framework oxygen donor atoms. 25 Quantitative assessment indicates that the EPR-active Cu is 84% of the total Cu content. On increasing the Cu loading, the amount of EPR-active Cu II decreases due to the formation of antiferromagnetic dimer species or Cu reduction (Section S3 Supporting Information). The EPR spectrum of sample B (Figure 1b) shows the presence of at least two Cu II species with similar parameters (Table 1 and Table S1) (Table 1 and Table S1), still in agreement with a dominant metal d x 2 −y 2 character of the SOMO (see Section S5 Supporting Information). These values remain constant in the interval 10 K−RT, and the species corresponds to 14% of total Cu, in good agreement with data from refs 8 and 12. At higher Cu loading (sample D, Si/Al = 12 and Cu/Al = 0.67) the amount of EPR-active Cu II falls to 45% of total Cu, while the contribution of [Cu II (OH)] + is 16%. We remark that this value corresponds only to framework-bound isolated species that did not undergo dimerization or reduction under the adopted experimental conditions. Further details on the quantitative aspects and comparison with literature data are reported as supporting material (Section S3 Supporting Information) The distinctive feature of the [Cu II (OH)] + species is expected to be the 1 H (I = 1/2) hyperfine coupling of the coordinated hydroxo group. This is too small to be detected in standard CW-EPR experiments but can be measured by hyperfine techniques, which allow recovering the nuclear magnetic resonance (NMR) transitions of magnetically active nuclei coupled to the unpaired electron spin, with sub-MHz resolution.
Hyperfine sublevel correlation (HYSCORE) experiments were therefore used to interrogate each sample, and the spectra, recorded at a magnetic field corresponding to the g ⊥  Figure 1a) is shown in Figure S1. (c) X-band 1 H HYSCORE spectra recorded at a magnetic field position corresponding to g = 2.072 (g ⊥ ) and T = 10 K. Experimental details are given in the Supporting Information. component of the CW-EPR spectrum, are presented in Figure  1c. We remark that under the experimental conditions Cucoordinated water is absent 8,13 and the only source of significant 1 H hyperfine coupling must arise from coordinated hydroxo ligands. All HYSCORE spectra display a complex signal in the low-frequency region of the spectrum due to the interaction of the unpaired electron with a nearby 27 Al nucleus (I = 5/2). 26  HYSCORE experiments indicate that large proton couplings, amenable to Cu coordinated to hydroxo ligands, emerge at zeolite compositions in agreement with predictions based on the distribution reported in Figure 1a. To correlate the observed 1 H hyperfine coupling with the specific EPR features observed in sample C, selective HYSCORE experiments have been carried out at EPR transitions pertaining exclusively to such species (Figure 2a−c). Figure 2 shows the electron spin echo (ESE)-detected EPR spectrum of sample C along with the simulation of the two main contributing species ([Cu II (O-6MR) 4 ], green line, and [Cu II (OH)] + , in orange) identified by simulation of the continuous wave (CW) experiments ( Figures  S1 and S4). The spectrum corresponds to the absorption of the CW-EPR signal, and the simulated components show that the spectral features of the two species overlap at high field (g ⊥ ), while they are sufficiently separated at low field to allow for selective excitation of the 1 H NMR transitions. The HYSCORE spectrum recorded at position 1 (Figure 2a) shows no trace of 1 H coupling, while clearly showing the expected 27 Al signal. The corresponding spectrum recorded at position 2 (Figure 2b), coinciding with the m I = −3/2 transition of the second Cu II species (orange trace) shows the distinct 1 H cross-peaks, allowing the unambiguous assignment of this species to the monomeric hydroxo-Cu II species.
To translate the spectroscopic features extracted from the analysis of the EPR and HYSCORE experiments into a microscopic structure of [Cu II (OH)] + species in Cu-CHA, we performed ab initio calculations at different levels of theory on periodic and cluster models (Supporting Information Section S5). The CHA lattice is made up of cages connected through adjoining 8MR windows, which have been proposed as privileged sites for stabilizing [Cu II (OH)] + . 11,23,27 The optimized structure of the mono-copper hydroxo species is shown in Figure 3a (see also Figure S7) and displays a 4-fold coordination, with three zeolite lattice oxygens from the 8MR (O-8MR) and the OH − ligand pointing toward the center of the cage. We point out that this coordination geometry ([Cu II OH(O-8MRs) 3 ]) is consistent with the Cu d x 2 −y 2 character of the SOMO (see Figure 3b and Figure S5) and differs from previous assignments, based on trigonal Cu coordination. 13,21,22 The computed spin Hamiltonian parameters consistently reproduce the 1 H coupling tensor detected experimentally together with the Cu II g-and A-tensors (see Figure S6 and Tables 1 and 2), reflecting the decrease of the g || and A || components with respect to the [Cu II (O-6MR) 4 ] species (Section S2.1 Supporting Information). The calculation of the 1 H hyperfine tensor is particularly delicate, requiring the careful scrutiny of the different levels of theory (see Table S4). As an independent validation, the OH stretching and bending frequencies for the structure presented in Figure 3 were calculated, providing values (3658 and 928 cm −1 ) in agreement with experimental results. 9,13 Computed values for the trigonal structure (Section S7 Supporting Information) are inconsistent with the experimental findings, Uncertainties of 1 MHz and 10°are estimated for the hyperfine couplings and Euler angles, respectively. *α angle was found immaterial. c The computed values were obtained at the DLPNO-CCSD/cc-pwCVQZ level of theory. Euler angles relating H A-and gtensors were calculated at the B2PLYP/EPR-III level of theory.   Figure 3. This structure corresponds to an energy minimum, coherent with spectroscopic data collected in the temperature interval 10 K−RT. We remark that spectroscopic data collected at high temperature (673 K) 13,23 may not be capable of distinguishing between the four and three coordination geometry due to fluctuations in Cu coordination at this temperature. In conclusion we provide a quantitative assessment of the electronic and geometric structure of monomeric hydroxo-Cu II species in Cu-CHA, which can be described in terms of 4fold-coordinated [Cu II (OH)(O-8MR) 3 ] complexes at 8MR cages. By combining HYSCORE experiments with advanced modeling, the EPR signature of such species is univocally identified. These results highlight the potential of advanced EPR techniques in the characterization of Cu species in zeolites and provide new structural data to enable structure− function correlation in Cu-loaded zeolites. ■ ASSOCIATED CONTENT
Experimental procedures, computational details, simulation of EPR spectra, and details on the EPR quantification and on the computation of spin Hamiltonian parameters (PDF)