Improvement and regeneration of Co–B amorphous alloy nanowires for the selective hydrogenation of cinnamaldehyde

One-dimensional Co–B amorphous alloy nanowires (NWs) were prepared using surfactant as a template and were treated with plasma to study the effect of different treatment times on the essential physical and chemical properties of the catalyst. The study showed that plasma with a certain amount of strength will not change the morphology and amorphous structure of the NWs within the chosen treatment time. It could, however, modify the electronic structure and active sites of the catalyst surface, increase its specific surface area and H2 adsorption capacity, and also improve the selective hydrogenation performance of cinnamaldehyde. Most of all, plasma treatment could also play an important role in the reuse of catalysts. After several recycling reactions, plasma treatment on Co–B amorphous alloy NWs could regenerate their high catalytic activity. This work provides a novel method for preserving the high catalytic activity and stability of amorphous alloy nanomaterials, as well as for increasing their reusability.


Introduction
The selective catalytic hydrogenation of cinnamaldehyde (CMA) that is representative of the bond coupling in C]C and C]O bonds of a,b-unsaturated aldehydes is appealing to both academic and industrial elds. [1][2][3][4] In CMA, hydrogenation that occurs at C]O could produce unsaturated cinnamyl alcohols (CMO), while at C]C it could yield saturated dihydrocinnamaldehydes (HCMA). These products are followed by total hydrogenation to 3-phenylpropanol (HCMO) (Fig. 1). 5,6 CMO could be an important hydrogenation product owing to its important applications in avors, pharmaceutical intermediates, and fragrances. However, the reduction of the C]C group is thermodynamically more favorable than that of the C]O group, and thus, it has attracted considerable attention that has led to the designing of catalysts with an ideal selectivity for CMO. 7,8 To obtain CMO, various catalysts have been developed. Catalysts based on noble metals (Ru, Pt, Rh, and Pd) or a combination of noble and transition metals (Pt-Co, Pt-Fe, etc.) are highly reactive; however, they have poor selectivity for CMO. 2,9 To improve their selectivity, the physicochemical properties of these catalysts (such as the metal atoms, the electronic effect of the second metal, surface ligands, local structure, as well as texture of the support) have been addressed. [10][11][12][13][14][15] The cost of a catalyst is a core concern in industrial catalysis; thus, it is necessary to develop low-cost and highly active hydrogenation catalysts to alleviate the demand for noble metals. [16][17][18][19][20] Nonprecious metal catalysts, such as Co-B amorphous alloys, are excellent hydrogenation catalysts for CMA owing to their low cost, easy access, and excellent selectivity for CMO. 21,22 Although there are also some disadvantages to them, such as the reduction of catalytic activity due to agglomeration, oxidation by oxygen in the air, etc. Nanoscale granular Co-B amorphous alloy catalysts can be easily obtained by wet chemical methods without using a surfactant as a template as the reaction between Co 2+ and reducing agents (such as BH 4 − ) is violent and can cause particle agglomeration. In addition, granular amorphous alloys easily agglomerate during the catalytic hydrogenation reaction, thereby reducing their catalytic activity. 23,24 Moreover, Co-B amorphous alloy catalysts are easily oxidized by oxygen in the air, leading to deactivation in their CMA hydrogenation performance. Determining a method to overcome this degradation of catalytic performance due to agglomeration and oxidation, and improve the reusability is a challenge. Preference has been given to research geared toward the synthesis of amorphous alloy catalysts with nanotube, [25][26][27] nanosphere, [28][29][30] and nanochain 22 morphologies, which can effectively prevent agglomeration and enhance the structural stability of nanocatalysts. We previously reported a series of one-dimensional (1D) amorphous alloy nanotubes with high catalytic hydrogenation activity and selectivity by using the layered liquid crystal template method. However, there was no signicant progress in the oxidation resistance of the amorphous alloy catalysts.
As an effective molecular activation technology, lowtemperature plasma is increasingly used in catalyst preparation and reaction. 31,32 Plasma technology is a low-energy process, which is regarded as an efficient tool for preparing or modifying materials. It is environmentally friendly as it does not produce solvent and chemical waste. Plasma surface treatment can change the valence state of metal active components to achieve catalyst reduction, and greatly optimize the physicochemical properties of catalysts. Plasma technology is widely used to treat electrocatalysts at room temperature. [33][34][35] However, only a few studies have reported the effect of plasma treatment on amorphous alloy catalysts for the enhancement of catalytic hydrogenation performance. In this study, we synthesized a 1D Co-B amorphous alloy catalyst with nanowire morphology which has higher structural stability and longer catalytic lifetime compared to granular and tubular counterparts. The effect of plasma treatment on the morphology, physicochemical properties of amorphous alloy catalysts, and the improvement of the selective hydrogenation performance of CMA were studied. Moreover, in the recycling catalytic process of the Co-B amorphous alloy catalyst, the degradation of catalytic hydrogenation performance caused by the oxidation of the catalyst surface due to unavoidable contact with air could also be regenerated by plasma treatment aer a certain number of cycles, which provides convenience for the application of amorphous alloy catalysts for catalytic hydrogenation.

Sample preparation
The Co-B amorphous nanowires (NWs) were prepared as follows: Tween 80 (0.005 mol), camphor sulfonic acid (CSA, 0.0025 mol) was dissolved in 12 mL of deionized water in a water bath at 343 K while stirring evenly. 0.005 mol of CoCl 2 $6H 2 O was then added to the above solution and constantly stirred until a transparent and homogeneous solution was formed. The resultant solution was placed in a water bath and slowly cooled from 343 to 298 K, aer which a mixture of NaBH 4 (4 mol L −1 ) and NaOH (0.1 mol L −1 ) was pumped into the system while stirring in a nitrogen atmosphere. Aer completion of the reaction, the resultant solution was aged for 36 h. A black precipitate was obtained, which was cleaned thrice with deionized water and anhydrous alcohol. It was then dried in an N 2 atmosphere. This sample of amorphous alloy NWs was labeled Co-B-0 NWs.
Low-temperature plasma treatment was performed on amorphous alloy catalysts as follows: Co-B NWs prepared were placed on a quartz boat in a plasma reactor aer which they were treated using argon plasma of 200 W power for 100, 200, and 300 seconds. The samples obtained were labeled Co-B-100 NWs, Co-B-200 NWs, and Co-B-300 NWs, respectively.

Characterization
The morphology of the Co-B NWs was inspected using transmission electron microscopy (TEM; JEM-1011) with an accelerating voltage of 120 kV. Their crystal structure was measured using powder X-ray diffraction (XRD; Philips). Their chemical compositions and electronic states were studied using X-ray photoelectron spectroscopy (XPS; Thermo ESCALAB 250). The nitrogen-sorption isotherms of the Co-B NWs were characterized using the ASAP 2020 apparatus. H 2 temperature programmed desorption was tested by using an apparatus (H 2 -TPD; AutoChem TP-5080) with a thermal conductivity detector.

Catalytic test
The catalytic performance of the Co-B amorphous alloy NWs was evaluated as follows: 0.3 g of catalyst, 2 mL of CMA, and 170 mL of absolute ethanol were added into a 200 mL reactor. Aer purging thrice with N 2 and H 2 while stirring, hydrogen at a predetermined pressure of 1.0 MPa was introduced into the system. These conditions were maintained throughout the reaction process. The reactor was heated to 373 K, which marked the beginning of the reaction time. As the reaction proceeded, samples were removed from the reactor regularly and analyzed using gas chromatography (GC-2014 Shimadzu). The conversion of CMA and selectivity of the products were calculated using the following formula: Selectivity ð%Þ ¼ moles of product moles of reacted CMA compound Â 100%

Characteristics of nanowires
As shown in Fig. 2 Co-B-0 NWs were prepared by reducing Co 2+ in the water layer of layered liquid crystal with sodium borohydride. The lamellar liquid crystal was formed of Tween 80, camphor sulfonic acid (CSA), and cobalt salt dissolved in water aer cooling from 348 to 298 K. Fig. 3(a) shows the small-angle XRD pattern of the layered liquid crystal. The layer spacing is 9.85 nm. When the layer spacing was relatively smaller, such as d = 7.37 nm as previously reported, 25 the amorphous alloy nanotubes were easily formed through the curling mechanism. [25][26][27] However, in this work, it was easy to form NWs because the layer spacing was large (d = 9.85 nm), and the lamellar liquid crystal could not be curled. The Co-B amorphous alloy NWs were conned to formation in the water layer of the liquid crystal. The wide-angle XRD spectra of Co-B-  0 NWs, Co-B-100 NWs, Co-B-200 NWs, and Co-B-300 NWs in Fig. 3(b) show amorphous structure, indicating that plasma treatment on Co-B NWs did not change the crystal structure of the amorphous alloy NWs. Fig. 4 shows the XPS spectra of Co-B-0 NWs and Co-B-200 NWs. The Co 2p 3/2 deconvolution for Co-B-0 NWs is demonstrated in Fig. 4(a). The elemental state was at 777.5 eV, while that of CoO and Co(OH) 2 was at 779.6 and 781.1 eV, respectively. The peak at 782.9 eV was attributed to the electron shakeup peak for Co(OH) 2 multiple splitting. 36,37 The deconvolution of the B 1s spectrum for Co-B-0 NWs is shown in Fig. 4(b). The peaks for B 1s at 187.9 and 192.1 eV corresponded to elemental and oxidized B, respectively. [38][39][40] Notably, the binding energy of elemental B in Co-B-0 NWs shied positively by approximately 0.8 eV compared to the binding energy of pure B at 187.1 eV, which indicated that B partially donated electrons to the alloyed Co. The electron transfer between Co and B in Co-B NWs made Co electronrich and B electron-decient. 22,36 The electron-rich Co in Co-B was then able to facilitate the catalytic reaction of CMA to CMO. 22 The composition of Co-B-0 NWs from XPS data was Co 72.1 B 27.9 . The deconvolution of Co 2p 3/2 and B 1s spectra of Co-B-200 NWs was similar to that of the Co-B-0 NWs except that the binding energy of Co had a small negative shi of approximately 0.1 eV, whereas the binding energy of B had a positive shi of approximately 0.6 eV. The relative peak areas for the elemental and the oxidation states in the XPS spectra changed. The relative proportions of each species of all samples are listed in Table 1. As the electron shakeup peak of Co(OH) 2 at 782.9 eV was not incorporated in calculations, the sum of the peak areas of Co 0 and Co 2+ was not 100%. 36 When the plasma treatment time was 100 and 200 seconds, the relative content of Co 0 and B 0 increased signicantly; however, the increase in the zero-valence species content of Co-B-300 NWs was not obvious as compared with that of Co-B-200 NWs. Research has shown that the higher the content of elemental Co and B, the greater the electron transfer and the faster the reaction. [36][37][38] In summary, the result indicated that the synergistic effect between Co and B was enhanced aer plasma treatment. Fig. 5(a) shows the nitrogen adsorption isotherm and pore size distribution curves for Co-B-200 NWs, while the specic surface and pore volume data for all samples are listed in Table  1. The results show that the Co-B-200 NWs maintained their mesoporous structure aer plasma treatment. 27 However, the treatment increased the specic surface and pore volume of the Co-B NWs. The H 2 -TPD curves for Co-B-0 and Co-B-200 NWs are shown in Fig. 5(b), and the H 2 uptake for all the samples are listed in Table 1. The TPD peak for Co-B-200 NWs moved toward a higher temperature as compared with that for Co-B-0 NWs, indicating that plasma treatment on Co-B NWs was conducive to the stronger adsorption of H 2 on the catalyst. Notably, the surface active site of Co-B-200 NWs was more uniform, which may promote the selectivity of catalytic hydrogenation reaction. 23 Moreover, the samples with plasma treatment had a higher H 2 uptake than the Co-B-0 NWs.    Paper RSC Advances hours, and the nal selectivity for CMO was only 89.1%. We also studied the impact of plasma treatment time on the catalytic reaction. It was found that the catalytic performance of Co-B NWs improved greatly aer plasma treatment. For Co-B-100, Co-B-200, and Co-B-300 NWs, the time for the complete conversion of CMA reached 4.5, 3.5, and 3.5 h, respectively, and the selectivity for the main product (CMO) was 94.4, 96.9, and 96.6%, respectively. As compared with Co-B-200 NWs, the catalytic performance of Co-B-300 NWs did not improve signicantly, indicating that aer a certain time (200 s in this case), the effect of plasma treatment on Co-B NWs could not be improved by simply prolonging the plasma treatment time.

Catalytic property for hydrogenation of CMA
The selective hydrogenation mechanism of cinnamaldehyde under Co-B NWs could be depicted as follows. The high CMA catalytic activity of Co-B NWs was due to the structural and electronic effect. [9][10][11] Structurally, Co-B amorphous alloy NWs that were long-range ordered and short-range disordered were very benecial to the hydrogenation reaction. The highly unsaturated and dispersed Co active sites that were fully exposed and the strong interaction between different Co active sites could improve the hydrogenation activity. From the perspective of electronic effect, the alloyed B in the Co-B NWs transferred some electrons to Co, making Co electron-rich, which was conducive to the hydrogenation reaction. The electron-decient B was also instrumental in the adsorption of the C]O group on the catalyst. 41 The high CMO selectivity of the Co-B NWs catalyst may be due to the unwelcome contact and adsorption between the Co active site and the C]C group because the steric hindrance caused by the direct connection with benzene ring made the C]C group on CMA adsorb readily on the Co active site. At the same time, it promoted the adsorption of C]O on the catalyst surface, thus improving the hydrogenation selectivity of C]O. 21,22,25,41 The improvement in the catalytic performance of Co-B NWs with plasma treatment as compared with those of their untreated counterparts was achieved through the higher specic surface area and pore volume of the catalyst, homogeneous active sites, and higher hydrogen adsorption capacity, as well as the stronger synergistic effect of Co and B on the catalyst surface.
To study the sustainable utilization of catalysts, a recycling experiment was performed. The results are shown in Fig. 7. Fig. 7(a) shows the experimental results of six cycles on Co-B-200 NWs. Each catalytic reaction lasted for 3 h. Aer the reaction was completed, the conversion of CMA and the selectivity for CMO in the product were tested. During the rst through to the h run of the recycling experiment, the catalyst maintained high catalytic activity, but when it was recycled for the sixth time, its catalytic performance decreased signicantly. The decline in catalytic performance may have resulted from the oxidation of the catalyst during experimental manipulation. To explore the effect of plasma treatment on the reusability of the catalysts, the Co-B-200 NWs were treated with plasma for 200 additional seconds aer four cycles of catalytic reactions, where each lasted for 3 h. Fig. 7(b) shows the experimental results of four cycles of Co-B-200 NWs activity aer the second plasma treatment. It can be observed that the catalyst retained high conversion and selectivity. However, aer the ninth plasma treatment, the activity of the catalyst declined signicantly as shown in Fig. 7(c). The TEM test results of the samples shown in Fig. 7(d) indicate that there were many nanoparticles aer the ninth plasma treatment, and the decline in catalytic performance may have been caused by the collapse of the NWs into nanoparticles. The SAED inset in Fig. 7(d) shows that the Co-B NWs were still amorphous aer many recycling test experiments. It was thus clear that plasma treatment played a positive role in the regeneration of Co-B NW catalysts.

Conclusions
In summary, 1D amorphous alloy Co-B NWs were prepared by using layered liquid crystals as templates. Co-B NWs had a diameter of 35-45 nm and a length of 2-5 mm. To improve CMA catalytic hydrogenation activity, the prepared amorphous alloy Co-B NWs were treated with low-temperature plasma. The results showed that the plasma treatment with appropriate power and time had little inuence on the morphology and amorphous structure of Co-B NWs, but it could increase the relative content of Co 0 on the surface, promote the specic surface area, and optimize the types of surface active sites present. These changes were benecial to the improvement of catalytic hydrogenation performance. In addition, during the catalytic hydrogenation cycling test, the amorphous alloy catalyst inevitably comes in contact with oxygen, leading to partial oxidation of the catalyst surface, which reduces the catalytic hydrogenation performance. Repeated plasma treatment could induce the activity and extend the lifetime of Co-B NWs. This work provides a convenient method for the improvement and regeneration of amorphous alloy catalysts.

Conflicts of interest