Improved ORR/OER bifunctional catalytic performance of amorphous manganese oxides prepared by photochemical metal–organic deposition

Transition metal oxide nanomaterials or nanocomposites containing transition metal oxides have the potential to replace traditional catalysts for electrochemical applications, photocatalysis, and energy storage. Amorphous manganese oxide catalysts were prepared via photochemical metal–organic deposition (PMOD). Through XRD, SEM-EDS, Raman spectroscopy, FTIR spectroscopy, HRTEM-EDS, and XPS, we confirmed that amorphous manganese oxide catalysts were successfully prepared. Amorphous catalysts prepared with different photolysis times were compared in terms of their performance for the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER), and catalyst MnOx-PMOD48 showed the best performance because of its high Mn3+ proportion and electrochemically active surface area. MnOx-PMOD48 showed better ORR/OER performance than the crystalline MnOx and MnOx/Ti4O7 catalysts from our previous work. Following our previous work on crystalline manganese oxide catalysts, we added Ti4O7 during the PMOD process with 48 h of treatment and obtained the amorphous catalyst MnOx/Ti4O7-PMOD. MnOx/Ti4O7-PMOD was supported by Ti4O7 particles, which led to improved stability. The ORR/OER catalytic activity of MnOx/Ti4O7-PMOD was better than that of crystalline catalyst MnOx/Ti4O7-300, which was the best crystalline catalyst in our previous work. We also compared lithium-oxygen batteries assembled with MnOx/Ti4O7-PMOD and MnOx/Ti4O7-300. The battery performance tests confirmed that the amorphous manganese catalyst had better ORR/OER bifunctional catalytic performance than the crystalline manganese catalyst because of its high defect state with more abundant edge active sites and more surface-exposed catalytic active sites.


Introduction
New material technologies play a key role in clean energy and low-carbon technologies. Thermoelectric materials, including organic, inorganic, and hybrid organic-inorganic materials, are widely considered suitable materials for thermoelectric devices. 1 Nanostructured metal oxides and their hybrids have attracted signicant attention from researchers for photocatalytic, anticancer, and antibacterial applications. 2,3 Nanocomposite membranes are at the heart of the process for pervaporation separation techniques. 4,5 Carbon neutrality is the new mission for future generations and the planet as a whole. It is increasingly clear that reducing the use of fossil energy, turning to green energy, and emphasising low-carbon lifestyles and production techniques must be the new direction for mankind. Metal-air batteries are clean, low-carbon, safe, and efficient new energy systems with the advantages of high energy density and large output power. 6 However, owing to factors like poor cyclic stability, large differences in charge-discharge voltage, and slow reaction kinetics, further application of metal-air batteries is greatly restricted. Many studies have shown that the slow reaction kinetics of the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) at the air electrode limit the performance improvement of metal-air batteries. [7][8][9] Therefore, it is urgent to develop efficient and stable ORR/OER bifunctional catalysts to promote the development of metal-air batteries.
Noble metals, such as platinum and iridium, are highly efficient and widely used ORR/OER catalysts. [10][11][12][13] But the scarcity and high cost of noble metals are the main reasons that restrict their further widespread use, especially for replacing traditional energy sources with clean energy sources in every aspect of our lives. 14 Mixed metal oxide nanocomposites (rareearth-based) are a target for antibacterial, electrochemical, and photocatalytic research. 15 Transition metals with large storage, low cost, and relatively high catalytic performance are very suitable substitutes for noble metals. 16 Co/Ni metal nanostructures have been reported as efficient photocatalysts. 17 Transition metal suldes used in supercapacitors have also attracted broad attention. 18 Among these transition metals, manganese is of particular interest because of its varied valencies and its ability to form a variety of oxides. [19][20][21] Most of them, such as MnO 2 , Mn 2 O 3 , and Mn 3 O 4 , have been conrmed to be efficient ORR/OER catalysts. 22 In particular, Mn 3+ has been found to be the key to ORR/OER bifunctional catalysis. [23][24][25] Manganese oxides have also been used in the Fischer-Tropsch (FT) process to improve the selectivity of long-chain carbon products. 26 Manganese oxide remains stable over a wide pH range at a certain potential. Therefore, manganese oxide is a potentially efficient and stable catalyst.
In our previous work, we prepared crystalline manganese oxide to test its catalytic performance. 27 Catalysts used in practical applications all contain defects. Srinivas showed that a smaller crystal size leads to the occurrence of oxygen vacancies at the surface and grain boundaries, which enhances catalytic performance. 17 For transition metal oxides, the increase in surface defects can provide more active sites to improve catalytic activity and ameliorate the problem of poor conductivity. 28,29 It is worth studying how to control the increase in defects during the preparation process to improve the catalytic activity. The synthesis of amorphous catalytic materials, or materials with high defects, can help to provide more active sites in another way. Several physical and chemical methods have been reported for preparing 2-dimensional (2D) lm nanomaterials. 30 Photochemical metal-organic deposition (PMOD) has been used to successfully prepare manganese oxide amorphous materials. 31,32 The PMOD strategy has also been used in the synthesis of amorphous oxides of lead, iron, cobalt, and nickel, and related studies have conrmed that the catalytic performance of amorphous catalysts is superior to that of the corresponding crystalline materials. [33][34][35][36][37] Although the conductivity of metal oxide nanomaterials or amorphous materials can be improved by changing their bandgap energy, it is still not as good as that of metallic or carbon materials. To improve the electrical conductivity, metal oxide nanomaterials or amorphous materials can be combined with other conductive carriers. In energy storage supercapacitors and solar cells, polyaniline combines with graphene and improves the conductivity by working as an organic conductive polymer. 38 Apart from improving the conductivity, SiO 2 carriers have been used to improve the surface area of the nanomaterial. 39 In this study, we synthesised amorphous manganese oxide catalysts using the PMOD method and introduced carbon particles to improve the electrical conductivity. Different catalysts were synthesized by controlling the irradiation time, and their phases and catalytic activities were compared to explore the essential relationship between the synthesis strategy and catalytic activity. The optimum amorphous catalyst was compared with the crystalline catalysts prepared in our previous work. The disappearance of defects from amorphous catalytic materials is an important cause of catalyst deactivation. To address this issue, we referred to our experience in the preparation of crystalline catalysts and introduced Ti 4 O 7 as a support material. We then compare the resulting catalyst with the optimal crystalline catalyst supported by Ti 4 O 7 from our previous work. Finally, we concluded that amorphous MnO x / Ti 4 O 7 -PMOD is the best catalyst for our system.

Sample synthesis
Amorphous manganese oxides were synthesised via PMOD. Manganese(II) 2-ethylhexanoate (7.1114 g, 6% manganese, Alfa Aesar), carbon powder XC-72 (0.3000 g, >99%, Alfa Aesar), and (A) none or (B) 0.3790 g Ti 4 O 7 (>95%, Titanium Energy Technology) were dispersed in 5 mL n-hexane (>97%, TongGuang Fine Chemicals) in a watch glass and treated with an ultrasonic cleaner for 10 min. Three watch glasses of A were placed in a dark chamber with 254 and 185 nm ultraviolet (UV) light sources and one glass each was irradiated for 24, 48, and 72 h. One watch glass of B was placed in the same chamber and irradiated for 48 h. Aer UV irradiation, all the watch glasses were dried in a drying oven at 60 C for 2 h. Amorphous manganese oxide MnO x -PMOD samples prepared with different UV treatment durations were named MnO x -PMOD24, MnO x -PMOD48, and MnO x -PMOD72. The amorphous MnO x composited with Ti 4 O 7 was named MnO x /Ti 4 O 7 -PMOD. More details are provided in the ESI. †

Characterization methods
Phase analysis of the MnO x -PMOD samples was performed using X-ray diffraction (XRD, Bruker D8 advance) at a scan rate of 10 min À1 from 10 to 80 . The morphology and microstructure were characterised using scanning electron microscopy (SEM, JEOL JSM-7900) and high-resolution transmission electron microscopy (HRTEM, FEI Tecnica G2 F20). Valence state analysis of the surface was carried out by X-ray photoelectron spectroscopy (XPS, ESCALAB 250Xi) with an Al Ka radiation source. To conrm the consumption of the manganese source, Fourier transform infrared (FTIR) spectroscopy was performed using a Bruker Vertex 70 spectrometer. Raman spectroscopy was performed using a Renishaw inVia™ Qontor instrument to conrm the formation of manganese oxides.

Electrochemical measurements
A three-electrode system was used in this study. A 5 mmdiameter glassy carbon (GC) controlled by a rotating ring and disk electrode (RRDE, IPS) was used as the working electrode, with a Hg/HgO reference electrode and carbon rod counter electrode. Cyclic voltammetry (CV), linear sweep voltammetry (LSV), and electrochemical impedance spectroscopy (EIS) were performed to evaluate the electrocatalytic performance. The electrode material was prepared by dispersing 2.0 mg MnO x -PMOD sample in 1 mL anhydrous ethanol and 0.5 mL 0.2% Naon ethanol solution and then forming a slurry using an ultrasonic dispersing instrument. The electrode material slurry (20 mL) was added dropwise onto the GC working electrode using a microsyringe. The three-electrode system was installed in a customised electrolytic cell and submerged in 0.1 mol L À1 KOH solution saturated with argon for activation and then saturated with oxygen for electrochemical measurement. For chronoamperometry (CA) and polarisation curve tests, a GC piece (10 Â 10 mm) was used as the working electrode. The above-mentioned formulation was used for the electrode material slurry; however, the slurry amount was changed to 200 mL, and all electrochemical tests were performed using a Metrohm Autolab PGSTAT302N electrochemical workstation without iR compensation.

Li-O 2 battery tests
The MnO x -PMOD sample, conductive carbon black (Super P, >99%, Alfa Aesar), and an agglomerant (polyvinylidene uoride, PVDF) were mixed in a mortar at a mass ratio of 3 : 6 : 1. Subsequently, N-methyl-2-pyrrolidinone (>99%, Aladdin) was added to congure the slurry. Carbon paper was used as the current collector substrate to spray the slurry. The whole electrode material was dried at 120 C for 12 h in an oven and then cut into pieces 14 mm in diameter for assembling the battery. Finally, a CR2032 coin lithium-oxygen battery was assembled in an argon-lled glove box (Braun, Lab Star) and tested in a customised pure oxygen-lled battery box for charge and discharge tests (Neware, CT-4008). More details regarding the carbon paper electrode are provided in the ESI. †

Phase identication and morphology analysis
The blue, red, and black curves in Fig. 1A show the XRD patterns of the amorphous manganese oxide MnO x -PMOD samples obtained with different UV light decomposition times. Protrusions were observed around 2q ¼ 28.9 , and no peaks were found in any of the three patterns. The samples prepared by PMOD did not show crystallisation and were still high-defect-state amorphous or primary crystallisation materials. From Fig. S1, † the absorption peaks at 2961 cm À1 , 2876 cm À1 , 2937 cm À1 , and 2853 cm À1 can be assigned to manganese(II) 2-ethylhexanoate from the organic manganese source used herein. 35,36 With increasing UV photolysis time, the intensities of the organic manganese absorption peaks decreased, indicating that the organic manganese source was consumed. We found a peak at approximately 650 cm À1 in all three Raman spectra, as shown in Fig. S2. † Compared with the standard Raman spectrogram, this peak corresponds to the Mn-O bond, and the peak intensity increases with increasing UV photolysis time. The FTIR and Raman results together show that the organic manganese source was converted to amorphous manganese oxides.
The SEM images in Fig. S3 † show the microstructures of MnO x -PMOD24, MnO x -PMOD48, and MnO x -PMOD72. The amorphous catalysts prepared by PMOD showed an irregular 2D morphology different from the 1D structure of crystalline manganese oxide. These surfaces had different degrees of folds and cracks. With different photolysis times, the morphologies of the catalysts showed similar lm structures. For example, the energy dispersive spectrum (EDS) of MnO x -PMOD72 (Fig. S4 †) shows that manganese and oxygen mainly existed in the irregular 2D lamellar morphology, while carbon mainly existed in the form of XC-72 carbon particles in the substrate. The irregular 2D structure has the advantages of mechanical peeling control, large surface area, and abundant edge active sites, which will improve the catalyst performance. [40][41][42][43] In the electrochemical tests, the catalysts were modied on the surface of the GC electrode to affect the real morphology. We dispersed MnO x -PMOD48 in a Naon-ethanol solution and performed SEM and EDS tests aer natural drying. A SEM test was performed on an XC-72 sample subjected to the same treatment for comparison. The SEM images of MnO x -PMOD48 and XC-72 show that the carbon nanoparticles were stacked in the same way, as shown in Fig. S5. † The MnO x -PMOD48 nanoparticles appeared closer than those of XC-72. In other words, amorphous manganese oxide had no obvious shape characteristics aer being dispersed in ethanol, and the original 2D structure disappeared. The EDS image of MnO x -PMOD48 in Fig. S6 † shows that manganese and oxygen were enriched in the carbon particles. In actual electrode materials, manganese oxides can be combined with XC-72 carbon particles. XC-72 can provide support for manganese oxides, which is helpful for improving the stability of catalysts during the catalytic process and reducing the crystallisation of manganese oxides. Amorphous manganese oxides were evenly dispersed in XC-72, which contributed to its better catalytic activity.
TEM characterisation was used to further explore the microstructure and the relationship between the amorphous manganese oxides and XC-72 carbon particles, as shown in Fig. 1B. In the TEM images, the morphology of crystalline manganese oxides was not observed, and only the accumulation of particles was observed. As shown in the HRTEM images in Fig. 1B, fuzzy lattice fringes appear within a narrow range of less than 10 nm, but it is difficult to match the crystal planes of crystalline manganese oxides. We believe that this nanoregion was formed by the initial crystallisation of manganese oxides. Amorphous manganese oxides began to show an ordered arrangement, but because of their high defect density, a stable and visible lattice structure could not be formed. In addition, the corresponding selective area electron diffraction image shows an obvious diffuse halo, and no regular spot group or diffraction ring is observed, which proves that the region existed in an amorphous form. The above characterisations conrm that catalysts composed of amorphous manganese oxide were successfully prepared.

Electrochemical properties and analysis
The ORR and OER performances of the amorphous catalysts MnO x -PMOD24, MnO x -PMOD48, and MnO x -PMOD72 were compared using CV and LSV measurements, as shown in Fig. S7 and S8. † MnO x -PMOD24 showed the worst catalytic activity for the ORR, as conrmed by the CV and ORR results. The ORR onset potentials of MnO x -PMOD48 and MnO x -PMOD72 were similar, and the ORR-limiting diffusion current of MnO x -PMOD72 was the highest among the three catalysts. For the OER performance, MnO x -PMOD48 showed the lowest overpotential at 10 mA cm À2 and the highest current density in the measurement potential range. MnO x -PMOD48 showed better catalytic activity for the OER than MnO x -PMOD24 and MnO x -PMOD72. MnO x -PMOD48 was found to be the best ORR/OER catalyst among the three tested catalysts. The electrochemical active surface area of each catalyst was estimated from the electrochemical double-layer capacitance (C DL ) of the catalytic surface and the specic capacitance, as shown in Fig. S9. † The C DL was calculated from the CV measurements at different scan rates, and the scan range was AE60 mV around the open circuit potential of each catalyst. The C DL calculation result for MnO x -48 was 6.135 mF, compared with 2.785 and 4.355 mF for MnO x -PMOD24 and MnO x -PMOD72, respectively. MnO x -PMOD48 had a larger electrochemically active surface area than the other catalysts, leading to better catalytic performance. Therefore, we chose MnO x -PMOD48 as the amorphous catalyst for subsequent tests.
According to Zhu et al., using manganese(II) 2-ethylhexanoate as the raw material for UV photolysis should produce a mixture of MnO and Mn 2 O 3 . 32 The Mn 2+ in MnO is unstable at room temperature and can continue to oxidise to MnO 2 . Therefore, Mn 2+ , Mn 3+ , and Mn 4+ may coexist on the surfaces of the as-prepared amorphous MnO x samples. Because all the generated products exist in amorphous form, the molecular formula shown in this work is convenient for characterising the valence state of manganese and the number of Mn-O bonds. The obtained valence state is not consistent with the actual form of manganese oxides.  Table S1 † for comparing the areas of Mn 2+ , Mn 3+ , and Mn 4+ .
The Mn 2+ ratio in the three catalysts was the highest at 24 h and decreased continuously on increasing the photolysis time to 72 h. In contrast, the Mn 4+ ratio increased gradually. This result is consistent with the mechanism by which Mn 2+ is oxidised to Mn 4+ at room temperature. The Mn 3+ ratio is unique in that the highest ratio was observed for MnO x -PMOD24, i.e. aer 24 h of UV photolysis. These results, in combination with the FTIR results in Fig. S1, † conrm that the oxidation of amorphous metal continued because of incomplete photolysis of the manganese source, and the ratio of Mn 3+ increased slightly from MnO x -PMOD24 to MnO x -PMOD48. Because the manganese source had completely reacted from MnO x -PMOD48 to MnO x -PMOD72, the formation of Mn 3+ is ended. Because of the high stability of Mn 3+ , only a small amount of Mn 3+ was further oxidised to Mn 4+ ; thus, the Mn 3+ ratio was only slightly reduced. In our previous work, we found that the Mn 3+ ratio obviously impacted the catalytic performance. 27 The electrochemical tests have proved that MnO x -PMOD48 is the best catalyst among the three tested herein.
The ORR and OER performances of the amorphous catalyst MnO x -PMOD48 and crystalline catalysts MnO x and MnO x /Ti 4 O 7 were evaluated by LSV measurements, as shown in Fig. 2A. MnO x and MnO x /Ti 4 O 7 are crystalline manganese oxide catalysts obtained in a previous work. The MnO x /Ti 4 O 7 catalyst includes Ti 4 O 7 as a catalyst support. The ORR onset potential of MnO x -PMOD48 was higher than those of MnO x and MnO x / Ti 4 O 7 , and the ORR-limiting diffusion current density of MnO x -PMOD48 was the highest. In terms of OER performance, MnO x -PMOD48 showed the lowest overpotential at 10 mA cm À2 for the OER and the highest current in the measurement potential range, whereas the OER currents of MnO x and MnO x /Ti 4 O 7 did not reach 10 mA cm À2 . This result is consistent with the fact that amorphous manganese oxides exhibit better ORR/OER performance than crystalline manganese oxides. Chronoamperometry tests were performed to compare the stability of the catalysts, as shown in Fig. 2B. Aer a 10 000 s test at 0.68 V vs. RHE, the current of MnO x -PMOD48 decreased by 35.4% compared with the initial current. The current declined by 50.1% and 39.4% for MnO x and MnO x /Ti 4 O 7 , respectively. Therefore, amorphous manganese oxide showed improved stability, performing even better than the Ti 4 O 7 -supported crystalline catalyst MnO x /Ti 4 O 7 .

Inuence of Ti 4 O 7 on manganese oxides
In our previous work, adding Ti 4 O 7 particles into a crystalline catalyst led to better performance. 27 This is mainly because Ti 4 O 7 induces the growth of manganese oxides and increases the number of active sites. The Ti 4 O 7 particles also had a supporting effect on the MnO x catalyst. We tested the effect of Ti 4 O 7 on the amorphous manganese oxides. The XRD, SEM, TEM, and EDS mapping results in Fig. 3 show the microstructure and elemental distribution of the amorphous catalyst MnO x /Ti 4 O 7 -PMOD. In Fig. 3A, the peaks at 2q ¼ 26.38 and 31.76 can be assigned to Ti 4 O 7 (PDF#71-1428) and no peaks corresponding to the crystal planes of manganese oxide were observed. The introduction of Ti 4 O 7 did not affect the formation of amorphous manganese oxides. The distribution of titanium was different from those of manganese and oxygen in the SEM image, as shown in Fig. 3B. The manganese oxides showed 2D growth on the Ti 4 O 7 particles. Therefore, the surface of MnO x /Ti 4 O 7 -PMOD is more concave and convex than that of MnO x -PMOD48, which leads to more folds and introduces more marginal active sites. This result is consistent with that of our previous work. In Fig. 3C, the TEM image of MnO x /Ti 4 O 7 -PMOD shows that the Ti 4 O 7 particle size was approximately 100 nm, and no lattice characteristics of manganese oxide were observed. According to the EDS mapping results in Fig. 3C, the distribution of titanium, manganese, and oxygen was identical, which conrms the above speculation about the growth of amorphous manganese oxide on Ti 4 O 7 particles. Amorphous manganese oxides have low stability and are easy to crystallise. Because of the support and stabilisation of Ti 4 O 7 particles, amorphous manganese oxide can be maintained well, which may further improve the catalytic performance and stability of MnO x /Ti 4 O 7 -PMOD.
We chose MnO x /Ti 4 O 7 -PMOD as the best amorphous manganese oxide catalyst to compare with crystalline catalyst MnO x /Ti 4 O 7 -300, the crystalline manganese oxide catalyst from our previous work. As shown in Fig. 4A, the ORR halfwave potential and ORR-limiting diffusion current of MnO x /Ti 4 O 7 -PMOD were 0.75 V VS RHE and À5.21 mA cm À2 , respectively, better than those of MnO x /Ti 4 O 7 -300 at 0.72 V vs. RHE and À4.34 mA cm À2 , respectively. As shown in Fig. 4B, the OER performance of MnO x /Ti 4 O 7 -PMOD was also better than that of MnO x /Ti 4 O 7 -300, with a potential of 1.60 V vs. RHE at 1 mA cm À2 and an overpotential of 530 mV at 10 mA cm À2 ; for comparison, MnO x /Ti 4 O 7 -300 had a potential of 1.71 V vs. RHE and could not reach 10 mA cm À2 . Amorphous materials exhibit better ORR/ OER performance because they show a high defect state with more abundant edge active sites and more surface-exposed catalytic active sites. A comparison of the ORR/OER performance of the MnO x /Ti 4 O 7 -PMOD synthesised in this work and those from other studies is presented in Table S2. † MnO x /Ti 4 O 7 -PMOD showed ORR/OER bifunctional catalytic performance, which led us to assemble a lithium-oxygen battery with it for further comparison with the crystalline catalyst MnO x /Ti 4 O 7 -300.
The K-L equation and RRDE curves could also be used to further conrm the catalytic performance based on the electron transfer numbers, as shown in Fig. S11     According to the battery performance comparison shown in Fig. 4C and D, the lithium-oxygen battery assembled with the amorphous catalyst MnO x /Ti 4 O 7 -PMOD is better than that assembled with the crystalline catalyst MnO x /Ti 4 O 7 -300, which is consistent with the ORR/OER performance results. As shown by the EIS tests in Fig. 4C Table S3. † Overall, the ORR/OER bifunctional catalytic activity of the amorphous catalyst MnO x / Ti 4 O 7 -PMOD was better than that of the crystalline catalyst MnO x /Ti 4 O 7 -300, especially in terms of OER catalysis performance. The performance of the lithium-oxygen battery assembled with MnO x /Ti 4 O 7 -PMOD was superior to that of the battery assembled with MnO x /Ti 4 O 7 -300. The amorphous catalyst prepared in this study not only has excellent ORR/OER bifunctional catalytic performance but also has good prospects for further development and potential for application in metal-air batteries.

Conclusions
Amorphous materials exhibit a high defect state with more abundant edge active sites and more surface-exposed catalytic active sites, which improves the catalytic performance. Amorphous materials also tend to form crystals, thereby losing active sites and reducing the catalytic activity. By adding a carrier like Ti 4 O 7 , the durability and conductivity of amorphous materials can be effectively increased. In this work, we prepared amorphous manganese oxide catalysts that show comparable ORR/ OER catalytic performance to catalysts from other studies. Several conclusions can be drawn from this study.
(1) Amorphous manganese oxides were prepared by PMOD and their composition, phase and morphology were proved using SEM, XPS, TEM, Raman spectroscopy, and FTIR spectroscopy. The ratio of Mn 3+ was different with different UV light irradiation times, which is a key point in the performance of the amorphous manganese oxide catalyst. Among the catalysts prepared with different irradiation times, MnO x -PMOD48 with 48 h irradiation had the highest Mn 3+ ratio and showed the best ORR/OER performance.
(2) MnO x -PMOD48 also showed better ORR/OER performance than the crystalline manganese oxide catalyst obtained in a previous work because of the high defect state with more abundant edge active sites and more surface-exposed catalytic active sites.
(3) Following our previous experience with the use of Ti 4 O 7 as a catalyst support for crystalline manganese oxide, we added Ti 4 O 7 during the synthesis of MnO x -PMOD48 and obtained amorphous manganese oxides supported with Ti 4 O 7 , denoted as MnO x /Ti 4 O 7 -PMOD. Ti 4 O 7 particles induced the formation of manganese oxides on themselves and supported the catalyst, leading to better stability. Comparing the amorphous catalyst MnO x /Ti 4 O 7 -PMOD and crystalline catalyst MnO x /Ti 4 O 7 -300, both of which are supported by Ti 4 O 7 , we can conclude that the amorphous catalyst has better ORR/OER performance.
In the future, we may perform more work to further stabilise the amorphous catalyst for applications like batteries. The PMOD method can also be used for the synthesis of other amorphous materials. This will help us to understand nanoparticles and nd more choices for the wider application of metal-air batteries.