Aging of Carbon Nanotubes Increases Their Adsorption towards Tetracycline

: Due to wide range of their applications, a large amount of carbon nanotubes (CNTs) is discharged into natural water. As an inevitable environmental fate, aging changes the physicochemical properties of carbon nanotubes, which in turn affects their interactions with other pollutants. In this study, the aging of CNTs accelerated with non-thermal plasma, and the interaction between aged CNTs and tetracycline were explored. The physicochemical properties of CNTs after aging were evaluated with speciﬁc surface area, zeta potential, FTIR, Raman, and XPS analysis. Adsorption and site energy distribution analyses were applied to explore the interaction between aged carbon nanotubes and tetracycline antibiotics. After aging, the speciﬁc surface area of carbon nanotubes decreases, defects increase, and the crystal morphology is disordered. More oxygen-containing functional groups are generated on the CNTs surface, including carbonyl, carboxyl, and hydroxyl groups. In addition, aged CNTs exhibited higher adsorption capacity for tetracycline. The results indicate that carbon nanotubes can adsorb more tetracycline after aging, which means that more antibiotics such as tetracycline may be enriched and transported on carbon nanotubes.


Introduction
Carbon nanotubes (CNTs) have been mass-produced and used widely due to their excellent properties in many fields, including aerospace, construction, medical, and biotechnology [1][2][3][4]. The global CNTs production reached 1000 t/a in 2009 and keeps increasing each year [5]. However, their extensive application leads to the potential release into nature. Meanwhile, the residual CNTs in soil and sediments may also transfer to surface water and even groundwater. It has been reported that the CNTs amount was about 0.025 ng/L in some natural water and even up to 400-500 µg/L in industrial sewage [5]. It is worth noting that CNTs exhibit high affinity for many heavy metals and organic pollutants and may play an important role in the migration of these pollutants [6][7][8]. Moreover, the adsorption capacity of CNTs primarily depends on their surface functional groups, including physical interaction with non-polar compounds and chemical interaction with polar compounds [9]. For example, pristine CNTs surfaces show high adsorption for non-polar compounds, while surface acidic groups (phenolic, carboxylic acid, and lactic acid groups) favor the adsorption of polar compounds [10][11][12]. To date, the sorption, aggregation, migration, deposition, and toxicity of CNTs in the natural environment have been well explored in many studies, where CNTs were regarded as static components [13][14][15]. However, less attention has been paid to their chemical transformation in nature, and the subsequent effects on other pollutants.
Aging is regarded as one of the primary environmental fates of many carbon materials, such as CNTs, biochar, and graphene [16]. CNTs in nature inevitably undergo different degrees of aging from the external environment, such as chemical oxidation, ultraviolet

Aging of CNTs with Non-Thermal Plasma
The aging of CNTs was performed in a dielectric barrier discharge plasma reactor (CTP-2000, Nanjing, China), and the details are described in the Supporting Information. In brief, CNTs (0.2 g) were first suspended in 10 mL deionized water and dispersed with ultrasound for 30 min. Then, the suspension was transferred into a glass dish on a ground electrode. The input voltage was set to 70 V. The treatment was performed for 3 h, and appropriate deionized water was added every 30 min to maintain equal volume. The aged CNTs were collected through filtering with a 0.22 µm nylon membrane and lyophilized for further experiments.

Characterization of CNTs
The functional groups of CNTs were identified with FTIR (Nicole, Waltham, MA, USA). Briefly, dried carbon nanotubes (1 mg) were mixed with KBr powder (100 mg) and pressed into a transparent sheet. Then, FTIR spectra were measured in wavenumbers from 4000 to 800 cm −1 with a resolution at 2 cm −1 . In addition, Raman spectra were also carried out to characterize the crystal structure and electronic energy band structure of CNTs using a Raman spectrometer (Thermo, Waltham, MA, USA). The pore characteristics and surface area of CNTs were analyzed with an SSA-4300 surface area analyzer at 77 K via the adsorption-desorption curve of nitrogen. Zeta potential and particle size distribution were analyzed using dynamic light scattering with a Zeta potentiometer (Malvern Instruments, Shanghai, China).
The elemental composition of CNTs was analyzed using an XPS spectroscopy (Thermo 250XI) with a monochromatic Al K X-ray source (1486.6 eV). The reduced power of the X-ray source was 150 W with a beam spot of 500 nm. Wide scans were carried out with pass energy at 70 eV, while pass energy of 20 eV was set for narrow scans of C 1s and O 1s. The neutral C 1s signal at 284.6 eV was used to correct the surface charging effects as the reference.

Interaction of Aged CNTs with Model Pollutants
TC was selected as a model emerging contaminant to evaluate the interaction between aged CNTs and model contaminants. The details of the adsorption kinetic and isothermal experiments are provided in the Supporting Information. The concentration of TC was measured using an HPLC (LC-20AT, Shimadzu, Tokyo, Japan) with C18 column (5 µm × 4 mm × 250 mm) and UV detector. The mobile phase (v/v) was composed of 0.01 M oxalic acid (80%), acetonitrile (16%), and methanol (4%). The flow rate was at 1.0 mL/min with detection wavelength at 360 nm.

Data Analysis
The equilibrium adsorption capacity of CNTs to TC was calculated according to Equation (1): where C 0 and C e are TC concentrations in the solution at the initial and equilibrium moment; m is the mass of CNTs, and V is the solution volume; q e is TC concentration adsorbed by CNTs when equilibrium is reached.
The pseudo-first-order kinetic and pseudo-second-order kinetic model were applied to fit the adsorption data according to Equations (2) and (3), respectively [34].
where q e and q t are adsorption equilibrium and TC amount on the CNTs at t, respectively; t is the adsorption time; k 1 and k 2 are the adsorption rate constants, which are calculated with the pseudo-first-order and pseudo-second-order kinetic equations, respectively. The adsorption isotherm data was fitted with two models, the Langmuir model and Freundlich model according to Equations (4) and (5) [35]. where q e and C e are the TC concentration in CNTs and water when equilibrium is reached; q max and k l are the maximum adsorption capacity and adsorption equilibrium constant of the Langmuir model, respectively; n and k f are the Freundlich constants, related to adsorption strength and adsorption capacity, respectively. Adsorption distribution coefficient, k 0 , is calculated according to Equation (6): The standard free energy change (∆G 0 ) is obtained using Equation (7): The standard enthalpy change (∆H 0 ) and the standard entropy change (∆S 0 ) are obtained according to Equations (8) and (9), respectively: where R is universal gas constant at 8.314 J mol −1 K −1 , and T is absolute temperature (K). Site energy distribution function, F(E*), is determined with condensation approximation [36]. For the Freundlich isotherm, the approximate site energy distribution is obtained from Equations (10) and (11): where E* is the difference of adsorption energy at C e and C s . C s stands for the solubility of the adsorbate.

Changes in CNTs Due to Aging
The chemical structure of CNTs was first investigated with FTIR and Raman spectroscopy (Figure 1a,b). For FTIR analysis, only a few peaks with low intensity were observed in both pristine CNTs and aged CNTs, indicating that nonpolar bonds like C=C and C-C were the main functional groups. For pristine CNTs, the signal at 860 cm −1 was assigned to the symmetric stretching of C-H bonds [37]. The signals at 1567 and 1029 cm −1 were due to the stretching vibrations of C-O [17,38]. The existence of H and O might be due to the impurity in pristine CNTs. After plasma treatment, little change was observed, suggesting that CNTs were quite stable and nonpolar bonds were still the major structure. In addition, the peak of C-O stretching vibration shifted slightly from 1029 cm −1 to 1010 cm −1 , indicating the possible changes of C-O groups during plasma treatment. Infrared spectroscopy is vibrational spectroscopy. Usually, the energy required is very low. A signal shifts to a lower wavenumber, implying that the energy required for vibration becomes lower and the group is more unstable. This may be due to the generation of auxochrome groups such as hydroxyl and other oxygen-containing groups, resulting in changes in the structure of CNTs [39,40]. In Raman spectra, two prominent peaks at~1340 cm −1 and~1580 cm −1 were assigned to D band and G band, resulting from the stretching vibration of sp 3 and sp 2 carbon atoms, respectively [41]. The peaks of D-band and G-band in aged CNTs shifted from 1340 cm −1 to 1343 cm −1 , and from 1584 cm −1 to 1581 cm −1 , respectively. Meanwhile, the half-width of D-band and G-band peaks widened from 96 cm −1 to 103 cm −1 , and from 64 cm −1 to 73 cm −1 , respectively. Both changes indicated that more defects and crystal Water 2022, 14, 2731 5 of 13 morphology disorder occurred in aged CNTs [42]. Moreover, the ID/IG ratio increased from 1.057 to 1.124 after plasma treatment, which might result from the generation of oxygen-containing functional groups on CNTs [43].  Furthermore, XPS spectra were recorded to explore the chemical states of pristine and aged CNTs. Two main elements, C and O, were detected with the C/O ratio at 52.19 and 25.18 in pristine and aged CNTs, respectively ( Figure S3 and Table S1). These results suggested that carbon was the primary element in CNTs, and oxygen-containing groups generated during aging, which was in accordance with the FTIR and Raman results. The C 1s signal was resolved into four peaks (Figure 1), where the peaks at~284 eV,~285 eV, 286 eV, and~290 eV were associated with sp2-hybridized, sp3-hybridized, C-O, and C=O, respectively (Table 1) [44]. Meanwhile, the O1s peaks at~532 eV and~533.57 eV were assigned to O=C and O-C, respectively [45]. Compared to pristine CNTs, the relative amount of C-O and C=O increased from 28.5% to 30.9%, implying the generation of oxygen-containing groups like carboxylic and carbonyl groups. These results confirmed the oxidation of CNTs by generating oxygen-containing groups during the aging process. Generally, these generating groups exhibit strong hydrophilic properties and thus could enhance the hydrophilicity of CNTs, suggesting that aged CNTs might exhibit different affinity to other pollutants [46]. Table 1. Results of deconvolution analysis of C1s and O1s spectra of the pristine and aged CNTs.

C1s
O1s The pore volume, specific surface area, and surface charge were also considered as key factors that affect the adsorption of CNTs on many pollutants [4]. There was no apparent difference in total pore volume ( Table 2). Mean pore size increased slightly after aging, which might improve the diffusion of adsorbate and thus enhance the adsorption. These results were also in accordance with adsorption isotherms analysis [47]. Moreover, specific surface area decreased from 81.78 to 76.42 m 2 /g, implying that plasma might partly sinter the surface of CNTs, collapse the crystal structure, and increase the crystal shape disorder [13]. This could increase surface defects and active sites on aged CNTs, leading to more reaction between TC and CNTs [47]. These results were consistent with the Raman analysis. As shown in Figure 2, zeta potential values of both pristine and aged CNTs reduced with the increasing pH, and the points of zero charge values (pH pzc ) were estimated at~6.1 and~4.4, respectively. Moreover, aged CNTs exhibited more negative surface charge and less positive charge at the same pH, resulting from more oxygen-containing groups on the surface [48]. Aged CNTs became more stable and dispersive in neutral water (pH = 7) with decreasing zeta potentials from −12.8 to −15.6 eV. In conclusion, lower specific surface area and higher electronegativity were detected on aged CNTs, which might affect the adsorption of other pollutants on CNTs [49].   Note: a SSA, specific surface area; b TPV, the total pore volume; c MPR, mean pore size.

Adsorption of TC on CNTs
CNTs can work as an excellent adsorbent for many pollutants due to their high affinity and adsorption capacity [50]. In this study, the physiochemical properties of CNTs were obviously changed during the aging process, which might directly disturb the adsorption of other pollutants on CNTs and further disturb the migration of these pollutants [51]. Tetracycline (TC), a broad-spectrum antibiotic detected frequently in aquatic environments, was selected as a model emerging contaminant to explore the adsorption behavior of aged CNTs. As shown in Figure 3a, the adsorption rates of aged CNTs were significantly slower in the initial adsorption stage than those of pristine CNTs. When equilibrium was reached, the adsorption of TC at 10 mg/L and 20 mg/L was almost the same on both pristine and aged CNTs. For high initial TC concentration (50 mg/L), aged CNTs adsorbed a little less TC at 1400 min, when the adsorption was not equilibrium due to high initial TC concentration. Furthermore, adsorption data was fitted using the pseudo-first-order and pseudo-second-order kinetic equations. The pseudo-second-order kinetic equation was a better for the adsorption of TC on both pristine and aged CNTs with similar q e cal values to q e exp at higher R 2 values (Table S2), implying that chemical adsorption might play the primary role [52]. The adsorption rate constants k 2 of aged CNTs were obviously lower than those of pristine CNTs, suggesting lower affinity of aged CNTs to TC. These results could explain why the adsorption of TC was significantly slower on aged CNTs in the initial adsorption stage than that on pristine CNTs. However, the similar q e of pristine and aged CNTs were observed at equilibrium point, suggesting that lower affinity might not decrease the adsorption capacity of aged CNTs. Adsorption isotherm experiments were designed to further explore the adsorpt of TC on aged CNTs. Figure 3 shows that all isotherms were non-linear. In addition, Freundlich model was much better than the Langmuir model in describing the adsorpt data with higher R 2 (Table S3). Hence, subsequent discussion was based on the adsorpt parameters from the results fitted with the Freundlich model. Moreover, it is obvious t the curves of aged carbon nanotubes are above those of pristine CNTs at both 28 °C a 40 °C, suggesting that the adsorption capacity of aged CNTs is higher than that of prist CNTs. Generally, the Freundlich isotherm model is appropriate to the adsorption on h erogeneous surfaces with varied affinities, which supposes that adsorption sites w strong affinity are first occupied and then the strength of binding weakens with increas degree of sites occupation [36]. In this study, various oxygen-containing groups were g erated on the CNTs surface during aging, and TC could adsorb on both carbon skele and oxygen-containing groups with varied affinities. In addition, these oxygen-contain groups also provided more sites for TC adsorption, and thus enhanced the adsorption TC on aged CNTs. In addition, the values of qe at 40 °C were much higher than those a °C for both pristine and aged CNTs, implying that the TC adsorption on CNTs migh endothermic, and high temperature is beneficial to enhancing the adsorption.

Site Energy Distribution Analysis
The site energy distribution was calculated to explore the energetic characteristic the interactions between CNTs and TC. E* decreased with the increasing qe for both p tine and aged CNTs (Figure 4a), indicating the existence of limited high-energy sites a the unevenness of site energy distribution [36]. These results were also in accordance w the adsorption isotherm analysis, which was better fitted with the Freundlich model heterogeneous adsorption. In addition, E* values for aged CNTs were higher than th for pristine CNTs, which was also consistent with the order of Kf (Table S3). Adsorption isotherm experiments were designed to further explore the adsorption of TC on aged CNTs. Figure 3 shows that all isotherms were non-linear. In addition, the Freundlich model was much better than the Langmuir model in describing the adsorption data with higher R 2 (Table S3). Hence, subsequent discussion was based on the adsorption parameters from the results fitted with the Freundlich model. Moreover, it is obvious that the curves of aged carbon nanotubes are above those of pristine CNTs at both 28 • C and 40 • C, suggesting that the adsorption capacity of aged CNTs is higher than that of pristine CNTs. Generally, the Freundlich isotherm model is appropriate to the adsorption on heterogeneous surfaces with varied affinities, which supposes that adsorption sites with strong affinity are first occupied and then the strength of binding weakens with increasing degree of sites occupation [36]. In this study, various oxygen-containing groups were generated on the CNTs surface during aging, and TC could adsorb on both carbon skeleton and oxygen-containing groups with varied affinities. In addition, these oxygen-containing groups also provided more sites for TC adsorption, and thus enhanced the adsorption of TC on aged CNTs. In addition, the values of q e at 40 • C were much higher than those at 28 • C for both pristine and aged CNTs, implying that the TC adsorption on CNTs might be endothermic, and high temperature is beneficial to enhancing the adsorption.

Site Energy Distribution Analysis
The site energy distribution was calculated to explore the energetic characteristics of the interactions between CNTs and TC. E* decreased with the increasing q e for both pristine and aged CNTs (Figure 4a), indicating the existence of limited high-energy sites and the unevenness of site energy distribution [36]. These results were also in accordance with the adsorption isotherm analysis, which was better fitted with the Freundlich model, as heterogeneous adsorption. In addition, E* values for aged CNTs were higher than those for pristine CNTs, which was also consistent with the order of K f (Table S3).
degree of sites occupation [36]. In this study, various oxygen-containing groups we erated on the CNTs surface during aging, and TC could adsorb on both carbon s and oxygen-containing groups with varied affinities. In addition, these oxygen-con groups also provided more sites for TC adsorption, and thus enhanced the adsorp TC on aged CNTs. In addition, the values of qe at 40 °C were much higher than tho °C for both pristine and aged CNTs, implying that the TC adsorption on CNTs m endothermic, and high temperature is beneficial to enhancing the adsorption.

Site Energy Distribution Analysis
The site energy distribution was calculated to explore the energetic character the interactions between CNTs and TC. E* decreased with the increasing qe for bo tine and aged CNTs (Figure 4a), indicating the existence of limited high-energy si the unevenness of site energy distribution [36]. These results were also in accordan the adsorption isotherm analysis, which was better fitted with the Freundlich mo heterogeneous adsorption. In addition, E* values for aged CNTs were higher tha for pristine CNTs, which was also consistent with the order of Kf (Table S3).   Figure 4b,c describes the site energy distribution curves for TC adsorption on pristine and aged CNTs. Obviously, all the curves exhibited similar shapes. F(E*) decreased sharply with increasing E*, implying that there are a few high-energy adsorption sites on both pristine and aged CNTs, and TC would occupy these high-energy sites first. In addition, relative lower F(E*) suggested that the contributions of high-energy sites (>8 kJ/mol) were limited to the overall adsorption of TC. In a certain range of E*, the area below the F(E*) curves can be regarded as the adsorption capacity and the number of available adsorption sites [35,36]. At a fixed value of E*, F (E*) was in the order of 313.15 K > 301.15 K and aged CNTs > pristine CNTs for TC. These results indicated that the adsorption sites of TC increased with increasing temperature, and that aged CNTs exhibited larger adsorption capacity and more adsorption sites than pristine CNTs, which was consistent with the adsorption isotherm analysis.

Thermodynamic Analysis
Temperature is a vital factor that influences adsorption via changing the viscosity of the aqueous solution and the brown motion of adsorbate molecules [36]. In this study, adsorption of TC on CNTs improved with increasing temperature (Figure 3b,c), and the average adsorption energy (E*) for TC is in the order of 313.15 K > 301.15 K (Figure 4), confirming that the TC adsorption on CNTs is endothermic, and high temperature is positive for their adsorption [53]. Therefore, thermodynamic parameters were calculated to further explore TC adsorption on both pristine and aged CNTs [54]. As shown in Figure 5, standard free energy change (∆G 0 ) values of aged CNTs were more negative than those of pristine CNTs, indicating that TC adsorption on aged CNTs was more spontaneous. Standard enthalpy (∆H 0 ) values for TC were positive within the tested loadings, indicating that the TC adsorption on CNTs was endothermic. Besides, ∆H 0 increased with the increasing TC loadings, implying that TC adsorption became more endothermic. Moreover, standard entropy (∆S 0 ) values of TC adsorption on both pristine and aged CNTs were positive, implying that randomness at solid-liquid interface was raised during the adsorption. Moreover, ∆S 0 values of aged CNTs increased more with the increasing loadings. These results further confirmed the conclusions of adsorption kinetics and the adsorption isotherms analysis.
increasing TC loadings, implying that TC adsorption became more endothermic. Moreover, standard entropy (△S 0 ) values of TC adsorption on both pristine and aged CNTs were positive, implying that randomness at solid-liquid interface was raised during the adsorption. Moreover, △S 0 values of aged CNTs increased more with the increasing loadings. These results further confirmed the conclusions of adsorption kinetics and the adsorption isotherms analysis.

Adsorption Mechanism
Adsorption is considered as an accumulation of adsorbate molecules from liquid phase to the adsorbent surfaces. For porous solids like CNTs, the adsorption process can be composed of three steps: (1) out-diffusion, when adsorbate molecules transfer through the liquid film to the outer surface of the adsorbent; (2) inner diffusion, when adsorbate molecules transfer from the exterior surface to the internal capillaries or pores of the adsorbent; (3) adsorbate molecules attach to the active sites on the internal and external surfaces of the adsorbent. The third step occurred rapidly, and thus it is not regarded as a rate-limiting step. In general, adsorption rate is limited by out-diffusion, inner diffusion, or both [55,56]. Meanwhile, the properties of both the adsorbate and adsorbent directly affect the adsorption [36]. In this study, aged CNTs exhibited higher adsorption capacity to TC but with a lower adsorption rate in the initial adsorption stage. These results were well explained by the changes in CNTs due to aging. Firstly, aged CNTs showed lower specific surface area and higher mean pore size (Table 2) with more defects and crystal morphology disorder ( Figure 1). The specific surface area is also vital for physical adsorption, and it also occurs rapidly in the initial adsorption stage [57]. Lower specific surface area might be the main reason why the initial adsorption rate of TC on aged CNTs was lower than that of pristine CNTs. Besides, the porous structure of CNTs is mainly mesoporous (2-50 nm), so TC molecules are mainly adsorbed on the material surface between layers, and most TC molecules are adsorbed on the pore surface of mesoporous structure [58]. Therefore, the higher mean pore size could improve the diffusion of TC in CNTs in the subsequent adsorption stage. Secondly, more oxygen-containing groups were identified on aged CNTs surface, including carbonyl and hydroxyl groups (Figure 1). Less entanglement and more fragments of CNTs were also observed in SEM images after aging ( Figure S2). Carbon nanotubes always contain many defects in structure, such as pentagonal or twist defects, heptagonal defects, and lattice defects (dangling bonds, atomic vacancies, dislocations, and interstitials) at the end caps. Defect and functional groups on aged CNTs tend to act as preferred reaction sites due to severe deformation, promoting the reaction of the chemisorption process [20]. During plasma treatment, ROS first attack the defect sites and then the edge sites, leading to the generation of oxygen-containing groups on the surfaces. There are also many polar functional groups on the TC molecule, which could interact with the oxygen-containing groups on aged CNTs via hydrogen bonding [59]. Therefore, TC could adsorb on both carbon skeleton and oxygen-containing groups of aged CNTs, and these oxygen-containing groups provided more adsorption sites, leading to higher adsorption of aged CNTs to TC. Electrostatic interaction is also considered as an important force for adsorption. TC is an amphoteric molecule, containing three protonated groups: dimethylamino, phenolic deketone, and tricarbonyl methane group [60]. In this study, aged CNTs exhibited more negative surface charge than pristine CNTs in neutral water (pH = 7) (Figure 2). However, TC exists mainly as a zwitterion at pH = 7, and thus electrostatic interaction might play a minor role in TC adsorption on CNTs in neutral water. In addition, pristine CNTs are unstable in aqueous solution and tend to aggregate, which greatly weakens their adsorption capacity. On the other hand, aged CNTs exhibited higher hydrophilicity with better dispersity, which also promoted the adsorption of TC.
In this study, we found that the adsorption of CNTs to TC is closely related to their aging. After aging, the specific surface area of CNTs decreases. More oxygen-containing groups are formed on the surface. In addition, the adsorption rate of TC is relatively slow at the beginning, but the adsorption amount is always higher than that of pristine CNTs. Previous studies have well explored the adsorption mechanism of TC on pristine CNTs: TC molecules attach tightly on CNTs surfaces due to the roles of protonated amino group and enone structures of TC, which can interact strongly with the polarized electron-rich graphene structures of CNTs via cation-π bonding and π-π electron donor-acceptor (EDA) interactions [61][62][63]. On the other hand, this could not well explain the adsorption of TC on aged CNTs. In this study, the specific surface area and surface groups of aged CNTs play more important roles in TC adsorption. The reduction of specific surface area resulted in a slow initial adsorption rate, while the generation of defects and oxygencontaining functional groups provided more active sites, improved the hydrophilicity, and facilitated the formation of hydrogen bonds. Moreover, the improved dispersity increases the number of available adsorption sites, thereby facilitating TC adsorption. In addition, the TC adsorption on CNTs was endothermic, and aged CNTs exhibited larger adsorption capacity and more adsorption sites than pristine CNTs.

Conclusions
This study investigated the aging of CNTs and explored tetracycline adsorption on aged CNTs. Plasma can comprehensively accelerate the aging of CNTs in nature. After aging, the specific surface area of CNTs decreased with more defects and crystal morphology disorder, leading to slower adsorption rate in the initial adsorption stage. More oxygen-containing functional groups were formed on the surface of aged CNTs, including carboxyl, carbonyl, and hydroxyl groups, which provide more adsorption sites for TC. Both enhancement in dispersity and hydrophilicity promoted the adsorption of TC on CNTs. Therefore, aged CNTs exhibited higher adsorption capacity to TC but with a lower adsorption rate in the initial adsorption stage. Moreover, TC adsorption on CNTs is endothermic, implying that high temperature is positive for their adsorption. As an inevitable environmental fate, aging can change the physiochemical properties of CNTs and thus affect their interaction with other pollutants. This study provides new insight for further exploration of the aging of nanomaterials in nature. Meanwhile, CNTs can adsorb more tetracycline after aging, implying that more antibiotics like tetracycline would be enriched and transported on CNTs during the aging process, increasing the threat to the ecosystem and human health.
Supplementary Materials: The following supporting information can be downloaded at: https:// www.mdpi.com/article/10.3390/w14172731/s1, Figure S1: Schematic diagram of plasma treatment of CNTs; Figure S2: SEM characterization of pristine CNTs (a, b) and aged CNTs (c, d); Figure S3: XPS spectra of pristine and aged CNTs; Figure S4: Adsorption isotherms fitted with Langmuir model of TC:(a)at 28 • C; (b)at 40 • C; Table S1: The chemical composition of the pristine and aged CNTs; Table S2: Kinetic parameters for the adsorption of tetracycline on the pristine and aged CNTs; Table S3: Isotherm parameters for tetracycline adsorbed by pristine and aged CNTs.
Author Contributions: Conceptualization, X.Z., H.L. and C.S.; methodology, C.S. and Z.Y.; Validation, C.S. and X.Z.; formal analysis, X.Z. and H.L.; investigation, X.Z. and H.L.; writing-original draft preparation, X.Z. and C.S.; writing-review and editing, C.S. and Z.Y. All authors have read and agreed to the published version of the manuscript.
Funding: This research was supported by the National Natural Science Foundation of China (U20A20146) and the Young Scholars Program of Shandong University.