Room temperature synthesis of water-soluble spherical particles of a uniform diameter composed of carbon nanobelts and C60 molecules

A carbon nanobelt (CNB) is a loop of fused benzene rings and a C60 molecule is a football shaped fullerene composed of 60 carbon atoms. In this study, we synthesize uniform spherical particles composed of (6,6)CNBs and C60 molecules in 1,2-dichlorobenzene at room temperature via bottom-up self-assembly, setting the molar concentrations of (6,6)CNBs and C60 molecules at appropriate values, and find that the particles are monodisperse even in water. The present room temperature synthetic methodology may well be applied to the creation of nano/micro structures/materials using basic carbon nano units such as cycloparaphenylene (CPP, carbon nanorings) and fullerenes; e.g., C60, C70 and C59N.


Scientific Reports
| (2022) 12:15207 | https://doi.org/10.1038/s41598-022-19475-z www.nature.com/scientificreports/ shown in Fig. 1, where the ratio of the molar concentration of (6,6)CNBs to that of C 60 was 1:2. The size of the particles increased with time (see also Fig. S3 in the Supplementary Information for the size distributions of the particles as a function of the time and Fig. 2 for the time variation of the diameter of a particle). Note that no particles were formed in the solution of (6,6)CNBs dissolved in 1,2-dichlorobenzene and in the solution of C 60 molecules dissolved in 1,2-dichlorobenzene. The surface of the spherical particles was smooth and the diameter of a particle was uniform when the particles were synthesized setting the ratio of the molar concentration of (6,6)CNBs to that of C 60 at 1:2 as mentioned, whereas the surface of the particles was uneven and the size of a particle varied when the ratio was different from 1:2 (see Fig. S4 in the supplementary Information for the size distributions and SEM images of particles produced when the ratio of the molar concentration of (6,6)CNBs to that of C 60 was 1:1, 1:2 and 1:3). The absorption spectra by the supernatant of the solution, in which a mixture of (6,6)CNBs and C 60 molecules were dissolved in 1,2-dichlorobenzene, are shown in Fig. S5 in the Supplementary Information, where the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules was changed (see Fig. S5a) in the Supplementary Information) and the time variation of the absorption spectra when the ratio of the molar concentration of (6,6) CNBs to that of C 60 molecules was 1:2 is shown in Fig. S5b in the Supplementary Information. Note that the wavelengths of photons absorbed by (6,6)CNBs and C 60 dissolved in 1,2-dichlorobenzene had been measured and those by (6,6)CNBs were 296, 318, 355, 373 and 396 nm, while those by C 60 were 297, 329 and 407 nm (see Fig. S6 in the Supplementary Information for the absorption spectra by the individual solution of C 60 and (6,6)CNBs dissolved in 1,2-dichlorobenzene). It is supposed that m × (6,6)CNBs and n × C 60 molecules ((m, n) = (2, 1) and (1, 1 ~ 3) in the present study. See Methods Table 2) were combined to form a compound of ((6,6)CNB) m -(C 60 ) n in the solution since the absorption peaks corresponding to (6,6)CNBs and C 60 decreased when the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules was m:n, noting that smooth spherical particles of a uniform diameter were formed when the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules  Time variation of the diameter of a particle and the peaks' intensities of the absorption spectra corresponding to (6,6)CNBs and C 60 molecules dissolved in 1,2-dichlorobenzene. The ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules is 1:2. Dotted red line-absorbance of 318 nm; dotted green line-absorbance of 329 nm; dotted blue line-average diameter of a particle. www.nature.com/scientificreports/ was 1:2 as mentioned. The ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules was increased by increasing the molar concentration of C 60 molecules, keeping the molar concentration of (6,6)CNBs constant (see Methods Table 2). When the ratio was 1:2, compounds composed of (6,6)CNB-(C 60 ) 2 were produced and spherical particles of a uniform diameter were formed by the compounds as mentioned above. However, there were still individual (6,6)CNBs, which did not participate in the formation of the compounds; (6,6)CNB-(C 60 ) 2 , in the solution from a statistical point of view. As the ratio of the molar concentrations was increased to 1:2.25, 1:2.5, 1:2.75 and 1:3, it is supposed that those individual CNBs and C 60 molecules formed different types of compounds such as (6,6)CNB-C 60 in addition to (6,6)CNB-(C 60 ) 2 , noting that the excess C 60 molecules were also physically attached to those compounds, and as a result, the number of (6,6)CNBs decreased in the solution and therefore the absorption at 318 nm was reduced. Note that the shape of the particles was non-spherical and the size distribution was broad as shown in Fig. S4c in the Supplementary Information in the case of higher ratio of the molar concentrations. The intensity of the absorption spectra corresponding to (6,6)CNBs and C 60 molecules decreased with time (see Fig. S5b in the Supplementary Information, where the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules was set at 1:2). In other words, the number of compounds; (6,6)CNB-(C 60 ) 2 , increased with time and those compounds formed spherical particles. The time variation of the diameter of a particle and the peaks of the absorption spectra corresponding to (6,6) CNBs and C 60 molecules in 1,2-dichlorobenzene are shown in Fig. 2, where the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules was set at 1:2. The diameter of a particle increased with time, whereas the amount of (6,6)CNBs and C 60 molecules in the solution decreased with time, which means that the number of (6,6)CNB-(C 60 ) 2 produced in the solution and the diameter of a particles formed by (6,6)CNB-(C 60 ) 2 increased with time as mentioned.
The mean diameter of a particle formed 168 h after the mixture of the two solutions and the hydrodynamic diameter and zeta potential of a particle dispersed in distilled water are shown in Table 1, where the particles were synthesized setting the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules at 1:2. The diameter and hydrodynamic diameter of a particle synthesized 168 h after the mixture of the two solutions were quite uniform. Importantly, the absolute value of the zeta potential of a particle dispersed in water was so high as 38.8 mV that the particles were monodisperse even in water (see Fig. S7 and Video S1 in the Supplementary Information for the precipitation process of the solution and Fig. S8 in the Supplementary Information for the time variation of the turbidity of the suspension). Note that the particles eventually precipitated in water due to their own weight, but once the suspension had been shaken, the particles evenly dispersed again thanks to the high absolute value of the zeta potential in water (see Video S2 in the Supplementary Information).
The result of the thermogravimetric (TG) analysis of the particles is shown in Fig. S9 in the Supplementary Information. There was no significant weight loss and the overall weight loss was 0.47% (7 µg/1.485 mg). We suppose that 1,2-dichlorobenzene was not contained in the particles. Even if it had been contained in the particles, the amount of 1,2-dichlorobenzene would have been only 47 nmol in 1485 mg of particles. Note that the Table 1. Diameter of a particle produced 168 h after the mixture of the two solutions, and the hydrodynamic diameter and zeta potential of a particle dispersed in distilled water. The particles were synthesized setting the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules at 1:2 (the concentrations of (6,6)CNBs and C 60 molecules were, respectively, 0.35 and 0.70 µmol ml −1 ). a The diameter of the particles was measured, targeting at 100 particles from SEM images. b The hydrodynamic diameter of a particle dispersed in distilled water was measured by Zetasizer. c The zeta potential of a particle dispersed in distilled water was measured by Zetasizer. www.nature.com/scientificreports/ particles were also monodisperse in water even after the TG analysis, the zeta potential of the particles after the TG analysis being the same as that of the particles before the TG analysis. The mass spectra of particles formed 168 h after the mixture of the two solutions are shown in Fig. S10 in the Supplementary Information, which indicates that (6,6)CNBs are positively charged, while C 60 molecules are negatively charged. It is therefore supposed that the particles were formed by compounds composed of positively charged (6,6)CNBs and negatively charged C 60 .
We carried out some preliminary simulations concerning the structures formed by compounds [(6,6)CNB-(C 60 ) m ] n , where (m, n) = (1, 1), (2, 1), (2,2) and (2,3), based on a semi-empirical method; PM6 25 , according to which a compound; (6,6)CNB-(C 60 ) 2 , can be stably formed, but triple compounds are not aligned in a regular form (see Fig. S11 in the Supplementary Information). Based on the experimental and numerical results, it is supposed that two C 60 molecules and one (6,6)CNB were bonded via charge transfer to form compounds composed of C 60 -(6,6)CNBs-C 60 , noting that a peak around 204 nm in the absorption spectrum by the particles dispersed in ethanol was induced by charge transition (see Fig. S12 in the Supplementary Information).
A TEM image of a particle formed when the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules was 1:2 is shown in Fig. S13 in the Supplementary Information. It is clearly shown that the particle is not formed by regularly oriented compounds. An XRD spectrum of the particles is shown in Fig. S14 in the Supplementary Information. There were no clear/sharp diffraction peaks and therefore it is supposed that the particles are formed by randomly oriented compounds composed of C 60 -(6,6)CNBs-C 60 .
In summary, particles composed of (6,6)carbon nanobelts and C 60 molecules were synthesized via selfassembly at room temperature by mixing two solutions of (6,6)carbon nanobelts and C 60 molecules dissolved in 1,2-dichlorobenzene. Smooth spherical particles of a uniform diameter were formed particularly when the ratio of the molar concentration of (6,6)CNBs to that of C 60 molecules was set at 1:2 (the concentrations of (6,6) CNBs and C 60 molecules were 0.35 and 0.70 µmol ml −1 ). It is supposed that compounds composed of C 60 -(6,6) CNBs-C 60 were self-assembled in the solution, two C 60 molecules and one (6,6)CNB having been bonded via charge transfer, and that the particles were formed by randomly oriented compounds. The absolute value of the zeta potential of the particles dispersed in distilled water was so high that the particles were monodisperse in water, which means that the particles may well be used as stable colloidal particles in water. The present synthetic methodology is so simple that it may also be applied to the creation of nano/micro structures/materials using basic carbon nano units such as [n]cycloparaphenylene (CPP, carbon nanorings) and fullerenes; e.g., C 60 , C 70 and C 59 N.

Methods
Synthetic procedure of particles. We developed a facile room temperature methodology for producing particles composed of (6,6)CNBs and C 60 molecules. The synthetic procedure is summarized below.
Characterization and observation procedure. The following is the characterization and observation procedure.
(a)The absorption spectra by the supernatant of the solution were measured by ultraviolet-visible (UV-Vis) spectroscopy (DU730, Beckman Coulter Inc.). The individual absorption spectrum of C 60 and (6,6)CNBs dissolved in 1,2-dichlorobenzene was also measured in the same manner. (b)The structures of the particles were observed by scanning electron microscopy (SEM) (SU8030, Hitachi Ltd.) and transmission electron microscopy (TEM) (2200FS, JEOL Ltd.). The size of the particles was measured, targeting at 100 particles from the SEM images. (c)The hydrodynamic diameter and zeta potential of the particles dispersed in distilled water were measured by Zetasizer (Nano-ZS, Malvern Panalytical Ltd.). (d)The precipitation process of the particles dispersed in distilled water was observed, photographed and recorded on videotape. The intensity of the transmitted light of 500 and 600 nm wavelengths through the whole solution confined in a glass container was measured with a spectral photometer (U-3500 Spectrophotometer, Hitachi High-Tech Co.) and the turbidity, which was defined as (1 − I trans /I in ) × 100% , where I in and I trans are, respectively, the intensities of the incident and transmitted light, was obtained. (e)Thermogravimetric (TG) analysis of the particles was carried out by a TG analyser (DTG-60, Shimadzu Corp.). The temperature was raised at a rate of 15.9 K min −1 up to 300 °C and the temperature was kept at 300 www.nature.com/scientificreports/°C for 60 min with the flow of N 2 gas. The measurement of the weight was calibrated with a precision scale (Excellence plus XP56, Mettler-Toledo International Inc.). (f)The molecular weight of the compounds forming the particles was measured with time-of-flight mass spectrometry (TOF-MS) (autoflex2, Bruker Co.). (g)The absorption spectrum by the particles dispersed in ethanol was measured by the UV-Vis spectroscopy (DU730, Beckman Coulter Inc.). (h)A droplet of the suspension of particles dispersed in ethanol was dropped onto a silicon-low background sample holder (M00016288, Rigaku Corp.) and X-ray diffractometric characterization of the particles was carried out by an X-ray diffractometer (SmartLab, Rigaku Corp.).

Data availability
All of the data supporting this work are available from the corresponding author upon reasonable request.