Waste Biomass Selective and Sustainable Photooxidation to High-Added-Value Products: A Review

: Researchers worldwide seek to develop convenient, green, and ecological production processes to synthesize chemical products with high added value. In this sense, lignocellulosic biomass photocatalysis is an excellent process for obtaining various outcomes for the industry. One issue of biomass transformation via heterogeneous catalysis into valuable chemicals is the selection of an adequate catalyst that ensures high conversion and selectivity at low costs. Titanium oxide (TiO 2 ), is widely used for several applications, including photocatalytic biomass degradation, depolymerization, and transformation. Graphite carbon nitride (g-C 3 N 4 ) is a metal-free polymeric semiconductor with high oxidation and temperature resistance and there is a recent interest in developing this catalyst. Both catalysts are amenable to industrial production, relatively easy to dope, and suited for solar light absorption. Recent investigations also show the advantages of using heterojunctions, for biomass derivates production, due to their better solar spectrum absorption properties and, thus, higher efﬁciency, conversion, and selectivity over a broader spectrum. This work summarizes recent studies that maximize selectivity and conversion of biomass using photocatalysts based on TiO 2 and g-C 3 N 4 as supports, as well as the advantages of using metals, heterojunctions, and macromolecules in converting cellulose and lignin. The results presented show that heterogeneous photocatalysis is an interesting technology for obtaining several chemicals of industrial use, especially when using TiO 2 and g-C 3 N 4 doped with metals, heterojunctions, and macromolecules because these modiﬁed catalysts permit higher conversion and selectivity, milder reaction conditions, and reduced cost due to solar light utilization. In order to apply these technologies, it is essential to adopt government policies that promote the use of photocatalysts in the industry, in addition to encouraging active collaboration between photooxidation research groups and companies that process lignocellulosic


Introduction
Biomass is a plentiful and carbon-neutral renewable energy source that may be used to create platform chemicals and fuels, especially considering that up to 75% of initial energy can be converted into biofuels. Lignocellulosic biomass comprises lignin, cellulose, and hemicellulose; lignin is almost 30% of the organic carbon in the biosphere. However, this lignin is regarded as waste material in several industries, for example, during paper TA and agricultural production, leaving significant amounts of biomass that contaminates the

Materials and Methods
The methodology employed to carry out this review centers on the keywords: "photocatalysis," "biomass," and "chemical products" using the Boolean operator AND, resulting in a total of 91 documents indexed in the Web of Science database (Figure 1). The last search was performed on 15 May 2022. Since 2016, it is possible to notice how the interest in obtaining chemical products from biomass has grown. Thus, in 2020 the number of publications doubled compared to 2018 and 2019, and the trend continues. Figure 2 shows relevant papers about the photocatalytic transformation of biomass, where the studies of Colmenares et al. [5] and Lang et al. [40] stand out. It is worth noting that Figure 2 arranges papers according to their similarity but is not a citation tree. Related reports show connecting lines and clusters. The larger the bubble, the more citations; the darker colors indicate recently published papers. products with high added value, as well as to determine if the addition of on the surface of photocatalysts will shorten the reaction time in the conver This review is organized as follows. The methodology adopted to cla pertinent articles is presented in Section 2. Then, the main concepts related t its derivatives are detailed in Section 3. Section 4 recounts a summary of th involved in heterogeneous photocatalysis. Then, the most used photocat sented in Section 5, highlighting titanium dioxide (TiO2), carbon nitride ( metals, and the applicability of heterojunctions and macromolecules. Then of cellulose and lignin is presented in Section 6, and finally, the main co perspectives for future work are set out.

Materials and Methods
The methodology employed to carry out this review centers on the ke tocatalysis," "biomass," and "chemical products" using the Boolean oper sulting in a total of 91 documents indexed in the Web of Science database ( last search was performed on 15 May 2022. Since 2016, it is possible to n interest in obtaining chemical products from biomass has grown. Thus, in ber of publications doubled compared to 2018 and 2019, and the trend con 2 shows relevant papers about the photocatalytic transformation of biom studies of Colmenares et al. [5] and Lang et al. [40] stand out. It is worth not 2 arranges papers according to their similarity but is not a citation tree. R show connecting lines and clusters. The larger the bubble, the more citatio colors indicate recently published papers.  Published articles Year Keywords: photocatalysis AND biomass AND chemical products

Biomass
Lignocellulosic biomass is the primary structural component of plant matter and is mostly inedible, generally referring to organic materials such as wood, grass, and agricultural crop residues [41,42]. The principal lignocellulosic biomass components are: lignin (20-30% w/w), cellulose (35-50% w/w) and hemicellulose (20-30% w/w) [41,42]. Regarding the structure of lignocellulosic biomass (Figure 3), the external cell of the biomass, which provides rigidity to the material, is rich in lignin [43,44]. It is a macromolecular polyaromatic with a high oxygen content [45,46]. On the other hand, cellulose is found inside lignin and forms hemicellulose-bound shells with a random structure. It is a stable crystalline biopolymer made of glycoside units. These units are insoluble in most solvents and difficult to hydrolyze [47]. Hemicellulose has an amorphous structure of pentose sugars such as xylose and arabinose, and hexose carbohydrates such as glucose, mannose, and galactose, so it is easier to hydrolyze than cellulose [10,47].
Although processing complex lignocellulosic materials is one of the main obstacles to commercial-scale biofuels and renewable chemicals, stimulating biofuel production has economic, environmental, and societal benefits. Different types of photocatalysts and reactors have been studied to decompose and process lignocellulosic biomass (or its components) [48,49].

Biomass
Lignocellulosic biomass is the primary structural component of plant matter and is mostly inedible, generally referring to organic materials such as wood, grass, and agricultural crop residues [41,42]. The principal lignocellulosic biomass components are: lignin (20-30% w/w), cellulose (35-50% w/w) and hemicellulose (20-30% w/w) [41,42]. Regarding the structure of lignocellulosic biomass (Figure 3), the external cell of the biomass, which provides rigidity to the material, is rich in lignin [43,44]. It is a macromolecular polyaromatic with a high oxygen content [45,46]. On the other hand, cellulose is found inside lignin and forms hemicellulose-bound shells with a random structure. It is a stable crystalline biopolymer made of glycoside units. These units are insoluble in most solvents and difficult to hydrolyze [47]. Hemicellulose has an amorphous structure of pentose sugars such as xylose and arabinose, and hexose carbohydrates such as glucose, mannose, and galactose, so it is easier to hydrolyze than cellulose [10,47].
Although processing complex lignocellulosic materials is one of the main obstacles to commercial-scale biofuels and renewable chemicals, stimulating biofuel production has economic, environmental, and societal benefits. Different types of photocatalysts and reactors have been studied to decompose and process lignocellulosic biomass (or its components) [48,49].
Bio-oil is obtained from the lignocellulosic biomass conversion through thermal, catalytic, or both processes combined. The resulting bio-oil comprises oxygenated monomers such as cresols and guaiacols [6,50]. However, due to its high oxygen content, bio-oil is unstable and has a low energy content, and requires additional treatment to be used industrially [51]. Consequently, the transformation of platform molecules from lignocellulosic biomass (starting materials or building blocks to produce chemical products) has been identified as critical in converting biomass into fuels and chemical compounds [52]. The goal is to replace petrochemical compounds with renewable and sustainable com- Bio-oil is obtained from the lignocellulosic biomass conversion through thermal, catalytic, or both processes combined. The resulting bio-oil comprises oxygenated monomers such as cresols and guaiacols [6,50]. However, due to its high oxygen content, bio-oil is unstable and has a low energy content, and requires additional treatment to be used industrially [51]. Consequently, the transformation of platform molecules from lignocellulosic biomass (starting materials or building blocks to produce chemical products) has been identified as critical in converting biomass into fuels and chemical compounds [52]. The goal is to replace petrochemical compounds with renewable and sustainable compounds progressively. Moreover, the derivatization of compounds from biomass is crucial in recovering chemical products.
Some of the factors responsible for the attractiveness of biomass as a renewable source for conversion to chemical products are climate change and reduction in greenhouse gases [53], the need to search for renewable carbon sources as an alternative to fossil sources [53], the possibility to optimize the process of obtaining energy and chemical products [54], and finally, increasing public trust in the chemical business.
Selective oxidation of derivatives of lignocellulosic biomass is a promising process for obtaining chemical products in a sustainable way [55]. The biggest challenge is to make this process profitable with a high conversion yield and selectivity of degradation reactions. However, producing these chemicals requires high temperatures and high pressures, which results in increased energy consumption [56]. Furthermore, the conversion and selectivity percentages are low [44,45,57]. For this reason, the photocatalytic process for the selective conversion of biomass derivatives is viewed as a sustainable and innovative technology. Because it is simple and low-cost, solar energy used in the process is abundant and is one of the cheapest alternative energy resources; photocatalytically, this can be transformed into chemical energy.

Heterogeneous Photocatalysis
In recent years, heterogeneous photocatalysis has been regarded as one of the most promising technologies for addressing environmental issues and the global energy crisis Some of the factors responsible for the attractiveness of biomass as a renewable source for conversion to chemical products are climate change and reduction in greenhouse gases [53], the need to search for renewable carbon sources as an alternative to fossil sources [53], the possibility to optimize the process of obtaining energy and chemical products [54], and finally, increasing public trust in the chemical business.
Selective oxidation of derivatives of lignocellulosic biomass is a promising process for obtaining chemical products in a sustainable way [55]. The biggest challenge is to make this process profitable with a high conversion yield and selectivity of degradation reactions. However, producing these chemicals requires high temperatures and high pressures, which results in increased energy consumption [56]. Furthermore, the conversion and selectivity percentages are low [44,45,57]. For this reason, the photocatalytic process for the selective conversion of biomass derivatives is viewed as a sustainable and innovative technology. Because it is simple and low-cost, solar energy used in the process is abundant and is one of the cheapest alternative energy resources; photocatalytically, this can be transformed into chemical energy.

Heterogeneous Photocatalysis
In recent years, heterogeneous photocatalysis has been regarded as one of the most promising technologies for addressing environmental issues and the global energy crisis [57][58][59]. This process is one of the cleanest because it needs few reactants, operates under smooth conditions, and takes advantage of visible and ultraviolet (U.V.) light [59][60][61][62][63]. Heterogeneous photocatalysis is a mechanism of absorbing direct or indirect radiant radiation (visible or U.V.) using a broadband semiconductor. It is feasible to activate it when the catalyst absorbs a photon with an energy equal to or greater than the bandgap (Bg); for example, solar radiation promotes electron transport from the valence band (V.B.) to the conduction band (C.B.) [64]. In this way, hole-electron pairs (h + -e − ) are formed, which are charge carriers for photochemical oxidation and reduction reactions (Equation (1)) [63][64][65][66][67][68].
Some of the pollutants that have been degraded by heterogeneous photocatalysis are rhodamine B [69], amoxicillin [70], tetracycline antibiotics [71], tetracycline hydrochloride [72], and phenol [73]. Based on these works, it is possible to state that the approach is effective because the deterioration percentages in all the experiments exceeded 70%. Moreover, in recent years this process has also been implemented to obtain specific chemical products, such as the selective photo-reduction of carbon dioxide (CO 2 ) to hydrocarbons [61,62,74,75]. Some clear examples are the studies developed by Ahmed et al. [76] and Tasbihi et al. [77], where methane is obtained. Selective photooxidation has also been used to produce aldehydes from alcohols [59,78]. López-Tenllado et al. [79] studied the oxidation of 2-butenol (crotyl alcohol) to 2-butenal (crotonaldehyde), achieving 70% conversion and 90% selectivity after 90 min of reaction. It was also shown that these processes are substantially influenced by the reaction time and pH of the solution. In addition, there are various intermediates between the reagents and the end products, which provide convenient control over the selective reactions of certain bonds in the lignin derivates to obtain useful chemical products [65,80]. Another advantage of the photocatalytic process is that the reactions can be carried out at mild conditions, such as room temperature and atmospheric pressure, thanks to a photon interchange instead of thermal energy [81]. Thus, it is possible to promote the selective photooxidation of by-products of lignocellulosic biomass. It is possible to obtain the so-called platform molecules that include a great variety of carboxylic acids [42,53,82].
Success in the photocatalysis process lies in the proper use of photocatalysts since they are the ones that use solar energy to promote the transport of electrons from the V.B. to the C.B. as seen in Figure 4 [7,65,83]. In heterogeneous photocatalysis, one electron (e − ) jumps up from the valence band to the conduction band, after absorbing a photon with higher energy than the bandgap energy. This leap leaves a vacancy called a hole (h + ) in the V.B. [84]. Electrons carry out the reduction process in the conduction band. The most typical reduction method is biomass photo-reforming, which involves the reduction of a proton by an e-to form hydrogen (H 2 ). During this process, photoinduced holes oxidize lignocellulose or its derivatives, lowering the recombination rate of photogenerated hole-electron pairs and boosting the water-splitting efficiency [85].
It is possible to obtain value-added products when intermediate partially oxidized products are determined as the final product. Photocatalytic holes produce oxidative radicals that directly or indirectly oxidize specific organic molecules [86]. An oxidative hole, for example, reacts with hydroxyl ions (OH − ) to form hydroxyl radicals (•OH, potential redox: +2.81 V versus standard hydrogen electrode (SHE)) [1,8,40,86]. Then, the oxidative radicals target the biomass molecules; for example, Figure 5 shows a lignin photo-reforming process, where reactive •OH radicals degrade lignin due to the bond cleavage of β-O-4 [87]. This lignin bond break results in the generation of benzyl, alkoxy, and alkyl radicals that produce lignin fragments with a low molecular weight during the depolymerization reaction. Hydroxyl and •OH radicals can also directly attack lignin's phenyl rings forming catechol, resorcinol, and hydroquinone [88]. During the photocatalytic process, other reactive oxygen species can be formed, including superoxide anions (O 2 •− , potential redox: +0.89 V versus SHE), singlet molecular oxygen (O 2 ), and ozone O 3 [62,63].  It is possible to obtain value-added products when intermediate partially o products are determined as the final product. Photocatalytic holes produce oxidat icals that directly or indirectly oxidize specific organic molecules [86]. An oxidati for example, reacts with hydroxyl ions (OH − ) to form hydroxyl radicals (•OH, p redox: +2.81 V versus standard hydrogen electrode (SHE)) [1,8,40,86]. Then, the o radicals target the biomass molecules; for example, Figure 5 shows a lignin photoing process, where reactive •OH radicals degrade lignin due to the bond cleavage 4 [87]. This lignin bond break results in the generation of benzyl, alkoxy, and alkyl that produce lignin fragments with a low molecular weight during the depolyme reaction. Hydroxyl and •OH radicals can also directly attack lignin's phenyl ring ing catechol, resorcinol, and hydroquinone [88]. During the photocatalytic proces reactive oxygen species can be formed, including superoxide anions (O2 •− , potentia +0.89 V versus SHE), singlet molecular oxygen (O2), and ozone O3 [62,63].

Photocatalysts for Biomass Conversion
The photocatalyst nature is the central part of the heterogeneous photocatalysis process. The success in biomass degradation and conversion reactions depends on its properties [58,89]. One of the most remarkable properties of TiO2 is absorbing visible light, Figure 5. Lignin photo-reforming process directly attacks lignin's phenyl rings, forming catechol and hydroquinone [87].

Photocatalysts for Biomass Conversion
The photocatalyst nature is the central part of the heterogeneous photocatalysis process. The success in biomass degradation and conversion reactions depends on its properties [58,89]. One of the most remarkable properties of TiO 2 is absorbing visible light, which permits it to work at an industrial level with sunlight [90,91]. Several works have been identified in which TiO 2 and g-C 3 N 4 have been used as successful photocatalysts for different degradation processes and some selective conversions, such as selective oxidation of alcohols to aldehyde [58,91]. In several studies, combining photocatalysts with other metals provided them with new and better properties. This doping increases the conversion and selectivity while improving the reaction yields [59,71,92]. The following section presents the major advances in photocatalysts, highlighting doping with noble metals, heterojunctions, and macromolecules to improve the performance of photocatalysts based on titanium dioxide and carbon nitride.

Titanium Dioxide TiO 2
Titanium dioxide (TiO 2 ) is one of the most used and attractive heterogeneous photocatalysts, especially in processes of degradation of pollutants in [73,93], due to its excellent properties such as high photocatalytic activity, strong oxidizing capacity, chemical stability, long durability, non-toxicity, low cost, and transparency to visible light [94]. The difficulty is that it has a bandgap in the ultraviolet area of the electromagnetic spectrum with an energy of 3.23 eV [70,94], i.e., TiO 2 can only use between 3% and 5% of the solar spectrum of visible light, in addition to the recombination of excited pairs (h + -e − ), which restricts its applications in photocatalysis [91][92][93][94][95][96][97][98][99]. There are several crystalline structures of TiO 2 , e.g., anatase, rutile, and brookite titanium dioxide; they differ in their three-dimensional form, as can be seen in Figure 6. TiO2, e.g., anatase, rutile, and brookite titanium dioxide; they differ in their three-dimensional form, as can be seen in Figure 6. In 1996, it was suggested that anatase's conduction band is 0.2 eV higher than that of rutile because the flat band potential of anatase is 0.2 eV lower than that of rutile, as seen in Figure 7; at an interface, this promotes photogenerated electron transfer from anatase to rutile and hole transfer from rutile to anatase [103,104]. However, new photoemission experiments show that the work function of anatase is 0.2 eV higher than that of rutile, implying that anatase's conduction band is 0.2 eV lower than that of rutile, and thus implying more light absorption [105,106]. In 1996, it was suggested that anatase's conduction band is 0.2 eV higher than that of rutile because the flat band potential of anatase is 0.2 eV lower than that of rutile, as seen in Figure 7; at an interface, this promotes photogenerated electron transfer from anatase to rutile and hole transfer from rutile to anatase [103,104]. However, new photoemission experiments show that the work function of anatase is 0.2 eV higher than that of rutile, implying that anatase's conduction band is 0.2 eV lower than that of rutile, and thus implying more light absorption [105,106].
In 1996, it was suggested that anatase's conduction band is 0.2 eV higher than that of rutile because the flat band potential of anatase is 0.2 eV lower than that of rutile, as seen in Figure 7; at an interface, this promotes photogenerated electron transfer from anatase to rutile and hole transfer from rutile to anatase [103,104]. However, new photoemission experiments show that the work function of anatase is 0.2 eV higher than that of rutile, implying that anatase's conduction band is 0.2 eV lower than that of rutile, and thus implying more light absorption [105,106].

Carbon Nitride (g-C 3 N 4 )
Carbon nitride (g-C 3 N 4 ) has a stable structure and semiconductor characteristics [93,107]. It has a bandgap energy of approximately 2.88 eV, allowing greater visible light absorption than TiO 2 [107,108]. It has an excellent photocatalytic performance, strong chemical stability, and good resistance to acid and alkali corrosion, making it a favorite in photocatalysis. Furthermore, it is easy to synthesize since it only requires a calcination step of readily available precursors such as cyanamide, melamine, or urea (in the range of 500-580 • C for 1-4 h) [109,110]. However, some defects have also been reported, such as a small specific area, low separation degree of electrons and holes, and a limited visible light range for some reactions [109,111].
The search for photocatalysts with higher efficiency in separating photogenerated pairs has become an important research field. Photocatalytic systems related to carbon nitride are practical and efficient for the spatial separation of photogenerated electron-hole pairs; furthermore, they permit the development of heterostructures based on g-C 3 N 4 [90,110,112]. The heterostructures based on g-C 3 N 4 offer superior photocatalyst qualities due to the synergy between g-C 3 N 4 and the other components of the heterostructures. The heterostructures based on g-C 3 N 4 may inhibit the recombination of photogenerated charge carriers offering better photocatalyst qualities [90,113].
The construction of photocatalysts with high efficiency driven by visible light for environmental and energy applications, as well as lowering processing time, may be possible by the design of g-C 3 N 4 -based heterostructures; Figure 8 [71,90,113]. due to the synergy between g-C3N4 and the other components of the heterostructures. The heterostructures based on g-C3N4 may inhibit the recombination of photogenerated charge carriers offering better photocatalyst qualities [90,113].
The construction of photocatalysts with high efficiency driven by visible light for environmental and energy applications, as well as lowering processing time, may be possible by the design of g-C3N4-based heterostructures; Figure 8 [71,90,113].

Doping with Noble Metals
Catalyst doping involves the addition of a foreign species to the catalytic system; therefore, the original activity of the catalyst varies. To improve the efficiency of sun-

Doping with Noble Metals
Catalyst doping involves the addition of a foreign species to the catalytic system; therefore, the original activity of the catalyst varies. To improve the efficiency of sun-driven photocatalysis, noble metal nanoparticles (N.P.s) extend the U.V. absorption characteristics of TiO 2 and g-C 3 N 4 to the visible area [111,114]. Surfaces doped with noble metals such as Au, Ag, Pd, and Pt lead to enhanced photogenerated electron transfer and lifetime extension of carriers'. As a result of localized surface plasmon resonance, N.P.s can absorb visible light and hence activate broadband semiconductors (e.g., TiO 2 ) on the visible light spectrum [96,110,112,114].
In the study of Darabdhara et al. [114], the degradation of several phenolic compounds by photocatalysis was analyzed, and an oxidation process was observed. Table 1 summarizes the primary metals used in the photocatalysis process, while Table 2 details the obtained reagents and products and conversion and selectivity percentages. The intermediate products were catechol, hydroquinone, and p-benzoquinone; the photocatalyst used was g-C 3 N 4 . It was possible to prove that when g-C 3 N 4 was doped with metallic N.P.s, the photocatalytic process presented a 90% percentage of degradation, compared to the 42% obtained when using no modified photocatalyst. Furthermore, it was shown that the process was more efficient when working with sunlight than with U.V. light, so it is concluded that the use of noble metals favors the absorption of light in the visible spectrum [109,117].

Heterojunctions
Another technique used to achieve high efficiency in space charge separation and extend light absorption to the visible range is the construction of heterojunctions, which involve the combination of two or more semiconductors depending on their band gaps [89,118].
Straddling, staggered and broken gap heterojunctions are based on the alignment of energy levels, as shown in Figure 9. The first type indicates that the bandgap of the semiconductor-I is wider than that of semiconductor-II, the V.B. of the semiconductor-I is below that of the semiconductor-II, and the C.B. of the semiconductor-II is higher than the C.B. of the semiconductor-I, forming a space that can take both directions. Due to this, the migration of charge carriers generates an accumulation of electrons and holes that occurs only in the semiconductor-I, which causes poor charge separation of the photogenerated pairs of electrons and holes, in addition to a lower redox potential because the oxidation and reduction reactions occur in the same semiconductor [64]. In the second heterojunction type, the band positions are at optimal levels (staggered gap), offering a space charge carrier for enhanced photocatalytic separation compared to type I. However, its redox potential is low due to oxidation and reduction reactions that occur in semiconductor-I with lower oxidation potential and semiconductor-II with lower reduction potential [89,118,119]. Type III heterojunctions have a broken gap involving charge carrier separation, similar to type II heterojunctions 119]. The broken bandgap of the heterojunction in type III does not cross and does not cause charge carrier separation to enhance photocatalytic activity.
In this way, the Z scheme is formed and the electrons receiving the irradiation of visible light in the C.B. of semiconductor-II are combined with holes of the photogenerated V.B. of semiconductor-I. This combination leads to the formation of sufficiently strong oxidative V.B. holes in semiconductor-II and reducing electrons in the C.B. of semiconductor-I, as seen in Figures 9 and 10. Due to the band difference, the induced interface results in an electric field capable of accelerating the separation of the photogenerated pairs (h + -e − ) [118,119].   The scheme name, Z, Figure 11, is proposed because it mimics photosynthesis in plants and follows the same charge transfer pathway mechanism containing two-step photoexcitation, which shows resemblance to the letter "Z" [89,119].
Some studies show that converting biomass-derived molecules into other more valuable ones is possible using middle reaction conditions. For example, Shao et al. [120] developed the Co/ZnO@C heterojunction catalyst for biomass derivative hydrogenation that permitted the selective hydrogenation of levulinic acid to γ-valerolactone, achieving 89.28% conversion and 92.47% selectivity at 120 °C, 2 MPa, and 4 h reaction conditions, improving previous investigations that needed higher temperature and pressure [6,121] Moreover, Chen et al. [121] converted furfural into cyclopentanone using their catalyst fabricated of a Ni−NiO heterojunction supported on TiO2 with anatase and rutile (Ni−NiO/TiO2-Re450), achieving 100% conversion and 84.7% yield under 1 MPa, 140 °C, and 6 h reaction conditions. Both examples show that heterojunctions improve the performance of commonly used catalyzers such as TiO2, lowering the reaction conditions and reducing energy costs if they are going to be applied at the industrial scale [122]. The scheme name, Z, Figure 11, is proposed because it mimics photosynthesis in plants and follows the same charge transfer pathway mechanism containing two-step photoexcitation, which shows resemblance to the letter "Z" [89,119].
Some studies show that converting biomass-derived molecules into other more valuable ones is possible using middle reaction conditions. For example, Shao et al. [120] developed the Co/ZnO@C heterojunction catalyst for biomass derivative hydrogenation that permitted the selective hydrogenation of levulinic acid to γ-valerolactone, achieving 89.28% conversion and 92.47% selectivity at 120 • C, 2 MPa, and 4 h reaction conditions, improving previous investigations that needed higher temperature and pressure [6,121] Moreover, Chen et al. [121] converted furfural into cyclopentanone using their catalyst fabricated of a Ni−NiO heterojunction supported on TiO 2 with anatase and rutile (Ni−NiO/TiO 2 -Re450), achieving 100% conversion and 84.7% yield under 1 MPa, 140 • C, and 6 h reaction conditions. Both examples show that heterojunctions improve the performance of commonly used catalyzers such as TiO 2 , lowering the reaction conditions and reducing energy costs if they are going to be applied at the industrial scale [122].

Photocatalysts Modified by Macromolecules
It is possible to modify photocatalysts, adding macromolecules on the surface, e.g., cyclodextrins (C.D.s), which are biodegradable cyclic hydrocarbons [123]. β-Cyclodextrin (β-CD) is essential in photogenerated charge transfer, as it can serve as a hole eliminator to suppress recombination of photogenerated (h + -e − ) pairs. It has also been shown that its presence contributes to a more selective reaction because it prevents the formation of the • OH radical, which is highly reactive but not selective, so its presence contributes to complete degradation reactions, obtaining as final products CO2 and H2O [95,124].
Cyclodextrins (C.D.s) commonly contain 6, 7, or 8 units of α-D-glucose and are called α, β, and γ-cyclodextrins, respectively [123,125]. C.D.s have a well-defined conical structure, Figure 12, with the broad rim surrounded by the secondary −OH groups and the narrow rim surrounded by the primary −OH groups [123,125]. The cyclodextrin has two faces: a hydrophobic inner and a hydrophilic outer; these characteristics allow C.D.s to form macromolecular complexes with a wide variety of organic and inorganic compounds that result in changes in the essential features of the compounds associated with them [63,126].

Photocatalysts Modified by Macromolecules
It is possible to modify photocatalysts, adding macromolecules on the surface, e.g., cyclodextrins (C.D.s), which are biodegradable cyclic hydrocarbons [123]. β-Cyclodextrin (β-CD) is essential in photogenerated charge transfer, as it can serve as a hole eliminator to suppress recombination of photogenerated (h + -e − ) pairs. It has also been shown that its presence contributes to a more selective reaction because it prevents the formation of the •OH radical, which is highly reactive but not selective, so its presence contributes to complete degradation reactions, obtaining as final products CO 2 and H 2 O [95,124].
Cyclodextrins (C.D.s) commonly contain 6, 7, or 8 units of α-D-glucose and are called α, β, and γ-cyclodextrins, respectively [123,125]. C.D.s have a well-defined conical structure, Figure 12, with the broad rim surrounded by the secondary −OH groups and the narrow rim surrounded by the primary −OH groups [123,125]. The cyclodextrin has two faces: a hydrophobic inner and a hydrophilic outer; these characteristics allow C.D.s to form macromolecular complexes with a wide variety of organic and inorganic compounds that result in changes in the essential features of the compounds associated with them [63,126]. Chen et al. [128] evaluated the degradation of naphthalene under visible light; they concluded that Ag-NPs added to the photocatalyst improved the absorbance in the visible region. On the other hand, the photocatalyst activity that contains β-CD traps the naphthalene inside it because its cavity is hydrophobic. Thus, the naphthalene molecules remain in contact with the surface photocatalyst for a longer time, which favors a more efficient reaction. Finally, experiments under visible light, with the photocatalyst containing Ag-NPs and β-CD, presented the highest photocatalytic activity, reaching a degradation of 98.4% of naphthalene in 150 min, as shown in Figure 13. This work demonstrates the possibility of modifying photocatalysts to make them efficient and work with visible light, which can be used since it is known that the combination between metals and β-CD provides new and better properties to the photocatalyst [128]. Therefore, it could be taken to an industrial application since only sunlight is required to activate the photocatalysts.  Chen et al. [128] evaluated the degradation of naphthalene under visible light; they concluded that Ag-NPs added to the photocatalyst improved the absorbance in the visible region. On the other hand, the photocatalyst activity that contains β-CD traps the naphthalene inside it because its cavity is hydrophobic. Thus, the naphthalene molecules remain in contact with the surface photocatalyst for a longer time, which favors a more efficient reaction. Finally, experiments under visible light, with the photocatalyst containing Ag-NPs and β-CD, presented the highest photocatalytic activity, reaching a degradation of 98.4% of naphthalene in 150 min, as shown in Figure 13. This work demonstrates the possibility of modifying photocatalysts to make them efficient and work with visible light, which can be used since it is known that the combination between metals and β-CD provides new and better properties to the photocatalyst [128]. Therefore, it could be taken to an industrial application since only sunlight is required to activate the photocatalysts. Chen et al. [128] evaluated the degradation of naphthalene under visible light; they concluded that Ag-NPs added to the photocatalyst improved the absorbance in the visible region. On the other hand, the photocatalyst activity that contains β-CD traps the naphthalene inside it because its cavity is hydrophobic. Thus, the naphthalene molecules remain in contact with the surface photocatalyst for a longer time, which favors a more efficient reaction. Finally, experiments under visible light, with the photocatalyst containing Ag-NPs and β-CD, presented the highest photocatalytic activity, reaching a degradation of 98.4% of naphthalene in 150 min, as shown in Figure 13. This work demonstrates the possibility of modifying photocatalysts to make them efficient and work with visible light, which can be used since it is known that the combination between metals and β-CD provides new and better properties to the photocatalyst [128]. Therefore, it could be taken to an industrial application since only sunlight is required to activate the photocatalysts.

Cellulose Conversion
Cellulose is a D-glucose linear polymer linked by b-1,4 glycosidic bonds; it is the most abundant biomass component in nature [2,86,129]. In addition to understanding the biomass photodegradation pathway, it is essential to design and manufacture suitable photocatalysts with excellent properties such as easy mass diffusion, light-harvesting, and improved separation of photogenerated pairs to obtain high conversion percentages and selectivity [6,59,71,92,129]. In selective photooxidation processes of compounds derived from cellulose, high-value chemical products have been obtained among the so-called platform molecules that include a wide variety of carboxylic acids such as succinic, fumaric, and malic acids, 2,5-furandicarboxylicc, 3-hydroxy propionic, aspartic, glucaric, glutamic, itaconic, and levulinic acids, and other basic molecules (3-hydroxybutyrolactone, glycerol, sorbitol and xylitol/arabitol) [6,22,86,130].
Colmenares and Magdziarz [42] studied the photocatalytic oxidation of glucose, where three organic compounds were obtained as a result: glucaric acid (GUA), gluconic acid (G.A.), and arabitol (AOH). These carboxylic acids are fundamental building blocks in manufacturing pharmaceuticals, foods, perfumes, and fuels [9,131]. Figure 14 summarizes the results obtained for glucose conversion and selectivity for GUA and G.A. using different photocatalysts immersed in three water-acetonitrile mixes (10% H 2 O/90% ACN, 50% H 2 O/50% ACN, 100% H 2 O). As can be observed, working with TiO 2 (U.S.) results in higher selectivity (total selectivity for GUA + GA is 71.3%) with 11.0% glucose conversion. In this work for all TiO 2 photocatalysts, the selectivity depends on the acetonitrile content in the mixture, although the relationship is not proportional; for example, using 50% ACN selectivity is better than 90% ACN mixtures.

Cellulose Conversion
Cellulose is a D-glucose linear polymer linked by b-1,4 glycosidic bonds; it is the most abundant biomass component in nature [2,86,129]. In addition to understanding the biomass photodegradation pathway, it is essential to design and manufacture suitable photocatalysts with excellent properties such as easy mass diffusion, light-harvesting, and improved separation of photogenerated pairs to obtain high conversion percentages and selectivity [6,59,71,92,129]. In selective photooxidation processes of compounds derived from cellulose, high-value chemical products have been obtained among the so-called platform molecules that include a wide variety of carboxylic acids such as succinic, fumaric, and malic acids, 2,5-furandicarboxylicc, 3-hydroxy propionic, aspartic, glucaric, glutamic, itaconic, and levulinic acids, and other basic molecules (3-hydroxybutyrolactone, glycerol, sorbitol and xylitol/arabitol) [6,22,86,130].
Colmenares and Magdziarz [42] studied the photocatalytic oxidation of glucose, where three organic compounds were obtained as a result: glucaric acid (GUA), gluconic acid (G.A.), and arabitol (AOH). These carboxylic acids are fundamental building blocks in manufacturing pharmaceuticals, foods, perfumes, and fuels [9,131]. Figure 14 summarizes the results obtained for glucose conversion and selectivity for GUA and G.A. using different photocatalysts immersed in three water-acetonitrile mixes (10% H2O/90% ACN, 50% H2O/50% ACN, 100% H2O). As can be observed, working with TiO2 (U.S.) results in higher selectivity (total selectivity for GUA + GA is 71.3%) with 11.0% glucose conversion. In this work for all TiO2 photocatalysts, the selectivity depends on the acetonitrile content in the mixture, although the relationship is not proportional; for example, using 50% ACN selectivity is better than 90% ACN mixtures. Another example of conversion of cellulose derivatives is reported by Jin et al. [132], where formic acid is obtained as a product of glucose conversion. This process is mainly attributed to the acceleration in the development of active oxidative radicals (O2 •− , • OH) in the presence of hydroxyl ions. Furthermore, hydroxyl ions regulate the charge of the Another example of conversion of cellulose derivatives is reported by Jin et al. [132], where formic acid is obtained as a product of glucose conversion. This process is mainly attributed to the acceleration in the development of active oxidative radicals (O 2 •− , •OH) in the presence of hydroxyl ions. Furthermore, hydroxyl ions regulate the charge of the TiO 2 surface and glucose adsorption and formic acid desorption, resulting in conversion of 79.6% and selectivity of 14.2%.
Payormhorm et al. [9], proposed a mechanism of conversion of glucose to gluconic acid, arabinose, xylitol, and formic acid, as shown in Figure 15. Three significant reactions are required to convert glucose into these compounds. First, a nucleophilic attraction of H 2 O molecules initiates these •OH radicals on the TiO 2 surface at O lattice sites (Ti-O•). When these H 2 O molecules come into contact with holes in the valence band of TiO 2 , they are oxidized to •OH. These •OH radicals oxidize glucose into gluconic acid. By photocatalytic decarboxylation, the gluconic acid transforms into arabinose and formic acid. Another possible reaction pathway is the photocatalytic decomposition of glucose to produce xylitol. The efficiency of the photodegradation process depends on the amount of energy that is radiated in the process; one exciting route is the conversion of glucose to gluconic acid and xylitol because, in this process, the energy consumption was reduced, and it was carried out under mild conditions compared to thermochemical catalysts and biological processes [9,133].
TiO2 surface and glucose adsorption and formic acid desorption, resulting in conversion of 79.6% and selectivity of 14.2%.
Payormhorm et al. [9], proposed a mechanism of conversion of glucose to gluconic acid, arabinose, xylitol, and formic acid, as shown in Figure 15. Three significant reactions are required to convert glucose into these compounds. First, a nucleophilic attraction of H2O molecules initiates these •OH radicals on the TiO2 surface at O lattice sites (Ti-O•). When these H2O molecules come into contact with holes in the valence band of TiO2, they are oxidized to •OH. These •OH radicals oxidize glucose into gluconic acid. By photocatalytic decarboxylation, the gluconic acid transforms into arabinose and formic acid. Another possible reaction pathway is the photocatalytic decomposition of glucose to produce xylitol. The efficiency of the photodegradation process depends on the amount of energy that is radiated in the process; one exciting route is the conversion of glucose to gluconic acid and xylitol because, in this process, the energy consumption was reduced, and it was carried out under mild conditions compared to thermochemical catalysts and biological processes [9,133]. These findings pave the way for developing a novel strategy process and the economically viable usage of sustainable biomass and clean solar energy to manufacture formic acid. It is interesting that sugars such as glucose, fructose, xylose, mannose, and arabinose can be extracted from biomass, but chemical processes combined with photooxidation are still needed to achieve good recoveries and high selectivity [134]. Figure 16 depicts the results obtained in the work of Bellardita et al. [22,135], where TiO2 was used as a photocatalyst in its three phases, anatase, rutile, and brookite. Each was modified with metallic doping of Pt and compared under ultraviolet light for a selective glucose conversion reaction to produce arabinose, erythrose, fructose, gluconic acid, glucaric acid, formic-acid, H2, and CO2. This study revealed that the distribution depends on the structural and physicochemical characteristics of the photocatalyst. Therefore, it is possible to obtain the desired product by controlling the process. For example, to obtain gluconic acid, it is observed that the only photocatalyst that provides this product is Pt-anatase. Similarly, Pt-rutile helps produce in large proportion formic acid as a final product. These findings pave the way for developing a novel strategy process and the economically viable usage of sustainable biomass and clean solar energy to manufacture formic acid. It is interesting that sugars such as glucose, fructose, xylose, mannose, and arabinose can be extracted from biomass, but chemical processes combined with photooxidation are still needed to achieve good recoveries and high selectivity [134]. Figure 16 depicts the results obtained in the work of Bellardita et al. [22,135], where TiO 2 was used as a photocatalyst in its three phases, anatase, rutile, and brookite. Each was modified with metallic doping of Pt and compared under ultraviolet light for a selective glucose conversion reaction to produce arabinose, erythrose, fructose, gluconic acid, glucaric acid, formic-acid, H 2 , and CO 2 . This study revealed that the distribution depends on the structural and physicochemical characteristics of the photocatalyst. Therefore, it is possible to obtain the desired product by controlling the process. For example, to obtain gluconic acid, it is observed that the only photocatalyst that provides this product is Pt-anatase. Similarly, Pt-rutile helps produce in large proportion formic acid as a final product.  Table 3 indicates the main products reported in the literature, the operating conditions, and the photocatalyst for cellulose and glucose conversion. It is evident that the products obtained after the conversion depend on the photocatalyst and the type of light used during the process. Therefore, there a wide field of research is necessary to obtain specific compounds with high conversion percentages.   Table 3 indicates the main products reported in the literature, the operating conditions, and the photocatalyst for cellulose and glucose conversion. It is evident that the products obtained after the conversion depend on the photocatalyst and the type of light used during the process. Therefore, there a wide field of research is necessary to obtain specific compounds with high conversion percentages.

Lignin Conversion
The depolymerization of oxygen-enriched lignin is facilitated primarily by selective cleavage of C-O bonds, in aryl ethers by cleavage of C-O-C bonds, and further hydrogenol-ysis of phenolic dimers to deoxygenated biofuels [138]. However, lignin's complex and irregular structure often misleads the search for selective chemical conversion; other known depolymerization approaches often produce vague and indistinct products in less quantity [138,139]. In this sense, photocatalysis is a promising and advantageous approach to replace or unify different techniques to induce selective oxidation of lignocellulosic biomass. It is a low molecular mass feedstock source through pretreatment; it further processes lignin model compounds into other value-added fine chemicals [140].
The specific photocatalytic conversion of poorly structured lignin into valuable chemicals is directly related to its strong oxidizing power for selective chemical transformations [141]. It is currently known that different strategies have been studied to update and improve the effectiveness of the photocatalytic conversion of lignin, which include, among others, the design of heterostructures through a combination of semiconductors with other hybrid materials, e.g., heteroatom doping (or compound formation) and heterojunctions, by combining the semiconductors with secondary semiconductors, noble metals, and carbon-based materials [89,141].
The major products of lignin oxidative breakdown are aromatic aldehydes and carboxylic acids. In the oxidative deconstruction of lignin, vanillin is a standard product, with yields ranging from 5 to 15% w/w concerning the lignin source [40]. Vanillin is a valuable industrial chemical used as a flavoring agent in food, cosmetics, pharmaceutical, nutraceutical, and fine chemical industries [134,141].
After the lignin degradation process, it is possible to identify different molecules as the final product: acetic acid, malonic acid, succinic acid, butylated hydroxytoluene, vanillin, veratric acid, and palmitic acid [132,141]. Catechol, resorcinol, and hydroquinone are first produced during the photodegradation of phenolic compounds employing TiO 2 as a photocatalyst. The phenyl rings in these compounds are broken to yield malonic acid and short-chain organic acids, such as maleic, oxalic, acetic, and formic acids, until the sample is mineralized, at which point CO 2 is produced as the ultimate product of the degradation process [60,94]. Figure 17 shows the results obtained by Kamwilaisak et al. [140]; here, a graphic representation of the percentages of identified intermediate compounds of lignin is observed for each experiment. All treated lignin samples had a comparable amount of fatty acids, 15%, while in the standard lignin samples, the percentage was only 10%. Carbohydrate was detected in the highest concentration in the biocatalytic reaction sample (20%), whereas it was insignificant in the photocatalytic reaction. In mono-and two-step reaction samples, the carbohydrate content was 10% and 5%, respectively. The highest organic acid concentration was measured in the photoreaction process, reaching 20%. This effect could be attributed because the photoreaction can produce compounds such as short-chain organic acids before finally degrading or fully mineralizing to CO 2 [42,142]. Some of these synthesized acids are of commercial interest, e.g., succinic, acetic, and lactic acids. Table 4 shows that TiO 2 -and modified TiO 2 -are the main photocatalysts used to convert lignin into useful industrial products such as vanillin. It is necessary to choose the right type of lignin and the suitable TiO 2 -modified catalyst to obtain specific products. Data in Table 4 also indicate that more than 40.3% of biomass converts during the photooxidation process-avoiding polluting residues-and more research is necessary in cases where the conversion is low.  Table 4 shows that TiO2-and modified TiO2-are the main photocatalysts used to convert lignin into useful industrial products such as vanillin. It is necessary to choose the right type of lignin and the suitable TiO2-modified catalyst to obtain specific products. Data in Table 4 also indicate that more than 40.3% of biomass converts during the photooxidation process-avoiding polluting residues-and more research is necessary in cases where the conversion is low.

Perspectives and Conclusions
Through this bibliographic review, we seek to provide a direction that will facilitate the development of future works based on the heterogeneous photocatalysis process, since efficient methods are needed to convert waste biomass into chemical products with high added value. Although the results presented here are encouraging, it is necessary to evaluate the photooxidation process not only at a laboratory scale, but also at an industrial level.
For the process to be profitable at an industrial level, it must be carried out with sunlight, and it is necessary to repeat experiments at pilot scale and not only at the laboratory level. For this reason, the importance of working with photocatalysts that are capable of absorbing visible light is highlighted. As a result, it will be essential to conduct an economic study to evaluate whether the process is lucrative and if it necessary to modify the photocatalysts so that they can absorb visible light. In addition, it should be considered that most of the studies are carried out with derivatives of lignocellulosic biomass or bio-oil, so it is necessary to study the direct photocatalytic degradation of biomass.
The heterogeneous photocatalysis process is presented as a viable technique for converting renewable energies such as lignocellulosic biomass and solar energy into fuels and chemicals. In this review, several works of interest are summarized in terms of their achievements in percentages of photocatalytic conversion of lignocellulosic biomass and its derivatives. The importance of breaking the bonds was identified thanks to the oxidizing power of the photocatalysis process to obtain chemical products with high added value, taking into account that the process must be controlled to prevent biomass derivatives from fully mineralizing to CO 2 and H 2 O.
Titanium dioxide is the most useful catalyst employed to convert biomass into new valuable products; this study showed several experiences where its catalytic ability increased when TiO 2 was doped with a proper metal or macromolecule. In the case of g-C 3 N 4 , the dopage with noble metals helped increase the biomass's selective conversion. Furthermore, the modified catalyzers decreased the temperature, pressure, and time during reactions, reducing energy and cost. The obtained products depend highly on the catalyst used, while the reaction conditions affect the conversion and selectivity. The addition of β-cyclodextrin on the surface of photocatalysts contributes to complete degradation reactions, decreasing the conversion time. It is crucial to note that further investigation will permit the design of customized catalysts for specific purposes.
The review lets us realize that it is possible to design custom catalysts, from TiO 2 , and g-C 3 N 4 , to obtain specific products from biomass with the minimum time and energy consumption.
A problem that became apparent during the investigation is that at the end of the photocatalytic process, separating and purifying the products obtained from the reaction medium represent a significant challenge. The study of separation methods is required to obtain products with high added value.
For this technology to be implemented at an industrial level, it is imperative to plan public policies that integrate advances in academia with industry needs, and thus define a roadmap for obtaining greater participation of bioenergy and biofuels and reduce dependence on non-renewable sources.