The effect of surface functionalization of aminophenyl and bromophenyl groups on carbon-coated LiFePO4 and the electrochemical properties of composite electrode containing these materials are reported. The functionalization was performed by spontaneous reduction of the corresponding in situ generated diazonium ions. The resulting chemically grafted LiFePO4/C materials were characterized by energy-dispersive X-ray spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS) to confirm the presence of the surface organic species. XRD analyses indicated the cathode material was partially oxidized. Thermogravimetric and elemental analyses revealed the loading of grafted molecules was between 0.2 and 1.1 wt.% depending on the reaction conditions. Interestingly, the electrochemical performances of the modified LiFePO4/C are not adversely affected by the presence of either aminophenyl and bromophenyl groups at the carbon surface, and in fact the grafted LiFePO4/C displayed slightly superior discharge capacity at the highest C rate investigated for a low loading of organic molecules.