The spinel compound Li4/3+x Ti5/3O4 is known to undergo reversible lithium intercalation up to x=1 with almost no change in lattice parameters, hence its designation as a “zero strain” intercalation compound. Structural changes that accompany electrochemical Li intercalation into this compound were studied by both 7 Li nuclear magnetic resonance (NMR) and Ti K-edge X-ray absorption fine structure (XAFS). The NMR results demonstrate that Li occupancies do not follow a simple distribution between two possible sites, one tetrahedral and one octahedral. The presence of at least one additional octahedral site is suggested. Line width measurements show that the Li+ ions do not return to their original distribution after cycling. XAFS results indicate the presence of modest static disorder in TiO and TiTi distances above x=0.5. Both methods thus reveal subtle structural details previously unobserved by X-ray diffraction (XRD).