Hydrogen and oxygen evolution at the negative and positive electrodes in AGM batteries are the main reasons of self-discharging. The self-discharge of five AGM batteries was investigated by measuring different potential between two electrodes during 48 days. Five different battery electrolytes were used including 35% (w/w) H2SO4 without additives and the remaining contain 7.1, 9.94, and 21.3gl−1 sodium sulfate, 4gl−1 boric acid, 3gl−1 citric acid, and finally 0.7 and 1gl−1 stearic acid except one containing boric acid that the concentration of H2SO4 was 36% (w/w). The results revealed that the rate of self-discharge for battery without additive was 0.01Vday−1. The battery with boric acid showed the lowest rate of self-discharge with 0.0025Vday−1. It was also found that stearic and citric acids are comparatively appropriate additives for decreasing the self-discharge. They caused a decrease of the self-discharge rate to 0.005 and 0.0075Vday−1 on appropriate concentration, respectively. In compared to other additives, sodium sulfate showed to be not an appropriate additive for decreasing battery self-discharging. The rate of 0.03Vday−1 of self-discharging was obtained for the battery containing all selected concentration of sodium sulfate during first 4 days of measuring.