The Li-ion and electronic conductivities of a series of p-doped poly(thiophene)s with oligo-ethylene oxide side chains have been determined at room temperature as functions of side-chain length and concentration of LiOTf dissolved in the polymers in order to assess their utility as binders in Li-ion batteries. The lithium triflate concentration was varied from 0.23 to 2.26mmol LiOTf/g –C2H4O– (100 O:Li to 10 O:Li), and the concentration of dissociated Li+ was determined from the IR spectra of the polymer solutions. The greatest ionic conductivity, 2×10−4 Scm−1, was attained with intermediate concentrations of added salt that corresponded with the greatest degree of LiOTf dissociation. Li-ion mobilities of 5×10−7 cm2 (Vs)−1 were measured for poly(thiophene)s (PT) with short oligo(ethylene oxide) side-chains (E n), PE2T and PE3T, whereas the polymers with longer side chains, PE7T and PE15T, had Li-ion mobilities about an order of magnitude greater, 5×10−6 cm2 (Vs)−1. The electronic conductivity of the polymers heavily doped with NOBF4 was near 0.1Scm−1 for PE2T and PE3T, but was orders of magnitude smaller for the polymers with longer side-chains. Addition of LiOTf caused the electronic conductivity of PE2T and PE3T to drop to that of the longer chain polymers whose conductivities were insensitive to the LiOTf concentration.