To improve the initial coulombic efficiency and bulk density of ordered mesoporous carbons, active Fe2O3 nanoparticles were introduced into tubular mesopore channels of CMK-5 carbon, which possesses high specific surface area (>1700 m2·g−1) and large pore volume (>1.8 cm3·g−1). Fine Fe2O3 nanoparticles with sizes in the range of 5–7 nm were highly and homogenously encapsulated into CMK-5 matrix through ammonia-treatment and subsequent pyrolysis method. The Fe2O3 loading was carefully tailored and designed to warrant a high Fe2O3 content and adequate buffer space for improving the electrochemical performance. In particular, such Fe2O3 and mesoporous carbon composite with 47 wt% loading exhibits a considerably stable cycle performance (683 mAh·g−1 after 100 cycles, 99% capacity retention against that of the second cycle) as well as good rate capability. The fabrication strategy can effectively solve the drawback of single material, and achieve a high-performance lithium electrode material.