The effects of changing the dipping and curing times of tubular positive electrodes on the discharge capacity were investigated. The comparative study showed that longer dipping and curing times do not necessarily result in electrodes with better first capacity performance. Acid adsorption studies of tubular plates filled with lead oxide showed that about one-third of the acid, that would have been adsorbed after 15h, was already adsorbed after 5s of dipping. The optimum surface area and porosity of the cured active material was obtained after 15–60min of dipping. This is equivalent to the rest period used in the formation process where the plates are kept in the acid just before charging. Curing times should be kept around 24h in order to reduce the free lead in the oxide. The study showed that the pore size distribution of the formed active material influenced the high current discharge ability more than the available surface area of the positive electrode. However, the surface area and pore size distribution changed dramatically during capacity cycling and the continuous capacity performance of the tubular electrode was partially influenced by the initial characteristics of the cured active material.