Ionic conductivity, mechanical stability and electrochemical property were examined on the poly ethyleneoxide (PEO) based cross-linked gel polymer electrolyte. Bisphenol A ethoxylate diacrylates (BPAEDA) with different numbers of ethylene oxide units (n=4, 15) were used as cross-linkers. The curing kinetics of the cross-linker was examined by an FT-IR study with two types of initiators and at different curing temperatures. Higher conductivity was observed for the longer ethylene oxide unit. Conductivity of the polymer electrolyte prepared from BPAEDA (n=15) and liquid electrolyte (70wt.%) was 3.47×10−3 S/cm at 30°C. Improved tensile strength and elongation at break were realized from the polymer electrolyte using BPAEDA as a cross-linker. Electrolyte having higher cross-linking density showed higher tensile strength, but showed decreased flexibility. The stability of the polymer electrolyte against electrochemical oxidation could be extended to larger than 4.5V (versus Li/Li+). Lithium cycling efficiency of the polymer electrolyte was about 80%.