This paper explores the synergistic and catalytic properties of a newly developed lithium ion battery (LIB) composite cathode of LiMn2O4 modified with bimetallic (Au–Fe) nanoparticle. Spinel phase LiMn2O4 was doped with bimetallic nanoparticles, LiM x Mn2−x O4 (M=FeAu), with concomitant oxidation of the Mn3+ ions (responsible for LIB capacity loss) to Mn4+. This nano-composite architecture accommodates the structural transformation that occurs during Li+ ion charge and discharge. Ultra-low scan rate (0.01mVs−1) cyclic voltammetry of the pure LiMn2O4 cathode material in 1M LiPF6/electrolyte solution, showed two sets of redox peaks with a third observed at lower potentials for LiM x Mn2−x O4. The FeAu incorporation increased the reaction rate upon reduction of LiMn2O4 as indicated by the enhanced reduction peak seen by cyclic voltammetry. Nyquist plots of the electrochemical impedance spectroscopy (EIS) results showed LiFeAu x Mn2−x O4 having increased conductivity with lower resistance of charge. X-ray diffraction studies showed the LiM x Mn2−x O4 material retained well-developed octahedral structures bounded by (111) planes. The material crystallite size was ∼10nm with clear lattice fringes having a separation value of 0.48nm which concurrently improved the diffusion rate of Li+ . Solid-state NMR results showed the progressive increase in average nominal manganese oxidation state from +3.5 to +4 resulted in an increase in the super-transferred hyperfine field at the 7Li nucleus of the FeAu doped cathode material. The LiFeAu x Mn2−x O4 material also showed improved cycleability, especially at high C rate. This improvement was due to the enhanced physical stability of LiMn2O4 and its improved electrical conductivity ascribed to the incorporated FeAu nanoparticles.