Li1+x (Ni1/3Mn1/3Co1/3)1−x O2 layered materials were synthesized by the co-precipitation method with different Li/M molar ratios (M =Ni+Mn+Co). Elemental titration evaluated by inductively coupled plasma spectrometry (ICP), structural properties studied by X-ray diffraction (XRD), Rietveld analysis of XRD data, scanning electron microscopy (SEM) and magnetic measurements carried out by superconducting quantum interference devices (SQUID) showed the well-defined α-NaFeO2 structure with cationic distribution close to the nominal formula. The Li/Ni cation mixing on the 3b Wyckoff site of the interlayer space was consistent with the structural model [Li1−y Ni y ]3b [Li x+y Ni(1−x)/3−y Mn(1−x)/3Co(1−x)/3]3a O2 (x =0.02, 0.04) and was very small. Both Rietveld refinements and magnetic measurements revealed a concentration of Ni2+-3b ions lower than 2%; moreover, for the optimized sample synthesized at Li/M =1.10, only 1.43% of nickel ions were located into the Li sublattice. Electrochemical properties were investigated by galvanostatic charge–discharge cycling. Data obtained with Li1+x (Ni1/3Mn1/3Co1/3)1−x O2 reflected the high degree of sample optimization. An initial discharge capacity of 150mAhg−1 was delivered at 1C-rate in the cut-off voltage of 3.0–4.3V. More than 95% of its initial capacity was retained after 30 cycles at 1C-rate. Finally, it is demonstrated that a cation mixing below 2% is considered as the threshold for which the electrochemical performance does not change for Li1+x (Ni1/3Mn1/3Co1/3)1−x O2.