A cathode was prepared by sealing a carbon supported sulfur electrode inside a composite ion-selective net made of carbon, binder and lithiated ionomer to restrict shuttling of polysulfide anionic species. As a result, the soluble polysulfide anions become unable to escape from the composite ion-selective films due to the electrostatic repulsion between the immobilized single ion conducting ionomers and the polysulfides with no dead angles. Experimentally, lithiated 4,4′-difluoro bis(benzene sulfonyl)imide and PEG200 were copolymerized to form a polyether based single ion conducting polymer. The ionic conductivity of the blend film made of ionomer and poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) at a mass ratio of 1:1 is 0.57 mS cm−1 at room temperature. The battery capacity with the sealed sulfur electrode is 1412 mAh g−1 at 0.5 C, 1041 mAh g−1 at 1.0 C, 873 mAh g−1 at 2.0 C and 614 mAh g−1 at 5.0 C, significantly better than the results with lithiated Nafion especially at high C rates. In addition, a long cycling test at 2 C for 500 cycles gives rise to a stable capacity of 800 mAh g−1. The intrinsic electrostatic repulsion between polysulfide anions and the negatively charged electrolyte film, together with the overall sealed electrode configuration, is responsible for blocking the shuttling of polysulfides effectively.