A novel solvoplasma based technique was used to fabricate highly uniform SnO2 nanowires (NWs) for application as an anode in sodium-ion batteries (SIBs). This technique is scalable, rapid, and utilizes a rigorous cleaning process to produce very pure SnO2 NWs with enhanced porosity; which improves sodium-ion hosting and reaction kinetics. The batch of NWs obtained from the plasma process were named the “as-made” sample and after cleaning the “pure” sample. Structural characterization showed that the as-made sample has a K+ ion impurity which is absent in the pure samples. The pure samples have a higher maximum specific capacity, 400.71 mAhg−1, and Coulombic efficiency, 85%, compared to the as-made samples which have a maximum specific capacity of 174.69 mAhg−1 and Coulombic efficiency of 74% upon cycling. A study of the electrochemical impedance spectra showed that the as-made samples have a higher interfacial and diffusion resistance than the pure samples and resistances increased after 50 cycles of cell operation for both samples due to progressive electrode degradation. Specific energy vs specific power plots were employed to analyze the performance of the system with respect to the working conditions.