The solid electrolyte interface (SEI) formation on the surface of LiMn2O4 electrodes during room temperature charge–discharge cycling was studied using soft X-ray absorption spectroscopy at the Fluorine (F) K-edge. LiMn2O4 electrodes without any binder were prepared by electrostatic spray deposition to eliminate the signal originating from the PVDF binder in the F K-edge X-ray absorption spectra. The F K-edge absorption spectra show that the SEI layer forms at a very early stage of cycling. SEI growth takes place during discharge. In addition, LiF formation is accelerated if the discharge step follows a charge step. The F K-edge absorption spectra suggest that the major component of the SEI is LiF.