In this work, a novel Cu/RGO@Pb alloy was prepared successfully and tested in the simulated lead-acid battery environment. In preparing the novel alloy, Cu/RGO composite was firstly synthesized in order to increase the wettability of RGO to Pb, and then the composite was added to the molten lead to obtain the target alloy. Scanning electron microscope, energy dispersive spectrometer, X-ray diffraction as well as electrochemical measurements were employed to evaluate the performance of the obtained composite and alloy. Results show that the prepared Cu/RGO@Pb possessed higher oxygen evolution over-potential and lower hydrogen evolution over-potential than the contrast alloy, indicating this novel alloy was more suitable for using as positive grids in lead acid batteries. Moreover, the RGO additive could inhibit the formation of Pb(II) and Pb(IV) film on the surface of the alloy, which could enhance the deep-charge/discharge performance of the grids and improve the corrosion resistance.