in excess of about 1 to 1 5 weight percent of such baths would be used for the purposes of this invention a web consisting of two plys of paper each having a basis weight of 13 pounds per 3000 square feet and which contained sufficient wet strength resin epichlorohydrin polyamine condensate 5 to 8 pounds per ton of dry paper so that the wet tensile strength is about 18 percent of the dry tensile strength was impregnated with a treating bath of the composition shown below in table ii table ii______________________________________ wet percent weight solids grams ______________________________________water n a 2548 0ammonium bromide 100 460 9urea 100 259 3glycerine 96 121 0polyethylene emulsion 42 103 3triton x 100 nonionic surfactant 98 1 84glyoxal 40 4 58titanium dioxide 67 254 4diarylide yellow pigment 21 0 53phthalocyanine blue pigment 39 1 98ethylene vinyl acetate copolymer 52 1244 9mineral oil based defoamer 100 15 0sodium alkylnaphthalene sulfonate 25 varied______________________________________ to this aqueous mixture was added sufficient ammonium hydroxide to adjust the ph to the range of from 6 5 to 7 5 a total of 5 000 grams was prepared this master batch was divided into six 800 gram portions and various amounts of calsol 150 sodium alkylnaphthalene sulfonate about 25 solids were added to each of the six portions the amounts added and the proportions of active surfactant based upon weight of bath are shown in table iii below table iii______________________________________ total weight ofrun calsol 150 grams proportion ______________________________________a 0 0b 4 0 125c 8 0 25d 12 0 375e 16.