acids in an approximately 70 30 weight ratio which had been reacted with ma was added to the reaction vessel to form a homogeneous blend the resulting mixture was allowed to cool to room temperature the final acid value of the blend was 226 4 mg koh g a portion of the blend prepared in example 4 was added to a 5 liter reaction vessel the blend was heated to a temperature of 50 55 u00b0 c 120 130 u00b0 f over a 30 minute period a 240 gram charge of 50 wt naoh solution was charged to the reaction vessel over 10 minutes after which the blend temperature increased to about 90 u00b0 c 195 u00b0 f a 120 gram portion of water was then added saponification at this temperature continued with additions of 203 grams of 12 5 wt ca oh 2 solution to obtain a ph of 8 97 and an acid value of 13 2 mg koh g followed by 15 grams of 50 wt naoh solution to obtain a ph of 9 67 and an acid value of 5 1 mg koh g the saponified blend was then diluted with an equal weight of water and the resulting solution was spray dried.