or from 10 to 100 by weight as a preferred range in addition it did not matter if the blended fabric was made from blended yarns or if the fabric was made from a pure fiber warp or weft woven in combination with a pure rayon or lyocell warp or weft also within the designated fiber types rayon and rayon blends the degree of wear and fading was related to the way the fibers were spun into yarn the type of weave and the finishing of the fabrics staple fibers looser weaves jacquard weaves and minimal finishing resulted in more wear and fading than longer filament yarns tight weaves plain weaves and heavy finishing processes however all rayon and rayon blended fabrics showed wear and fading within the grade ranges specified in table 2 the surface dimension was strongly related to the batting fiber the cotton batting produced a rippled surface and the polyester batting a smoother puffed surface the type of batting did not effect the wear or fading of the surface fabrics since the rippled surface is often viewed as a vintage look this invention will improve and enhance that process in addition this invention will also provide a method for antiquing for those who want to retain the puffed sculptured look that can be caused by polyester batting stitched in whole cloth quilted fabric other cellulosic fibers in addition to rayon and lyocell may also work to achieve the desired extent of antiquing there are three different types of rayon for apparel and home textiles the most dominant form with the largest market share is called u201c regular rayon u201d or u201c viscose u201d it is the regular or viscose rayon.