nonwovens of examples 1 10 were prepared as described in general procedure i for each example 200 g of the polymeric solution 2 5 wt of r1130 was added with the reactants described below along with 0 1 g of orcabrite green bn 4009 pigment the wt designated below represents the wt of active reactant solid over the r1130 polymer the coated samples were dried at 150 u00b0 f 65 5 u00b0 c for 2 hrs then 250 u00b0 f 121 1 u00b0 c for 2 hrs and finally cured at 300 u00b0 f 148 8 u00b0 c for 10 minutes all samples had excellent dry wiping properties low drag and good feel table 1______________________________________ g h2o sample wet out abs g of g h2o h2oex description sec dry wipe abs ft sup 2 loss______________________________________1 uncoated 0 11 37 148 7 24 78 nonwoven substrate comparative2 r1130 0 8 90 158 6 18 553 r1130 0 5 0 8 37 159 7 17 2 wt nalco 8676 5 wt tyzor 1314 r1130 0 5 wt 0 7 46 145 7 21 2 nalco 8676 15 wt tyzor 1315 r1130 0 5 wt 0 8 42 150 3 15 95 nalco 8676 5 wt tyzor la6 r1130 0 5 wt 0 7 79 155 9 16 73 nalco 8676 15 wt tyzor la7 r1130 5 wt 0 8 26 145 5 15 71 tyzor 1318 r1130 15 wt 0 7 83 150 4 17 11 tyzor 1319 r1130 5 wt.