str1 layer 4 2nd red sensitized layer red sensitized silver iodobromide emulsion 4 8 mol iodide average grain diameter 0 6 u03bcm containing 0 85 g agno 3 0 7 g gelatine and 1 04 mmol of the cyan coupler contained in layer 3 green sensitized silver iodobromide emulsion 4 3 mol iodide average grain diameter 0 28 u03bcm containing 0 85 g agno 3 0 75 g gelatine and 0 43 mmol magenta coupler corresponding to the following formula str2 layer 7 2nd green sensitized layer green sensitized silver iodobromide emulsion 3 8 mol iodide average grain diameter 0 62 u03bcm containing 1 03 g agno 3 0 89 g gelatine and 0 91 mmol of the magenta coupler contained in layer 6 yellow colloidal silver sol containing 0 2 g ag and 0 9 g gelatine blue sensitized silver iodobromide emulsion 4 9 mol iodide average grain diameter 0 36 u03bcm containing 0 76 g agno 3 0 56 g gelatine and 0 53 mmol yellow coupler corresponding to the following formula str3 layer 11 2nd blue sensitized layer blue sensitized silver iodobromide emulsion 3 3 mol iodide average grain diameter 0 78 u03bcm containing 1 30 g agno 3 0 76 g gelatine and 1 62 mmol of the yellow coupler contained in layer 10 1 5 g of gelatine and 0 7 g of hardener corresponding to the following formula str4 the photographic recording material prepared as described above was cut into strips of 35 mm widths and as well made up into a sheet film excellent mechanical and photographic properties were obtained in every case summarizing the process according to the invention affords.