it will be noted that fig1 herein is similar in many important respects to the illustration in fig1 of the field references mentioned hereinabove except as regards matters that may be different from field 39 s process it would be superfluous to repeat herein what is similar and already described in the art all parts and percentages herein are by weight unless otherwise indicated a series of examples of intertwined yarn most having excellent cut resistance were prepared by the process of this invention five comparatives were prepared by a similar process without the wire by way of contrast and are included in the table for convenience along with the examples of the invention the equipment is illustrated in fig1 at least two continuous core elements in all examples and comparatives these were continuous multifilament yarns were fed from supply packages such as yarns 1 2 3 or 4 from supply packages 11 12 13 and 14 in fig1 past guide 8 to a pair of feed rolls 6 and 7 7 is a driven roll 6 is a nip roll operating at a speed of 365 yards per minute and then through separate openings 38 in a collector plate 39 and into a convergence tube 33 to form the desired yarn 40 at convergence point 41 for the examples of the invention at least one stainless steel wire is simultaneously fed to the collector plate and convergence tube in the same manner as the core elements each end of wire was processed together with one core element this is desirable so that the core element 34 carries 34 or supports the wire and avoids abrasion and breakage of the wire this is illustrated in fig1.