a coating surfactant sf1023 was added at a concentration of 0 003 wt of the total solution a second layer cgl was coated on the barrier layer at a dry coverage of 0 05 g ft 2 the cgl mixture comprised 50 of a 90 10 cocrystalline pigment mixture of titanyl pthalocyanine and tetrafluoro titanyl phthalocyanine prepared as described in molaire et al u s pat no 5 614 342 and 50 of a polyester ionomer binder poly 2 2 dimethyl 1 3 propylene co oxydiethylene 80 20 isophthalate co 5 sodiosulfoisophthalate 95 5 prepared as described in molaire et al u s pat no 5 733 695 the cgl mixture was prepared at 3 wt in a 65 35 wt wt mixture of dichloromethane and 1 1 2 trichloroethane as described in u s pat no 5 614 342 a leveling agent dc510 was added at a concentration of 0 019 wt a third layer ctl was coated onto the cgl at a dry coverage of 2 3 g ft 2 the ctl mixture comprised 30 wt makrolon 5705 polymer 20 lexan polymer 10 poly 4 4 u2032 norbornylidene bisphenol terephthalate co azelate 60 40 20 wt of 1 1 bis 4 di 4 tolylamino phenyl cyclohexane 20 wt tri 4 tolyl amine.