sub 2 ono wt wt wt ______________________________________1 90 10 02 85 0 153 85 5 10______________________________________ in examples 1 and 2 the sintered alumina substrate is used as the base of the substrate but another ceramic sintered material such as sic beo aln or mgal 2 o 4 may be used also the base may be a green sheet row sheet of ceramic or glass or mixture of them having the same composition as the dielectric paste further the dielectric paste is not limited to the mixture of alumina and borosilicate lead glass but may be other ceramics or glasses which can be sintered under the melting point of cu next a laminated ceramic capacitor having a structure as shown in fig4 was produced in fig4 reference numeral 1 designates dielectric layers 2 designates conductor layers and 3 designates external electrodes dielectric material used was a dielectric material y5u 153u made by tam ceramic co having a pb mg 1 3 nb 2 3 o 3 based lead perovskite structure the average particle size was about 1 5 u03bcm this dielectric material as an inorganic component butyral resin as an organic binder di n butyl phthalate as a plasticiser and toluene as a solvent were mixed in amounts as shown in table 3 to obtain a slurry the slurry is filmed on an organic film by the doctor blade method and dried to produce a green sheet which was about 30 u03bcm in thickness after being dried table 3______________________________________inorganic component 100 partsbutyral resin 25 partsdi n butyl phthalate 5 partstoluene 40 parts______________________________________ next an inorganic component which was a mixture of 85 wt of.