<p>This is an ugly question, and an ugly answer.</p>

<ol>
<li><p>Nail polish doesn't come with an ingredient list. Nor are there MSDS's available to refer to what solvents are in it. So it's "unknown 1"</p></li>
<li><p>Most every filament company will not give you a list of compounds for colorants or plasticizers used. MSDS is off the table. So, even though we do know what PLA and ABS is inherently, we have no clue about the other ingredients used to make your particular filament. This is "unknown 2".</p></li>
</ol>

<p>What both of these comes down to is a very nasty situation indeed. We know for a fact that ABS dissolves into acetone. PLA does not.... Except we have had reports of PLA that does. When we look further into those responses, and ask them to do a burn test, they smell popcorn and something acrid (ABS). </p>

<p>This guarantees unless we have virgin material and MSDS in hand, you only have a close guess at what material you have. And that's to say nothing about "nail polish", and its components.</p>

<p>There are also other solvents that will dissolve PLA. MakerBot back before they turned evil, noted a solution called Beta Solution (90% isopropyl alcohol, 9% KOH, 1% Al(OH)3  ). This stuff is noted for dissolving PLA and leaving ABS intact.</p>

<p>Long story short: "Could Nail Polish damage pure PLA?" We can't guarantee purity of PLA, we can't guarantee contents of nail polish's solvents. The only answer is to print a swatch and test yourself. Calibration cubes are quick and easy.</p>

CC BY-SA 3.0
2017-10-25T03:26:46.597Z
2017-10-25T03:26:46.597Z
joshConway
<p>Nail polish will not damage your PLA model.</p>

<p>1) Let's talk about "gel" nail polish. Gel polish self-levels, does not drip, is cheap, is much more health-friendly than many finishing methods, and only takes 30 seconds under a suitable strength UV/LED lamp to dry, providing a thick smooth coat (clear, color, glitter!, anything) that makes any layer lines disappear. </p>

<p>2) The FDA regulates nail polish in its "cosmetics" category, so, not only are the ingredients known, they have to be printed on the bottle.</p>

<p>3) Gel polish consists of various methacrylate monomers which undergo a radical (in the chemistry sense, although it is pretty darn cool too) polymerization process that is UV-activable. Filament is primarily polyactide, which is polymerized at room temperature. Polymerized polyactide reacts with methylacrylate at the ends of the long strands (not in the middle, which is what you would describe as "damage"). Methylacrylate actually makes the PLA ends less reactive (read: it makes it stronger). As an industrial material, this compound is known as "supertoughened" PLA.</p>

<p>Hope that clears things up a bit. As an aside, if you're not familiar with the different families of nail polishes, and you want to try this, you can tell if the polish you're looking at is "gel" because the bottle will be opaque (keeps UV out).</p>

CC BY-SA 4.0
2019-06-12T22:55:16.533Z
2019-06-12T22:55:16.533Z
moe
<p>I would not expect a problem.  The greatest problem I would expect would be if the PLA layers were not well bonded, and the coating material could work in between layers.  If so, over time the difference in water absorption or thermal expansion could further separate the layers.</p>

CC BY-SA 3.0
2017-10-07T19:56:35.887Z
2017-10-07T19:56:35.887Z
cmm
<p>Nail polish contains acetone.  It melts PLA, so yes you <em>could</em> damage it.  Google acetone vapor batch to read up on a safer way to do the job.</p>

CC BY-SA 3.0
2017-10-07T06:59:48.310Z
"Nail polish contains acetone." - doesn't this depend on the brand of nail polish? Acetone also doesn't "melt" PLA that readily, though it can soften it if you expose it long enough.
Tom van der Zanden
CC BY-SA 3.0
2017-10-07T15:49:20.083Z
Yep.  I am thinking nail polish remover.
EvilTeach
CC BY-SA 3.0
2017-10-07T19:54:41.770Z
Also, PLA is not very soluble in Acetone.  ABS, otoh, is quite soluable.  Finding a suitable solvent for PLA is challenging.
cmm
CC BY-SA 3.0
2017-10-07T21:49:59.830Z
Even nail polish remover is not necessarily acetone.
Tom van der Zanden
CC BY-SA 3.0
2017-10-07T02:30:03.780Z
2017-10-07T02:30:03.780Z
EvilTeach
<p>NO if you want to smooth your print, gently heat the plastic and with a utensil smooth out the plastic. A hair dryer is a good way of doing this but be careful to only lightly melt the outside of the model.</p>

CC BY-SA 3.0
2017-10-14T08:23:31.413Z
I'm not sure this fully answers the question. You're offering a good alternative suggestion to using nail polish, but it still doesn't tell us whether "nail polish will damage pure PLA". Does it?
Tom van der Zanden
CC BY-SA 3.0
2017-10-24T17:43:32.087Z
@TomvanderZanden - No. It'll discolor colored PLA, but it should have no effect on "natural" PLA.
William
CC BY-SA 4.0
2018-08-01T06:02:22.093Z
@William-Rem - You should add that as an answer (and maybe expand upon it a little - if possible)
Greenonline
CC BY-SA 3.0
2017-10-13T20:51:11.590Z
2017-10-23T05:37:23.473Z
2017-10-23T05:37:23.473Z
Mark Williamson
<p>I would like to use nail polish to paint and smooth a PLA model. Could nail polish damage a model made out of pure PLA?</p>

CC BY-SA 3.0
2017-10-06T15:54:38.787Z
Why not just print a test cube and see what happens?
Carl Witthoft
<pla><color><smoothing>
Could nail polish damage pure PLA?
Sparkler
# Could nail polish damage pure PLA?

(Asked by: username_0 on 2017-10-05)

I would like to use nail polish to paint and smooth a PLA model. Could nail polish damage a model made out of pure PLA?

**Tags:** pla, color, smoothing

> **Comments:**
> **username_1**: Why not just print a test cube and see what happens?  

---

## 5 answers

### Answer by username_7 on 2017-10-13. Score: 2 | Accepted answer

NO if you want to smooth your print, gently heat the plastic and with a utensil smooth out the plastic. A hair dryer is a good way of doing this but be careful to only lightly melt the outside of the model.

> **Comments:**
> **username_6**: I'm not sure this fully answers the question. You're offering a good alternative suggestion to using nail polish, but it still doesn't tell us whether "nail polish will damage pure PLA". Does it?  
> **username_8**: @username_6 - No. It'll discolor colored PLA, but it should have no effect on "natural" PLA.  
> **username_9**: @username_8-Rem - You should add that as an answer (and maybe expand upon it a little - if possible)  

---

### Answer by username_2 on 2017-10-25. Score: 9

This is an ugly question, and an ugly answer.

1. Nail polish doesn't come with an ingredient list. Nor are there MSDS's available to refer to what solvents are in it. So it's "unknown 1"
2. Most every filament company will not give you a list of compounds for colorants or plasticizers used. MSDS is off the table. So, even though we do know what PLA and ABS is inherently, we have no clue about the other ingredients used to make your particular filament. This is "unknown 2".

What both of these comes down to is a very nasty situation indeed. We know for a fact that ABS dissolves into acetone. PLA does not.... Except we have had reports of PLA that does. When we look further into those responses, and ask them to do a burn test, they smell popcorn and something acrid (ABS).

This guarantees unless we have virgin material and MSDS in hand, you only have a close guess at what material you have. And that's to say nothing about "nail polish", and its components.

There are also other solvents that will dissolve PLA. MakerBot back before they turned evil, noted a solution called Beta Solution (90% isopropyl alcohol, 9% KOH, 1% Al(OH)3 ). This stuff is noted for dissolving PLA and leaving ABS intact.

Long story short: "Could Nail Polish damage pure PLA?" We can't guarantee purity of PLA, we can't guarantee contents of nail polish's solvents. The only answer is to print a swatch and test yourself. Calibration cubes are quick and easy.


---

### Answer by username_3 on 2019-06-12. Score: 4

Nail polish will not damage your PLA model.

1) Let's talk about "gel" nail polish. Gel polish self-levels, does not drip, is cheap, is much more health-friendly than many finishing methods, and only takes 30 seconds under a suitable strength UV/LED lamp to dry, providing a thick smooth coat (clear, color, glitter!, anything) that makes any layer lines disappear.

2) The FDA regulates nail polish in its "cosmetics" category, so, not only are the ingredients known, they have to be printed on the bottle.

3) Gel polish consists of various methacrylate monomers which undergo a radical (in the chemistry sense, although it is pretty darn cool too) polymerization process that is UV-activable. Filament is primarily polyactide, which is polymerized at room temperature. Polymerized polyactide reacts with methylacrylate at the ends of the long strands (not in the middle, which is what you would describe as "damage"). Methylacrylate actually makes the PLA ends less reactive (read: it makes it stronger). As an industrial material, this compound is known as "supertoughened" PLA.

Hope that clears things up a bit. As an aside, if you're not familiar with the different families of nail polishes, and you want to try this, you can tell if the polish you're looking at is "gel" because the bottle will be opaque (keeps UV out).


---

### Answer by username_4 on 2017-10-07. Score: 2

I would not expect a problem. The greatest problem I would expect would be if the PLA layers were not well bonded, and the coating material could work in between layers. If so, over time the difference in water absorption or thermal expansion could further separate the layers.


---

### Answer by username_5 on 2017-10-07. Score: 0

Nail polish contains acetone. It melts PLA, so yes you *could* damage it. Google acetone vapor batch to read up on a safer way to do the job.

> **Comments:**
> **username_6**: "Nail polish contains acetone." - doesn't this depend on the brand of nail polish? Acetone also doesn't "melt" PLA that readily, though it can soften it if you expose it long enough.  
> **username_5**: Yep.  I am thinking nail polish remover.  
> **username_4**: Also, PLA is not very soluble in Acetone.  ABS, otoh, is quite soluable.  Finding a suitable solvent for PLA is challenging.  
> **username_6**: Even nail polish remover is not necessarily acetone.  

---