<p>PLA would be a non-starter for outdoor use as it's biodegradable and can breakdown in sunlight. Albeit slowly, but won't be useful for long term project. </p>

<p>ABS would be a good choice for longevity, as it can last in outdoor situations for quite a while. Its glass transition temperature is above 100 degrees celsius so it'll last in most climates. As for strength ABS is one of the better choices out there, also it's slightly softer than PLA meaning it will flex before breaking, PLA is much more likely to shatter. ABS is well known for warping while printing though. Not a huge problem though, if you're used to printing with it. </p>

<p>PETG not a bad choice either. It has a glass transition temperature around 80-90°C. So if you're building in a hot place with direct sunlight with some reflection, you could have deformation issues, though not that likely. It is stronger than ABS and it's also easier to print (less warping issues). PETG is also supposedly 'food safe' meaning if the outdoor animals start pecking at it, it'll probably not kill them... I wouldn't recommend trying to taste it though. Finally PETG is a bit closer to PLA in terms of brittleness so it may shatter before flexing. ABS is less brittle than PETG.</p>

<p>If it were me I'd go with ABS despite its issues with warping while printing. If you're newer to printing, then probably better to go with PETG.</p>

CC BY-SA 3.0
2017-05-02T16:16:27.550Z
I do not think PLA is more susceptible to breaking down from sunlight than any other plastic. Biodegradation of PLA will not take place if it's only sitting outside - you need a carefully controlled commercial composting facility to get it to do anything.
Tom van der Zanden
CC BY-SA 3.0
2017-05-02T16:44:22.967Z
According to this article: http://www.emerginginvestigators.org/2013/11/the-effect-of-uv-treatment-on-the-degradation-of-compostable-polylactic-acid/     Degradation of PLA is  significantly increased with exposure to UV light.
Diesel
CC BY-SA 3.0
2017-05-02T19:02:05.030Z
They were specifically trying to get PLA to degrade. According to that article "The specific type of light used in this experiment is UVC [...] UVC light is not commonly found in sunlight because the ozone layer of the atmosphere absorbs most UVC light.".
Tom van der Zanden
CC BY-SA 4.0
2018-07-15T08:56:41.973Z
Another benefit of ABS: if you vaporsmooth the surface. This does prevent moisture from creeping in through the layer boundries.
Trish
CC BY-SA 4.0
2018-09-14T13:28:33.707Z
Prints over time do handle well: https://www.youtube.com/watch?v=qqNfa_zExRU
Trish
CC BY-SA 3.0
2017-04-13T22:22:48.977Z
2017-05-02T22:47:01.283Z
2017-05-02T22:47:01.283Z
Diesel
<p>I might be late to the party, but I have a suggestion. Why not use ASA filament, it's the kind of plastic used in car cup holders, lawn rakes and sprinkler heads, it is both heat and cold resistant, as well as solar stable and weatherproof. As far as printing with it it is similar to printing in ABS as far as I am aware, I might be wrong though. I personally am surprised how often this kind of question pops up and literally No One mentions ASA filament. I think I might buy some because I like the idea of printing something that can be left outside.</p>

CC BY-SA 4.0
2020-01-28T17:37:42.993Z
I wouldn't be so quick to dismiss this suggestion. I didn't know about ASA, yet I have an enclosed, air filtered printer with a 300ºC+ extruder w/ heated bed. Looking it up, dozens of choices available next day on Amazon Prime for me - I live in Scotland.
Rab
CC BY-SA 4.0
2019-04-05T04:57:35.570Z
ASA needs a print temperature of 250+ °C, which most printers with lined hotends can't reach without destroying the liner. Some ASA filament (3DXMax) even wants 270-290 °C. Heated bed is mandatory and ask for 80 to 110 °C. It *also* is best printed in an enclosure, which all are facts that make it a nieche product. It's fumes from the printing from printing also are likely to be toxic (research pending), and is one of those notorious hard to print filaments as it has severe layer adhesion problems and answers to those with splitting.
Trish
CC BY-SA 4.0
2019-04-08T13:08:33.137Z
In addition to what @Trish said, ASA is also relatively hard to get (unless you live in amazon-prime-free-shipping-land, sometimes referred to as the USA), I don't know of any filament supplier in my entire country that sells ASA
Nir
CC BY-SA 4.0
2020-06-03T17:22:01.607Z
I've been using ASA and I'm pretty happy with it. Agreed that you need some high temps, I think I have to print at 270 which is the absolute tops of what my printer does, and bed, and enclosed, and mind the fumes, but if you happen to have that tech, it's easier to print than either PETG or ABS. Few colors. Supply in the USA is easy, multiple vendors, don't need amazon to get it.
Brian Bulkowski
CC BY-SA 4.0
2019-04-05T03:32:17.337Z
2019-04-05T03:32:17.337Z
James Hanvey
<p>We use PLA in an outdoor environment, non-direct sunlight.  PLA seems to be just as strong as day one. It has been about six months now. </p>

<p>Of course, you must seal coat to protect from moisture.</p>

CC BY-SA 4.0
2018-07-18T06:13:19.777Z
I have some PLA parts outside since about 18 months now with no protection whatsoever. Except for some discoloration the parts are as strong as the first day. Of course the climate of your region plays a role in this too. I'm in Belgium, not in Arizona!
ON5MF Jurgen
CC BY-SA 4.0
2018-07-23T01:55:21.013Z
I'm in California, 30 degrees Fahrenheit up to 110.
Rob
CC BY-SA 4.0
2018-09-14T13:29:42.253Z
Good watch in this regard: https://www.youtube.com/watch?v=qqNfa_zExRU
Trish
CC BY-SA 4.0
2018-07-14T21:04:23.613Z
2018-07-14T23:57:17.087Z
2018-07-14T23:57:17.087Z
Rob
<p>What colour was your PLA? PLA will soften around 60C and a dark colour will easily get hotter than that in direct sun on a 30C day.  Clear PLA seems to have much, much better temperature resistance, but any sort of PETG will kick it's butt in that regard.</p>

CC BY-SA 4.0
2024-06-08T09:35:30.663Z
Sorry for resurrecting.
Colors definitely affect performance in my experience. I have several printed pieces of white PLA that are outside 24/7 for several years now in the Spanish sun (Alicante, easily one of the sunnier places in Spain) without any problems whatsoever. But I printed some black trains and train tracks for my nephew using PLA and they'd go soft simply lying in the sun on the floor inside (in summer, 36-38C).
Quintesse
CC BY-SA 4.0
2019-03-25T15:16:25.100Z
2019-03-25T15:16:25.100Z
Tim
<p>Ok, I tried all 3 materials.</p>

<p>PLA failed after less then one day, I believe it deformed from the constant pressure and fell out (I didn't find the part but I didn't really search for it, there's some tall grass below the window)</p>

<p>ABS lasted about a year, it fell strait down and I found the part, it looks ok if probably deformed by just a few mm so it doesn't pressure fit anymore.</p>

<p>PETG still going strong as I write this</p>

CC BY-SA 4.0
2018-07-14T22:34:30.293Z
PLA is not ice to desappear in one day, I have parts printed two years ago an still is working in good shape. Also "nice" testing if you loose one testing part and don't try to find it, what kind of proof is that?
Fernando Baltazar
CC BY-SA 4.0
2018-07-18T05:18:16.887Z
@FernandoBaltazar - those parts are pressure-fit on the outside of a ledge on the 3rd floor and hold a tight pigeon net, the most likely failure mode is that the part deforms just enough to not hold the ledge any more and is then shot into the street below by the tension of the net. it makes sense PLA does not work for this specific case because it involves constant pressure and PLA is known for deforming under pressure, the direct sun and heat probably doesn't help - this isn't proof that PLA isn't good for outdoor use but it does show PLA doesn't work for my specific use
Nir
CC BY-SA 4.0
2018-07-18T16:54:26.280Z
Well, all depends on kind of testing and robustness of the parts involved. I have parts as supports for antenna for repetiers directly to sun exposed with no shadow during the whole day. Of course some parts need to be for stronger material like ABS and some polycarbonates, but as a hobbie we will use the material available on the market.
Fernando Baltazar
CC BY-SA 4.0
2018-12-12T18:07:39.703Z
Very interesting that PETG outperformed ABS, as ABS has a higher Tg temperature. I'm curious what filament colors you used? That might have made a difference.
timetofly
CC BY-SA 4.0
2018-12-13T06:41:42.130Z
@Blossoming_Flower - Both ABS and PETG are completely solid at any outdoor temperature anywhere on earth, so the Tg temperature is kind of irrelevant here. I used cheap Chinese "natural" PETG (also, natural ABS from the same supplier)
Nir
CC BY-SA 4.0
2018-12-13T19:54:40.960Z
@Nir then any clue why the ABS deformed and the PETG didn't?
timetofly
CC BY-SA 4.0
2018-12-13T22:10:42.143Z
@Blossoming_Flower - I don't know, all I know it was pressure-fit into place outside and it fell down after about a year, it didn't break and without measuring it looked like it kept it's shape, I assume it deformed because otherwise it didn't have a reason for falling, it could be any combination of UV from the sun, water from rain, temperature changes, wind, or anything else, for all I know a bird might have pulled it our intentionally. I'm not a material scientist, chemist, or anyone who has any business talking about this but if I had to guess I would go with UV as the dominant factor
Nir
CC BY-SA 4.0
2020-12-27T13:00:10.740Z
(Late to the party) With luck, you will have figured out by now that it really doesn't matter much which filament chemistry you use, as long as you PAINT IT. Paint blocks the UV and prevents moisture intrusion, stabilizing the object. Recommendation: prime with shellac, then paint with "aluminum" colored paint.
TDHofstetter
CC BY-SA 4.0
2021-07-12T01:23:49.153Z
I can confirm this, i printed a 3D dragon with separated fit parts, they fit perfectly yesterday. I've sprayed prime into the pieces and let they cure through the day and now i cant connect any of the parts ahahah
Gonna need to sand all the pieces a lot because of one day into the sun.
Wallysson Nunes
CC BY-SA 4.0
2017-12-21T15:48:20.280Z
2018-07-18T05:22:38.230Z
2018-07-18T05:22:38.230Z
Nir
<p>The backstory: I'm installing a pigeon net in my home. Because of the shape of the opening I'm installing the net in and the material on the sides it's difficult to anchor the net using the normal means but I can print clips that will hold the net in place.</p>

<p>The clips will be outside and will be exposed to the weather and direct sunlight, the weather here is relatively hot (up to 30C) with a lot of sun most of the year and rain in the winter.</p>

<p>I only have PLA, ABS and PETG available, anything else will take too long to arrive.</p>

<p>I don't care about the parts changing color and mostly I don't care about them deforming a little bit - only about breaking.</p>

<p>If the parts have to be replaced after a year I'm ok with it, less then that will be annoying, longer will be better.</p>

<p>So, under those conditions, which of the 3 materials is more durable?</p>

<print-material><material><outdoors>
Which is more durable to sunlight/weather - PLA, ABS or PETG
Nir
# Which is more durable to sunlight/weather - PLA, ABS or PETG

(Asked by: username_0 on 2017-04-13)

The backstory: I'm installing a pigeon net in my home. Because of the shape of the opening I'm installing the net in and the material on the sides it's difficult to anchor the net using the normal means but I can print clips that will hold the net in place.

The clips will be outside and will be exposed to the weather and direct sunlight, the weather here is relatively hot (up to 30C) with a lot of sun most of the year and rain in the winter.

I only have PLA, ABS and PETG available, anything else will take too long to arrive.

I don't care about the parts changing color and mostly I don't care about them deforming a little bit - only about breaking.

If the parts have to be replaced after a year I'm ok with it, less then that will be annoying, longer will be better.

So, under those conditions, which of the 3 materials is more durable?

**Tags:** print-material, material, outdoors


---

## 5 answers

### Answer by username_0 on 2017-12-21. Score: 24 | Accepted answer

Ok, I tried all 3 materials.

PLA failed after less then one day, I believe it deformed from the constant pressure and fell out (I didn't find the part but I didn't really search for it, there's some tall grass below the window)

ABS lasted about a year, it fell strait down and I found the part, it looks ok if probably deformed by just a few mm so it doesn't pressure fit anymore.

PETG still going strong as I write this

> **Comments:**
> **username_11**: PLA is not ice to desappear in one day, I have parts printed two years ago an still is working in good shape. Also "nice" testing if you loose one testing part and don't try to find it, what kind of proof is that?  
> **username_0**: @username_11 - those parts are pressure-fit on the outside of a ledge on the 3rd floor and hold a tight pigeon net, the most likely failure mode is that the part deforms just enough to not hold the ledge any more and is then shot into the street below by the tension of the net. it makes sense PLA does not work for this specific case because it involves constant pressure and PLA is known for deforming under pressure, the direct sun and heat probably doesn't help - this isn't proof that PLA isn't good for outdoor use but it does show PLA doesn't work for my specific use  
> **username_11**: Well, all depends on kind of testing and robustness of the parts involved. I have parts as supports for antenna for repetiers directly to sun exposed with no shadow during the whole day. Of course some parts need to be for stronger material like ABS and some polycarbonates, but as a hobbie we will use the material available on the market.  
> **username_12**: Very interesting that PETG outperformed ABS, as ABS has a higher Tg temperature. I'm curious what filament colors you used? That might have made a difference.  
> **username_0**: @Blossoming_Flower - Both ABS and PETG are completely solid at any outdoor temperature anywhere on earth, so the Tg temperature is kind of irrelevant here. I used cheap Chinese "natural" PETG (also, natural ABS from the same supplier)  
> **username_12**: @username_0 then any clue why the ABS deformed and the PETG didn't?  
> **username_0**: @Blossoming_Flower - I don't know, all I know it was pressure-fit into place outside and it fell down after about a year, it didn't break and without measuring it looked like it kept it's shape, I assume it deformed because otherwise it didn't have a reason for falling, it could be any combination of UV from the sun, water from rain, temperature changes, wind, or anything else, for all I know a bird might have pulled it our intentionally. I'm not a material scientist, chemist, or anyone who has any business talking about this but if I had to guess I would go with UV as the dominant factor  
> **username_13**: (Late to the party) With luck, you will have figured out by now that it really doesn't matter much which filament chemistry you use, as long as you PAINT IT. Paint blocks the UV and prevents moisture intrusion, stabilizing the object. Recommendation: prime with shellac, then paint with "aluminum" colored paint.  
> **username_14**: I can confirm this, i printed a 3D dragon with separated fit parts, they fit perfectly yesterday. I've sprayed prime into the pieces and let they cure through the day and now i cant connect any of the parts ahahah Gonna need to sand all the pieces a lot because of one day into the sun.  

---

### Answer by username_1 on 2017-04-13. Score: 13

PLA would be a non-starter for outdoor use as it's biodegradable and can breakdown in sunlight. Albeit slowly, but won't be useful for long term project.

ABS would be a good choice for longevity, as it can last in outdoor situations for quite a while. Its glass transition temperature is above 100 degrees celsius so it'll last in most climates. As for strength ABS is one of the better choices out there, also it's slightly softer than PLA meaning it will flex before breaking, PLA is much more likely to shatter. ABS is well known for warping while printing though. Not a huge problem though, if you're used to printing with it.

PETG not a bad choice either. It has a glass transition temperature around 80-90°C. So if you're building in a hot place with direct sunlight with some reflection, you could have deformation issues, though not that likely. It is stronger than ABS and it's also easier to print (less warping issues). PETG is also supposedly 'food safe' meaning if the outdoor animals start pecking at it, it'll probably not kill them... I wouldn't recommend trying to taste it though. Finally PETG is a bit closer to PLA in terms of brittleness so it may shatter before flexing. ABS is less brittle than PETG.

If it were me I'd go with ABS despite its issues with warping while printing. If you're newer to printing, then probably better to go with PETG.

> **Comments:**
> **username_2**: I do not think PLA is more susceptible to breaking down from sunlight than any other plastic. Biodegradation of PLA will not take place if it's only sitting outside - you need a carefully controlled commercial composting facility to get it to do anything.  
> **username_1**: According to this article: http://www.emerginginvestigators.org/2013/11/the-effect-of-uv-treatment-on-the-degradation-of-compostable-polylactic-acid/     Degradation of PLA is  significantly increased with exposure to UV light.  
> **username_2**: They were specifically trying to get PLA to degrade. According to that article "The specific type of light used in this experiment is UVC [...] UVC light is not commonly found in sunlight because the ozone layer of the atmosphere absorbs most UVC light.".  
> **username_3**: Another benefit of ABS: if you vaporsmooth the surface. This does prevent moisture from creeping in through the layer boundries.  
> **username_3**: Prints over time do handle well: https://www.youtube.com/watch?v=qqNfa_zExRU  

---

### Answer by username_4 on 2019-04-05. Score: 9

I might be late to the party, but I have a suggestion. Why not use ASA filament, it's the kind of plastic used in car cup holders, lawn rakes and sprinkler heads, it is both heat and cold resistant, as well as solar stable and weatherproof. As far as printing with it it is similar to printing in ABS as far as I am aware, I might be wrong though. I personally am surprised how often this kind of question pops up and literally No One mentions ASA filament. I think I might buy some because I like the idea of printing something that can be left outside.

> **Comments:**
> **username_3**: ASA needs a print temperature of 250+ °C, which most printers with lined hotends can't reach without destroying the liner. Some ASA filament (3DXMax) even wants 270-290 °C. Heated bed is mandatory and ask for 80 to 110 °C. It *also* is best printed in an enclosure, which all are facts that make it a nieche product. It's fumes from the printing from printing also are likely to be toxic (research pending), and is one of those notorious hard to print filaments as it has severe layer adhesion problems and answers to those with splitting.  
> **username_0**: In addition to what @username_3 said, ASA is also relatively hard to get (unless you live in amazon-prime-free-shipping-land, sometimes referred to as the USA), I don't know of any filament supplier in my entire country that sells ASA  
> **username_5**: I wouldn't be so quick to dismiss this suggestion. I didn't know about ASA, yet I have an enclosed, air filtered printer with a 300ºC+ extruder w/ heated bed. Looking it up, dozens of choices available next day on Amazon Prime for me - I live in Scotland.  
> **username_6**: I've been using ASA and I'm pretty happy with it. Agreed that you need some high temps, I think I have to print at 270 which is the absolute tops of what my printer does, and bed, and enclosed, and mind the fumes, but if you happen to have that tech, it's easier to print than either PETG or ABS. Few colors. Supply in the USA is easy, multiple vendors, don't need amazon to get it.  

---

### Answer by username_7 on 2018-07-14. Score: 3

We use PLA in an outdoor environment, non-direct sunlight. PLA seems to be just as strong as day one. It has been about six months now.

Of course, you must seal coat to protect from moisture.

> **Comments:**
> **username_8**: I have some PLA parts outside since about 18 months now with no protection whatsoever. Except for some discoloration the parts are as strong as the first day. Of course the climate of your region plays a role in this too. I'm in Belgium, not in Arizona!  
> **username_7**: I'm in California, 30 degrees Fahrenheit up to 110.  
> **username_3**: Good watch in this regard: https://www.youtube.com/watch?v=qqNfa_zExRU  

---

### Answer by username_9 on 2019-03-25. Score: 1

What colour was your PLA? PLA will soften around 60C and a dark colour will easily get hotter than that in direct sun on a 30C day. Clear PLA seems to have much, much better temperature resistance, but any sort of PETG will kick it's butt in that regard.

> **Comments:**
> **username_10**: Sorry for resurrecting. Colors definitely affect performance in my experience. I have several printed pieces of white PLA that are outside 24/7 for several years now in the Spanish sun (Alicante, easily one of the sunnier places in Spain) without any problems whatsoever. But I printed some black trains and train tracks for my nephew using PLA and they'd go soft simply lying in the sun on the floor inside (in summer, 36-38C).  

---